Pengembangan Material Aktif Komposit CuCoFe₂O₄@AC Sebagai Elektroda Superkapasitor Asimetrik

Aprilia Pramu Dhita, . (2026) Pengembangan Material Aktif Komposit CuCoFe₂O₄@AC Sebagai Elektroda Superkapasitor Asimetrik. Sarjana thesis, Universitas Negeri Jakarta.

	Text 01_COVER_merged.pdf Download (1MB)
	Text 02_BAB_1_PENDAHULUAN.pdf Download (299kB)
	Text 03_BAB_2_KAJIAN_PUSTAKA.pdf Restricted to Registered users only Download (589kB) | Request a copy
	Text 04_BAB_3_METODOLOGI.pdf Restricted to Registered users only Download (356kB) | Request a copy
	Text 05_BAB_4_HASIL_DAN_PEMBAHASAN.pdf Restricted to Registered users only Download (602kB) | Request a copy
	Text 06_BAB_5_KESIMPULAN.pdf Restricted to Registered users only Download (200kB) | Request a copy
	Text 07_DAFTAR_PUSTAKA.pdf Download (261kB)
	Text 08_LAMPIRAN.pdf Restricted to Registered users only Download (1MB) | Request a copy

Abstract

Penelitian ini bertujuan untuk mensintesis dan mengkarakterisasi komposit Copper Cobalt Ferrite (CuCoFe₂O₄) dengan karbon aktif berbasis tandan kosong kelapa sawit (CCF@AC) sebagai elektroda superkapasitor. Penambahan karbon aktif berperan meningkatkan luas permukaan komposit, sementara ferit spinel memberikan kontribusi aktivitas elektrokimia tambahan. Kombinasi keduanya memperkuat kinerja elektroda secara keseluruhan. Hasil penelitian menunjukkan bahwa elektroda CCF@AC dengan perbandingan 20:1 menghasilkan kapasitansi spesifik tertinggi, yaitu 0035 F/g pada sistem tiga elektroda, yang menunjukkan potensi komposit CCF@AC sebagai material elektroda superkapasitor dengan kinerja penyimpanan energi yang baik. Kata Kunci: superkapasitor asimetrik, logam oksida, elektroda, karbon aktif, biomassa ***** This work presents the synthesis and characterization of a Copper Cobalt Ferrite (CuCoFe₂O₄)/activated carbon composite (CCF@AC) prepared from empty oil palm fruit bunches as a high-performance supercapacitor electrode. The introduction of activated carbon enhances the composite by providing a larger Luas area, while the CuCoFe₂O₄ spinel ferrite contributes additional electrochemical activity. As a result, the composite exhibits improved charge storage performance. The CCF@AC electrode with a 20:1 mass ratio demonstrated the best electrochemical performance, achieving a specific capacitance of 0035 F/g in a three-electrode system confirming the suitability of the CCF@AC composite for high-performance energy storage devices. Keywords: assymmetric supercapacitor; metal oxide; electroda; activated carbon; biomass.

Item Type:	Thesis (Sarjana)
Additional Information:	1). Prof. Dr. Iwan Sugihartono, M.Si 2). Prof. Dr. Rike Yudianti, M.Sc
Subjects:	Sains > Fisika
Divisions:	FMIPA > S1 Fisika
Depositing User:	Aprilia Pramu Dhita .
Date Deposited:	14 Aug 2026 07:14
Last Modified:	14 Aug 2026 07:14
URI:	http://repository.unj.ac.id/id/eprint/70889

Actions (login required)

View Item