KARAKTERISASI KALSIUM KLORIDA HEKSAHIDRAT BERBAHAN DASAR CANGKANG TELUR AYAM SEBAGAI PHASE CHANGE MATERIAL

NASYWA RAIHAN DHIYAULHAQ, . (2026) KARAKTERISASI KALSIUM KLORIDA HEKSAHIDRAT BERBAHAN DASAR CANGKANG TELUR AYAM SEBAGAI PHASE CHANGE MATERIAL. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text COVER.pdf Download (4MB)
	Text BAB 1.pdf Download (376kB)
	Text BAB 2.pdf Restricted to Registered users only Download (1MB)
	Text BAB 3.pdf Restricted to Registered users only Download (1MB)
	Text BAB 4.pdf Restricted to Registered users only Download (1MB)
	Text BAB 5.pdf Restricted to Registered users only Download (359kB)
	Text DAFTAR PUSTAKA.pdf Download (393kB)
	Text LAMPIRAN.pdf Restricted to Registered users only Download (1MB)

Abstract

Penelitian ini mengkaji sintesis dan karakteristik kalsium klorida heksahidrat (CaCl2.6H2O) berbahan dasar limbah cangkang telur sebagai Phase Change Material (PCM) untuk Thermal Energy Storage (TES). Proses preparasi sampel meliputi perubahan cangkang telur menjadi bubuk, diikuti sintesis menggunakan HCl untuk menghasilkan CaCl2.2H2O dan CaCl2.6H2O. Analisis x-ray diffraction (XRD) menunjukkan kristalinitas tinggi pada seluruh sampel yang sesuai dengan referensi standar dan munculnya fase metastabil CaCl2.4H2O pada sampel heksahidrat. Analisis fourier-transform infrared (FTIR) mengonfirmasi ikatan kimia yang serupa dengan referensi, meskipun sifat higroskopis menyebabkan hidrasi berlebih pada sampel dihidrat. Berdasarkan pengujian differential scanning calorimetry (DSC) pada CaCl2.6H2O, diperoleh nilai entalpi sebesar 187,94 J/g. Termogram DSC juga menampilkan puncak ganda pada 27.9°C dan 44.8 °C yang mengindikasikan pelelehan tidak merata dan pemisahan fase. Meskipun karakteristik tersebut memerlukan penambahan zat aditif atau metode enkapsulasi untuk stabilisasi PCM, keberadaan fase tetrahidrat memungkinkan penyesuaian temperatur termal untuk aplikasi temperatur di atas temperatur leleh normal CaCl2.6H2O. Hasil penelitian membuktikan bahwa limbah cangkang telur merupakan material yang kompetitif sebagai bahan baku CaCl2.6H2O dengan entalpi tinggi. ***** This study evaluates the synthesis and characterization of eggshell-based calcium chloride hexahydrate (CaCl2.6H2O) as a Phase Change Material (PCM) for Thermal Energy Storage (TES). The synthesis involved converting eggshell powder into CaCl2.2H2O and subsequently CaCl2.6H2O. X-ray diffraction (XRD) confirmed high crystallinity in all samples, with CaCl2.6H2O exhibiting minor peaks corresponding to the metastable CaCl2.4H2O phase. Fourier-transform infrared spectroscopy (FTIR) verified chemical bonds consistent with references, though the dihydrate showed increased hydration due to hygroscopicity. Differential scanning calorimetry (DSC) on CaCl2.6H2O revealed a total enthaply of 187,94 J/g. DSC thermograms displayed double peaks at 27.9 °C and 44.8°C, indicating incongruent melting and phase separation. While these characteristics necessitate additives or encapsulation for stabilization, the presence of the tetrahydrate phase allows for potential thermal tuning. The results demonstrate that eggshell waste is a viable precursor for producing high-enthalpy CaCl2.6H2O PCM.

Item Type:	Thesis (Sarjana)
Additional Information:	1). Dr. Dyah Arum Wulandari, S.T., M.T. ; 2). Dr. Wardoyo, S.T., M.T.
Subjects:	Teknologi dan Ilmu Terapan > Teknik Mesin, Mekanika Teknik Teknologi dan Ilmu Terapan > Teknik Energi
Divisions:	FT > S1 Pendidikan Teknik Mesin
Depositing User:	Nasywa Raihan Dhiyaulhaq .
Date Deposited:	12 Feb 2026 03:13
Last Modified:	12 Feb 2026 03:46
URI:	http://repository.unj.ac.id/id/eprint/64883

Actions (login required)

View Item