HAFIDHOH TASYA, . (2026) ANALISIS TERMAL PHASE CHANGE MATERIAL CaCl2·6H2O BERBAHAN DASAR LIMBAH CANGKANG TELUR DENGAN PENAMBAHAN SrCl2·6H2O dan KCl. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text COVER.pdf Download (1MB)
	Text BAB I Pendahuluan.pdf Download (398kB)
	Text BAB II Landasan Teori.pdf Restricted to Registered users only Download (905kB) | Request a copy
	Text BAB III Metodologi.pdf Restricted to Registered users only Download (815kB) | Request a copy
	Text BAB IV Hasil dan Pembahasan.pdf Restricted to Registered users only Download (1MB) | Request a copy
	Text BAB V Kesimpulan dan Saran.pdf Restricted to Registered users only Download (449kB) | Request a copy
	Text Daftar Pustaka.pdf Download (448kB)
	Text Lampiran dan Daftar Riwayat Hidup.pdf Restricted to Registered users only Download (2MB) | Request a copy

Abstract

Kebutuhan sistem thermal energy storage (TES) yang efisien dan berkelanjutan, mendorong pengembangan phase change material (PCM) berbasis garam hidrat sebagai media penyimpanan energi termal. Penelitian ini bertujuan untuk menganalisis gugus fungsi, karakteristik struktur kristal, dan sifat termal kalsium klorida heksahidrat (CaCl2·6H2O) yang disintesis dari limbah cangkang telur dengan penambahan aditif SrCl2·6H2O dan KCl. Proses preparasi sampel diawali dengan pengolahan cangkang telur menjadi bubuk, kemudian disintesis secara bertahap menjadi CaCl2·2H2O, CaCl2·6H2O, serta CaCl2·6H2O yang dimodifikasi menggunakan 2 wt.% SrCl2·6H2O dan 5 wt.% KCl. Karakterisasi material dilakukan menggunakan metode fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD), dan differential scanning calorimetry (DSC). Hasil FTIR mengonfirmasi keberadaan gugus karbonat pada bubuk cangkang telur serta molekul air kristal pada CaCl2·2H2O, CaCl2·6H2O, serta CaCl2·6H2O yang dimodifikasi menggunakan 2 wt.% SrCl2·6H2O dan 5 wt.% KCl. Analisis XRD menunjukkan bahwa bubuk cangkang telur dan CaCl2·2H2O memiliki pola difraksi yang sesuai dengan referensi masing-masing. Pada sampel CaCl2·6H2O yang dimodifikasi menggunakan 2 wt.% SrCl2·6H2O dan 5 wt.% KCl, fase CaCl2·6H2O tetap teridentifikasi sebagai fase dominan dengan kemunculan fase stabil CaCl2·4H2O sebagai fase minor. Hasil pengujian DSC menunjukkan puncak endotermik utama pada suhu 27,9 °C dan puncak endotermik kedua pada sekitar 44,4 °C yang berkaitan dengan fenomena incongruent melting, dengan total entalpi sebesar 99,59 J/g. Dibandingkan dengan hasil penelitian terdahulu, penambahan SrCl2·6H2O dan KCl menunjukkan kecenderungan meningkatkan entalpi pada puncak pertama serta mengurangi kontribusi entalpi pada puncak kedua yang berkaitan dengan pembentukan fase CaCl2·4H2O. Temuan tersebut mengindikasikan bahwa kedua aditif berpotensi meningkatkan stabilitas termal sistem PCM berbasis CaCl2·6H2O. ***** The need for an efficient and sustainable thermal energy storage (TES) system drives the development of phase change materials (PCM) based on hydrated salts as a medium for thermal energy storage. This research aims to analyse the functional groups, crystal structure characteristics, and thermal properties of hexahydrate calcium chloride (CaCl2·6H2O) synthesised from chicken egg shell waste with the addition of SrCl2·6H2O and KCl additives. The sample preparation process began with the processing of chicken egg shells into powder, which was then gradually synthesised into CaCl2·2H2O, CaCl2·6H2O, and CaCl2·6H2O modified with 2 wt.% SrCl2·6H2O and 5 wt.% KCl. Material characterisation was conducted using Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD), and differential scanning calorimetry (DSC) methods. FTIR results confirmed the presence of carbonate groups in the chicken egg shell powder and water molecules in CaCl2·2H2O, CaCl2·6H2O, and CaCl2·6H2O modified with 2 wt.% SrCl2·6H2O and 5 wt.% KCl. XRD analysis showed that the chicken egg shell powder and CaCl2·2H2O had diffraction patterns corresponding to their respective references. In the CaCl2·6H2O sample modified with 2 wt.% SrCl2·6H2O and 5 wt.% KCl, the CaCl2·6H2O phase remained identified as the dominant phase, with the stable CaCl2·4H2O phase appearing as a minor phase. The DSC test results show a main endothermic peak at a temperature of 27.9 °C and a second endothermic peak at around 44.4 °C, which are related to the phenomenon of incongruent melting, with a total enthalpy of 99.59 J/g. Compared to previous research results, the addition of SrCl2·6H2O and KCl shows a tendency to increase the enthalpy at the first peak and reduce the enthalpy contribution at the second peak related to the formation of the CaCl2·4H2O phase. These findings indicate that both additives have the potential to enhance the thermal stability of the CaCl2·6H2O-based PCM system.

Item Type:	Thesis (Sarjana)
Additional Information:	1). Dr. Dyah Arum Wulandari, M.T; 2). Dr. Wardoyo, M.T.
Subjects:	Teknologi dan Ilmu Terapan > Teknik Mesin, Mekanika Teknik Teknologi dan Ilmu Terapan > Teknik Energi
Divisions:	FT > D IV Teknologi Rekayasa Manufaktur
Depositing User:	Users 35154 not found.
Date Deposited:	05 Aug 2026 03:33
Last Modified:	05 Aug 2026 03:33
URI:	http://repository.unj.ac.id/id/eprint/68285

Actions (login required)

View Item