PENGARUH VARIASI KOMPOSISI SERAT ECENG GONDOK, SERBUK KAYU JATI, SERAT PISANG KEPOK, DAN RESIN POLIESTER SEBAGAI PENGUAT PADA KOMPOSIT TERHADAP KEKUATAN TARIK DAN KEKUATAN IMPAK

ALIF SYAFAJAR YUSUF, . (2026) PENGARUH VARIASI KOMPOSISI SERAT ECENG GONDOK, SERBUK KAYU JATI, SERAT PISANG KEPOK, DAN RESIN POLIESTER SEBAGAI PENGUAT PADA KOMPOSIT TERHADAP KEKUATAN TARIK DAN KEKUATAN IMPAK. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text COVER.pdf Download (1MB)
	Text BAB I.pdf Download (295kB)
	Text BAB II.pdf Restricted to Registered users only Download (1MB) | Request a copy
	Text BAB III.pdf Restricted to Registered users only Download (1MB) | Request a copy
	Text BAB IV.pdf Restricted to Registered users only Download (493kB) | Request a copy
	Text BAB V.pdf Restricted to Registered users only Download (240kB) | Request a copy
	Text DAFTAR PUSTAKA.pdf Download (284kB)
	Text LAMPIRAN.pdf Restricted to Registered users only Download (4MB) | Request a copy

Abstract

Material komposit berbasis serat alam berpotensi menjadi alternatif material ramah lingkungan karena memiliki bobot ringan, mudah diperoleh, dan dapat terurai secara alami. Penelitian ini bertujuan untuk mengetahui pengaruh variasi komposisi serat eceng gondok dan serat pisang kepok terhadap kekuatan tarik dan kekuatan impak komposit bermatriks resin poliester dengan serbuk kayu jati sebagai komposisi tetap. Metode yang digunakan adalah eksperimen dengan komposisi resin poliester 50% dan serbuk kayu jati 10% dibuat konstan, sedangkan eceng gondok dan pisang kepok divariasikan. Spesimen A menggunakan 10% eceng gondok dan 30% pisang kepok, spesimen B menggunakan 20% eceng gondok dan 20% pisang kepok, serta spesimen C menggunakan 30% eceng gondok dan 10% pisang kepok. Serat pisang kepok diberi perlakuan perendaman asap cair selama 1 jam. Hasil penelitian menunjukkan bahwa spesimen A menghasilkan nilai terbaik pada seluruh pengujian, yaitu kekuatan tarik sebesar 2,22 MPa, elongasi 0,71%, kekuatan impak 0,0637 J/mm², dan energi serap 5,250 J. Spesimen B menghasilkan kekuatan tarik 1,80 MPa dan kekuatan impak 0,0598 J/mm², sedangkan spesimen C menghasilkan kekuatan tarik 1,53 MPa dan kekuatan impak 0,0595 J/mm². Berdasarkan hasil tersebut, peningkatan persentase serat pisang kepok memberikan pengaruh lebih baik terhadap kekuatan tarik dan kekuatan impak komposit. ***** Natural-fiber-based composite materials have the potential to serve as environmentally friendly alternatives because they are lightweight, readily available, and naturally biodegradable. This study aims to determine the effect of varying the composition of water hyacinth fibers and kepok banana fibers on the tensile strength and impact strength of polyester resin-matrix composites with teak wood powder as a constant component. The method used was an experiment in which the composition of 50% polyester resin and 10% teak wood powder was kept constant, while the proportions of water hyacinth and kepok banana were varied. Specimen A contained 10% water hyacinth and 30% kepok banana; specimen B contained 20% water hyacinth and 20% kepok banana; and specimen C contained 30% water hyacinth and 10% kepok banana. The kepok banana fibers were treated by soaking in liquid smoke for 1 hour. The research results show that Specimen A produced the best values in all tests, namely a tensile strength of 2.22 MPa, an elongation of 0.71%, an impact strength of 0.0637 J/mm², and an energy absorption of 5.250 J. Specimen B yielded a tensile strength of 1.80 MPa and an impact strength of 0.0598 J/mm², while specimen C yielded a tensile strength of 1.53 MPa and an impact strength of 0.0595 J/mm². Based on these results, increasing the percentage of kepok banana fibers has a more positive effect on the tensile strength and impact strength of the composite.

Item Type:	Thesis (Sarjana)
Additional Information:	1). Dr. Ferry Budhi Susetyo, M.T., M.Si. ; 2). Rani Anggrainy, S.Pd., M.T.
Subjects:	Teknologi dan Ilmu Terapan > Teknik Pertambangan, Metalurgi
Divisions:	FT > D IV Teknologi Rekayasa Manufaktur
Depositing User:	Alif Syafajar Yusuf .
Date Deposited:	05 Aug 2026 02:25
Last Modified:	05 Aug 2026 02:25
URI:	http://repository.unj.ac.id/id/eprint/68414

Actions (login required)

View Item