PENGARUH KECEPATAN SPINDEL DAN DIAMETER MATA BOR TERHADAP DELAMINASI PADA PENGEBORAN MATERIAL CARBON FIBER REINFORCED POLYMER (CFRP) TERMODIFIKASI SILIKA ABU SEKAM PADI

REZA REVITA ZAHRA, . (2026) PENGARUH KECEPATAN SPINDEL DAN DIAMETER MATA BOR TERHADAP DELAMINASI PADA PENGEBORAN MATERIAL CARBON FIBER REINFORCED POLYMER (CFRP) TERMODIFIKASI SILIKA ABU SEKAM PADI. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text COVER.pdf Download (2MB)
	Text BAB 1.pdf Download (371kB)
	Text BAB 2.pdf Restricted to Registered users only Download (906kB) | Request a copy
	Text BAB 3.pdf Restricted to Registered users only Download (504kB) | Request a copy
	Text BAB 4.pdf Restricted to Registered users only Download (449kB) | Request a copy
	Text BAB 5.pdf Restricted to Registered users only Download (352kB) | Request a copy
	Text DAFTAR PUSTAKA.pdf Download (354kB)
	Text LAMPIRAN.pdf Restricted to Registered users only Download (1MB) | Request a copy

Abstract

Penelitian ini menganalisis pengaruh kecepatan spindel dan diameter mata bor terhadap delaminasi pada pengeboran material Carbon Fiber Reinforced Polymer (CFRP) yang dimodifikasi dengan silika hasil ekstraksi abu sekam padi. Material komposit CFRP termodifikasi ini memiliki peningkatan ketahanan termal dan sifat mekanis berdasarkan penelitian sebelumnya, namun kajian mengenai responsnya terhadap parameter pemesinan masih terbatas. Proses pengeboran dilakukan menggunakan mesin bor duduk dengan mata bor tipe Brad Spur berdiameter 4 mm, 6 mm, dan 8 mm serta variasi kecepatan spindel 1190 rpm, 1970 rpm, dan 2100 rpm. Delaminasi dianalisis pada dua mode kerusakan di delaminasi, yaitu delaminasi sisi masuk (Peel-up) dan delaminasi sisi keluar (Push-out). Pengolahan data menggunakan metode Taguchi dengan Orthogonal Array L9 serta Analysis of Variance (ANOVA) untuk menentukan pengaruh signifikan setiap faktor. Hasil penelitian menunjukkan bahwa diameter mata bor berpengaruh signifikan terhadap delaminasi Peel-up, sementara kecepatan spindel tidak berpengaruh signifikan. Pada sisi Push-out, kedua faktor tidak menunjukkan pengaruh signifikan, namun analisis S/N rasio menunjukkan kecenderungan pola kerusakan tertentu. Parameter optimum untuk meminimalkan delaminasi sisi masuk adalah diameter 4 mm – 2100 rpm, sedangkan untuk sisi keluar adalah diameter 8 mm – 2100 rpm. Temuan ini menegaskan perlunya pemilihan parameter yang seimbang untuk kualitas lubang yang lebih baik. ***** This study investigates the effect of spindle speed and drill bit diameter on delamination during the drilling of Carbon Fiber Reinforced Polymer (CFRP) modified with silica extracted from rice husk ash. Although previous studies have shown that silica-modified CFRP exhibits improved thermal and mechanical properties, research on its machining response remains limited. Drilling experiments were performed using a bench drilling machine with Brad Spur drill bits of 4 mm, 6 mm, and 8 mm diameters, combined with spindle speeds of 1190 rpm, 1970 rpm, and 2100 rpm. Delamination was evaluated in two damage modes: Peel-up (entry side) and Push-out (exit side). Data were analyzed using the Taguchi method with an L9 Orthogonal Array and Analysis of Varians (ANOVA) to determine the significance of each factor. The results indicate that drill bit diameter significantly affects Peel-up delamination, while spindle speed has no significant effect. For Push-out delamination, both factors were statistikally insignificant, although S/N rasio analysis revealed specific trends in damaged behaviour. The optimal parameters for minimizing Peel-up delamination were identified as a 4 mm drill bit with spindle speed of 2100 rpm, while the optimal conditions for reducing Push-out delamination were an 8 mm drill bit at 2100 rpm. These findings emphasize the impotance of selecting balanced machining parameters to achieve better overall hole quality.

Item Type:	Thesis (Sarjana)
Additional Information:	1). Dr. Ir. Himawan Hadi Sutrisno, M.T. ; 2). Dr. Siska Titik Dwiyati, M.T.
Subjects:	Teknologi dan Ilmu Terapan > Manufaktur
Divisions:	FT > S1 Rekayasa Keselamatan Kebakaran
Depositing User:	Reza Revita Zahra .
Date Deposited:	22 Jan 2026 04:12
Last Modified:	22 Jan 2026 04:12
URI:	http://repository.unj.ac.id/id/eprint/63297

Actions (login required)

View Item