PEMANFAATAN ABU SEKAM PADI SEBAGAI BAHAN TAMBAH PADA PEMBUATAN PRODUK PAVING BLOCK

OSVALDO RAYHAN SATRIA, . (2026) PEMANFAATAN ABU SEKAM PADI SEBAGAI BAHAN TAMBAH PADA PEMBUATAN PRODUK PAVING BLOCK. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text COVER.pdf Download (936kB)
	Text BAB I.pdf Download (263kB)
	Text BAB II.pdf Restricted to Registered users only Download (369kB) | Request a copy
	Text BAB III.pdf Restricted to Registered users only Download (776kB) | Request a copy
	Text BAB IV.pdf Restricted to Registered users only Download (5MB) | Request a copy
	Text BAB V.pdf Restricted to Registered users only Download (232kB) | Request a copy
	Text DAFTAR PUSTAKA.pdf Download (207kB)
	Text LAMPIRAN.pdf Restricted to Registered users only Download (2MB) | Request a copy

Abstract

Osvaldo Rayhan Satria, Ir. Erna Septiandini, M.T., Adhi Purnomo, M.T. (2025). “Pemanfaatan Abu Sekam Padi Sebagai Bahan Tambah Pada Pembuatan Produk Paving block”. Skripsi. Jakarta: Program Studi Sarjana Terapan Teknologi Rekayasa Konstruksi Bangunan Gedung. Fakultas Teknik. Universitas Negeri Jakarta. Penelitian ini bertujuan untuk memanfaatkan limbah abu sekam padi sebagai bahan tambah dalam pembuatan produk paving block dengan variasi persentase sebesar 0%, 11%, 13%, dan 15% terhadap berat semen. Penelitian ini menggunakan perbandingan semen:pasir:air yaitu 1:4:0,35. Metode yang digunakan ialah metode 4D (Define, Design, Develop, dan Disseminate) dengan menggunakan benda uji paving block berbentuk balok dengan ukuran panjang 21 cm, lebar 10,5 cm, dan tebal 8 cm. Pengujian paving block dilakukan setelah benda uji berumur 28 hari. Pengujian yang dilakukan diantaranya uji sifat tampak, uji ukuran , uji kuat tekan, uji ketahanan aus, uji penyerapan air dan uji ketahanan terhadap natrium sulfat dengan acuan SNI 03-0691-1996. Hasil pengujian menunjukkan bahwa penambahan abu sekam padi dapat meningkatkan mutu paving block. Didapatkan nilai kuat tekan 0%, 11%, 13%, dan 15% secara berturut-turut adalah 14,93 MPa, 31,93 MPa, 33,4 MPa, dan 32,17 MPa. Daya serap air masing-masing sebesar 4,4%, 5,5%, 3,7%, dan 6,8%. Nilai ketahanan aus secara berturut-turut sebesar 0,195 mm/menit, 0,059 mm/menit, 0,069 mm/menit, dan 0,181 mm/menit. Terbukti variasi dengan tambahnan abu sekam padi tahan terhadap natrium sulfat dengan kehilangan massa di bawah 1%. Berdasarkan hasil penelitian dapat disimpulkan bahwa penambahan abu sekam padi berpengaruh terhadap mutu paving block, dengan variasi optimum berada pada kadar 13% yang mampu menghasilkan paving block bermutu B untuk lahan parkir berdasarkan SNI 03-0691-1996. Kata Kunci: Paving block, Abu Sekam Padi, Kuat Tekan, Penyerapan Air, Ketahanan Aus, Penyerapan Air, Ketahanan terhadap natrium sulfat. (*****) Osvaldo Rayhan Satria, Ir. Erna Septiandini, M.T., Adhi Purnomo, M.T. (2025). “Utilization of Rice Husk Ash as an Additive in Paving block Production” Undergraduate Thesis. Jakarta: Applied Bachelor’s Degree Program in Building Construction Engineering Technology. Faculty of Engineering. Jakarta State University. This research aims to utilise rice husk ash waste as an added ingredient in the manufacture of paving block products with percentage variations of 0%, 11%, 13%, and 15% by weight of cement. This research used a cement:sand:water ratio of 1:4:0.35. The method used is the 4D method (Define, Design, Develop, and Disseminate) using block-shaped paving block test objects with a length of 21 cm, width of 10.5 cm, and thickness of 8 cm. Testing of paving blocks was carried out after the test specimens were 28 days old. Tests carried out include visible properties test, size test, compressive strength test, wear resistance test, water absorption test and resistance to sodium sulfate test with reference to SNI 03-0691-1996. The test results show that the addition of rice husk ash can improve the quality of paving blocks. The compressive strength values obtained for 0%, 11%, 13%, and 15% were 14.93 MPa, 31.93 MPa, 33.4 MPa, and 32.17 MPa, respectively. Based on the research results, it can be concluded that the addition of rice husk ash affects the quality of paving blocks, with the optimum variation being at a content of 11% and 13%, which is capable of producing grade B paving blocks for parking lots based on SNI 03-0691-1996. Keywords: Paving block, Rice Husk Ash, Compressive Strength, Water Absorption, Wear Resistance, Water Absorption, Resistance to sodium sulfate.

Item Type:	Thesis (Sarjana)
Additional Information:	1). Ir. Erna Septiandini, M.T. 2). Adhi Purnomo, M.T.
Subjects:	Teknologi dan Ilmu Terapan > Teknik Sipil
Divisions:	FT > D IV Teknologi Rekayasa Konstruksi Bangunan Gedung
Depositing User:	Osvaldo Rayhan Satria .
Date Deposited:	24 Aug 2026 06:58
Last Modified:	24 Aug 2026 06:58
URI:	http://repository.unj.ac.id/id/eprint/73068

Actions (login required)

View Item