PEMANFAATAN LIMBAH ABU BONGGOL JAGUNG SEBAGAI PENGGANTI SEBAGIAN SEMEN PADA PEMBUATAN PAVING BLOCK UNTUK LAHAN PARKIR

REZA FADILAH, . (2026) PEMANFAATAN LIMBAH ABU BONGGOL JAGUNG SEBAGAI PENGGANTI SEBAGIAN SEMEN PADA PEMBUATAN PAVING BLOCK UNTUK LAHAN PARKIR. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text COVER.pdf Download (4MB)
	Text BAB 1.pdf Download (354kB)
	Text BAB 2.pdf Restricted to Registered users only Download (662kB) | Request a copy
	Text BAB 3.pdf Restricted to Registered users only Download (1MB) | Request a copy
	Text BAB 4.pdf Restricted to Registered users only Download (4MB) | Request a copy
	Text BAB 5.pdf Restricted to Registered users only Download (262kB) | Request a copy
	Text Daftar Pustaka.pdf Download (293kB)
	Text Lampiran.pdf Restricted to Repository staff only Download (3MB) | Request a copy

Abstract

Penelitian ini bertujuan untuk menganalisis pemanfaatan penggunaan abu bonggol jagung sebagai pengganti sebagian semen terhadap kualitas Paving block untuk lahan parkir. Campuran Paving block dibuat dengan perbandingan semen, pasir, dan air sebesar 1 semen : 4 pasir : 0,35 FAS, dengan variasi penggunaan abu bonggol jagung sebesar 0%, 10%, 13%, dan 16% dari berat semen. Pasir yang digunakan sebagai agregat halus berdasarkan hasil analisis gradasi termasuk ke dalam Zona II (pasir agak kasar). Pengujian yang dilakukan meliputi uji kuat tekan, penyerapan air, ketahanan aus, dan ketahanan natrium sulfat. Hasil pengujian kuat tekan menunjukkan bahwa variasi 0% menghasilkan kuat tekan sebesar 14,93 MPa, variasi 10% sebesar 25,95 MPa, variasi 13% sebesar 31,39 MPa, dan variasi 16% sebesar 28,81 MPa, dimana nilai tertinggi diperoleh pada variasi 13%. Hasil pengujian penyerapan air menunjukkan nilai sebesar 4,43% pada variasi 0%, 5,055% pada variasi 10%, 7,715% pada variasi 13%, dan 8,913% pada variasi 16%, yang menunjukkan bahwa penggunaan abu bonggol jagung cenderung meningkatkan penyerapan air. Sementara itu, hasil pengujian ketahanan aus menunjukkan nilai keausan sebesar 0,195 mm/menit pada variasi 0%, 0,155 mm/menit pada variasi 10%, 0,158 mm/menit pada variasi 13%, dan 0,082 mm/menit pada variasi 16%. Uji ketahanan natrium sulfat menunjukkan nilai kehilangan berat terendah pada variasi 16% sebesar 0,0545, yang mengindikasikan ketahanan yang lebih baik dibandingkan variasi lainnya. Berdasarkan hasil pengujian tersebut, variasi 13% abu bonggol jagung memberikan kombinasi sifat mekanik yang paling optimal dan Paving block yang dihasilkan memenuhi mutu B sehingga layak digunakan untuk lahan parkir. Kata kunci: abu bonggol jagung, Paving block, kuat tekan, penyerapan air, ketahanan aus***** This study aims to determine the effect of using corncob ash as a partial replacement for cement on the quality of Paving blocks for parking areas. The Paving block mixture was prepared with a cement–sand–water ratio of 1 : 4 : 0.35 (water–cement ratio), with corncob ash usage variations of 0%, 10%, 13%, and 16% by weight of cement. Based on the gradation analysis results, the fine aggregate used was classified as Zone II (medium-coarse sand). The tests conducted included compressive strength, water absorption, abrasion resistance, and sodium sulfate resistance. The compressive strength test results showed that the 0% variation produced a strength of 14.93 MPa, the 10% variation 25.95 MPa, the 13% variation 31.39 MPa, and the 16% variation 28.81 MPa, with the highest value obtained at the 13% variation. The water absorption test results were 4.43% for the 0% variation, 5.055% for the 10% variation, 7.715% for the 13% variation, and 8.913% for the 16% variation, indicating that the use of corncob ash tends to increase water absorption. Meanwhile, the abrasion resistance test results showed abrasion values of 0.195 mm/min for the 0% variation, 0.155 mm/min for the 10% variation, 0.158 mm/min for the 13% variation, and 0.082 mm/min for the 16% variation. The sodium sulfate resistance test showed the lowest weight loss value at the 16% variation of 0.0545, indicating better resistance compared to the other variations. Based on these results, the 13% corncob ash variation provides the most optimal combination of mechanical properties, and the resulting Paving blocks meet Grade B requirements, making them suitable for use in parking areas. Keywords: corncob ash, Paving block, compressive strength, water absorption, abrasion resistance

Item Type:	Thesis (Sarjana)
Additional Information:	1). Ir. Erna Septiandini, M.T. ; 2). Adhi Purnomo, M.T.
Subjects:	Teknologi dan Ilmu Terapan > Teknik Sipil
Divisions:	FT > D IV Teknologi Rekayasa Konstruksi Bangunan Gedung
Depositing User:	Reza Fadilah .
Date Deposited:	26 Aug 2026 07:10
Last Modified:	26 Aug 2026 07:10
URI:	http://repository.unj.ac.id/id/eprint/73229

Actions (login required)

View Item