EFEK PENAMBAHAN NIKEL SAAT PROSES SMAW MENGGUNAKAN ELEKTRODA HV 600 TERHADAP STRUKTUR MIKRO, LAJU KOROSI dan KEKERASAN

Mochamaf Abdul Latif Zaenudin, . (2025) EFEK PENAMBAHAN NIKEL SAAT PROSES SMAW MENGGUNAKAN ELEKTRODA HV 600 TERHADAP STRUKTUR MIKRO, LAJU KOROSI dan KEKERASAN. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text COVER.pdf Download (1MB)
	Text BAB I.pdf Download (275kB)
	Text BAB II.pdf Restricted to Registered users only Download (512kB) | Request a copy
	Text BAB III.pdf Restricted to Registered users only Download (672kB) | Request a copy
	Text BAB IV.pdf Restricted to Registered users only Download (430kB) | Request a copy
	Text BAB V.pdf Restricted to Registered users only Download (236kB) | Request a copy
	Text DAFTAR PUSTAKA.pdf Download (234kB)
	Text LAMPIRAN.pdf Restricted to Registered users only Download (1MB) | Request a copy

Abstract

Excavator memiliki komponen yang sangat penting yaitu bagian bucket, komponen ini harus memiliki kekuatan dan ketahan terhadap korosi, karena komponen ini digunakan untuk menggali material yang keras dan padat, biasanya tanah, atau untuk mengangkat beban berat. Pada bucket excavator terdapat kuku bucket . Teeth atau gigi bucket sering dibuat dari through-hardened alloy steel yang diproses hingga mencapai kekerasan di kisaran 45–55 HRC, setara 800 VHN (Wang dkk., 2023). Komponen ini kerap mengalami keausan akibat interaksi langsung dengan material keras seacara terus menerus. Permasalahan ini dapat menurunkan peforma alat serta dapat menimbulkan kerusakan lebih lanjut. Hardfacing dengan metode SMAW merupakan salah satu cara untuk yang dapat dipakai untuk menaikan tingkat kekerasan dan ketahanan aus pada suatu material dengan penambahan lapisan logam keras pada permukaannya. Hardfacing dapat dilakukan dengan las busur menggunakan elektroda HV 600 dengan penambahan variasi nikel 2g, 2,5g, dan 3g menghasilkan ketebalan 5mm. Kemudian sampel yang telah di hardfacing diuji struktur mikro, kekerasan, dan laju korosinya menggunakan mikroskop optik, alat uji kekerasan vickers dan metode weight loss. Pengujian struktur mikro menunjukkan terbentuknya martensit pengaruh dari penambahan Ni.Variasi penambahan nikel 3g memiliki martensit yang lebih seragam yang menjadikan sampel memiliki kekerasan yang tinggi 919,16 VHN dan laju korosi yang rendah 1,325 mpy. Penelitian ini dapat disimpulkan bahwa hardfacing dengan penambahan Ni dapat meningkatkan kekerasan dan menurunkan laju korosi. ***** The Excavator has a very important component, namely the bucket part, this component must have strength and resistance to corrosion, because this component is used to dig hard and dense materials, usually soil, or to lift heavy loads. On the excavator bucket there is a bucket nail . Teeth or bucket teeth are often made of through-hardened alloy steel that is processed to reach a hardness in the range of 45-55 HRC, equivalent to 800 VHN (Wang et al., 2023). This component often experiences wear due to direct interaction with hard materials continuously. This problem can degrade the performance of the tool and can cause further damage. Hardfacing with SMAW method is one way that can be used to increase the level of hardness and wear resistance in a material with the addition of a layer of hard metal on its surface. Hardfacing can be done by arc welding using hv 600 electrodes with the addition of nickel variations 2g, 2,5g, and 3g resulting in a thickness of 5mm. Then the hardfacing samples were tested for microstructure, hardness, and corrosion rate using optical microscopes, Vickers hardness testing equipment and weight loss methods. Microstructure testing showed the formation of martensitic influence from the addition of Ni.The variation of 3G nickel addition has a more uniform martensitic which makes the sample have a high hardness of 919.16 VHN and a low corrosion rate of 1.325 mpy. This study can be concluded that hardfacing with the addition of Ni can increase hardness and reduce corrosion rate.

Item Type:	Thesis (Sarjana)
Additional Information:	1). Drs. Syaripuddin, M.Pd. ; 2). Dr. Ferry Budhi Susetyo,.M.T,.M.Si
Subjects:	Teknologi dan Ilmu Terapan > Teknik Mesin, Mekanika Teknik
Divisions:	FT > S1 Pendidikan Teknik Mesin
Depositing User:	Mochamad Abdul Latif Zaenudin .
Date Deposited:	11 Aug 2025 02:30
Last Modified:	11 Aug 2025 02:30
URI:	http://repository.unj.ac.id/id/eprint/59503

Actions (login required)

View Item