PENGARUH PENAMBAHAN UNSUR MAGNESIUM PADA ALUMUNIUM SAAT PROSES PENGECORAN TERHADAP KEKERASAN DAN LAJU KOROSI

SHEREN AZHARA, . (2026) PENGARUH PENAMBAHAN UNSUR MAGNESIUM PADA ALUMUNIUM SAAT PROSES PENGECORAN TERHADAP KEKERASAN DAN LAJU KOROSI. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text COVER.pdf Download (1MB)
	Text BAB I.pdf Download (255kB)
	Text BAB II.pdf Restricted to Registered users only Download (378kB) | Request a copy
	Text BAB III.pdf Restricted to Registered users only Download (794kB) | Request a copy
	Text BAB IV.pdf Restricted to Registered users only Download (486kB) | Request a copy
	Text BAB V.pdf Restricted to Registered users only Download (189kB) | Request a copy
	Text DAFTAR PUSTAKA.pdf Download (215kB)
	Text LAMPIRAN.pdf Restricted to Registered users only Download (1MB) | Request a copy

Abstract

Penelitian ini menganalisis pengaruh penambahan unsur magnesium (Mg) terhadap kekerasan dan laju korosi logam alumunium (Al) melalui proses pengecoran dengan metode gravity die casting. Fokus utama dari penelitian ini, membahas bagaimana pengaruh komposisi unsur Mg terhadap nilai kekerasan dan ketahanan korosi. Metode eksperimen dilakukan dengan variasi penambahan unsur Mg sebesar 0 wt. 2 wt.%, 5 wt.%, dan 10 wt.%. Hasil penelitian ini menunjukan bahwa peningkatan komposisi unsur Mg pada paduan Al berpengaruh terhadap kekerasan dan ketahanan korosi material. Hasil pengujian kekerasan menujukkan bahwa semakin besar komposisi Mg yang ditambahkan, maka semakin tinggi nilai kekerasan yang diperoleh. Sementara itu, hasil pengujian korosi menyebabkan peningkatan laju korosi, sehingga semakin besar kandungan unsur Mg yang ditambahkan maka semakin tinggi laju korosi yang terjadi. Kata kunci: gravity die casting, kekerasan, ketahanan korosi. ***** This study looks at how adding magnesium (Mg) on the hardness and corrosion rate of aluminum (Al) through gravity die casting. The main focus is on how the Mg composition hardness, and corrosion resistance. The experiments were done by varying the Mg content at 0 wt.%, 2 wt.%, 5 wt.%, and 10 wt.%. This research shows that increasing the Mg content in Al alloys affects the hardness and corrosion resistance of the material. Hardness tests indicate that the more Mg added, the higher the hardness value obtained. Meanwhile, corrosion tests show an increase in the corrosion rate, so the higher the Mg content added, the higher the corrosion rate. Keywords: gravity die casting, hardness, corrosion resistance.

Item Type:	Thesis (Sarjana)
Additional Information:	1). Dr. Ferry Budhi Susetyo, M.T., M.Si. ; 2). Drs. Syamsuir, M.T.
Subjects:	Teknologi dan Ilmu Terapan > Teknik Mesin, Mekanika Teknik Teknologi dan Ilmu Terapan > Manufaktur
Divisions:	FT > D IV Teknologi Rekayasa Manufaktur
Depositing User:	Sheren Azhara .
Date Deposited:	04 Aug 2026 08:37
Last Modified:	04 Aug 2026 08:37
URI:	http://repository.unj.ac.id/id/eprint/68379

Actions (login required)

View Item