PENGARUH PENAMBAHAN SERBUK ECENG GONDOK PADA MATERIAL KOMPOSIT BERBASIS POLYESTER TERHADAP KEKERASAN DAN KEAUSAN KAMPAS REM

DAENG MOHAMAD JABEL, . (2026) PENGARUH PENAMBAHAN SERBUK ECENG GONDOK PADA MATERIAL KOMPOSIT BERBASIS POLYESTER TERHADAP KEKERASAN DAN KEAUSAN KAMPAS REM. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text 1. COVER (3).pdf Download (2MB)
	Text 2. BAB 1 (2).pdf Download (551kB)
	Text 3. BAB 2 (2).pdf Restricted to Registered users only Download (753kB)
	Text 4. BAB 3 (2).pdf Restricted to Registered users only Download (922kB)
	Text 5. BAB 4 (2).pdf Restricted to Registered users only Download (632kB)
	Text 6. BAB 5 (2).pdf Restricted to Registered users only Download (515kB)
	Text 7. DAFTAR PUSTAKA (2).pdf Download (501kB)
	Text 8. LAMPIRAN (2).pdf Restricted to Registered users only Download (1MB)

Abstract

Kampas rem merupakan salah satu komponen penting dalam sistem pengereman kendaraan yang berfungsi menghasilkan gaya gesek untuk memperlambat atau menghentikan laju kendaraan. Pengembangan kampas rem berbasis serat alam menjadi alternatif untuk mengurangi penggunaan material sintetis yang kurang ramah lingkungan. Penelitian ini bertujuan untuk mengetahui pengaruh variasi komposisi serat eceng gondok dan resin polyester terhadap nilai kekerasan dan keausan kampas rem komposit. Metode penelitian yang digunakan adalah metode eksperimental dengan pembuatan spesimen kampas rem menggunakan variasi komposisi serbuk eceng gondok dan resin polyester. Pengujian kekerasan dilakukan menggunakan durometer Shore D, sedangkan pengujian keausan dilakukan menggunakan metode Ogoshi. Hasil penelitian menunjukkan bahwa peningkatan persentase resin polyester menyebabkan nilai kekerasan kampas rem meningkat, sedangkan peningkatan persentase serat eceng gondok cenderung meningkatkan nilai keausan. Nilai kekerasan tertinggi diperoleh pada spesimen dengan kandungan resin polyester yang lebih tinggi, sementara nilai keausan terendah juga diperoleh pada spesimen dengan komposisi tersebut. Hasil penelitian ini menunjukkan adanya hubungan berbanding terbalik antara nilai kekerasan dan nilai keausan. Berdasarkan hasil yang diperoleh, kampas rem berbasis serat eceng gondok memiliki potensi untuk dikembangkan sebagai material alternatif yang ramah lingkungan, meskipun masih diperlukan penelitian lanjutan agar memenuhi standar yang berlaku. ***** Brake pads are one of the essential components in vehicle braking systems, functioning to generate friction in order to decelerate or stop the vehicle. The development of brake pads based on natural fibers has become an alternative approach to reduce the use of synthetic materials that are less environmentally friendly. This study aims to investigate the effect of variations in the composition of water hyacinth fiber and polyeste resin on the hardness and wear properties of composite brake pads. The research employed an experimental method by fabricating brake pad specimens with varying compositions of water hyacinth powder and polyester resin. Hardness testing was conducted using a Shore D durometer, while wear testing was performed using the Ogoshi method. The results indicate that an increase in the percentage of polyester resin leads to higher hardness values, whereas an increase in the proportion of water hyacinth fiber tends to increase the wear rate. The highest hardness value and the lowest wear value were obtained in specimens with higher polyester resin content. The findings also reveal an inverse relationship between hardness and wear properties. Based on these results, water hyacinth fiber–based brake pads show potential to be developed as an environmentally friendly alternative material; however, further research is required to meet applicable standards.

Item Type:	Thesis (Sarjana)
Additional Information:	1). Rani Anggrainy, S.Pd., M.T. ; 2). Dr. Ferry Budhi Susetyo, M.T., M.Si.
Subjects:	Teknologi dan Ilmu Terapan > Teknik Mesin, Mekanika Teknik Teknologi dan Ilmu Terapan > Otomotif, Astronotika
Divisions:	FT > S1 Pendidikan Teknik Mesin
Depositing User:	Daeng mohamad jabel .
Date Deposited:	04 Feb 2026 07:54
Last Modified:	04 Feb 2026 07:54
URI:	http://repository.unj.ac.id/id/eprint/64906

Actions (login required)

View Item