PENGARUH PENGGUNAAN AGREGAT KASAR BUATAN FLY ASH DAN PLASTIK JENIS PET (FAPET) SEBAGAI SUBTITUSI BATU APUNG TERHADAP KUAT LENTUR BETON RINGAN (IMPLEMENTASI MATA KULIAH TEKNOLOGI BETON PADA PROGRAM STUDI PENDIDIKAN TEKNIK BANGUNAN FAKULTAS TEKNIK UNIVERSITAS NEGERI JAKARTA)

MUHAMMAD YUDHI ASHFIHANI, . (2022) PENGARUH PENGGUNAAN AGREGAT KASAR BUATAN FLY ASH DAN PLASTIK JENIS PET (FAPET) SEBAGAI SUBTITUSI BATU APUNG TERHADAP KUAT LENTUR BETON RINGAN (IMPLEMENTASI MATA KULIAH TEKNOLOGI BETON PADA PROGRAM STUDI PENDIDIKAN TEKNIK BANGUNAN FAKULTAS TEKNIK UNIVERSITAS NEGERI JAKARTA). Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text COVER.pdf Download (680kB)
	Text BAB 1.pdf Download (258kB)
	Text BAB 2.pdf Restricted to Registered users only Download (695kB) | Request a copy
	Text BAB 3.pdf Restricted to Registered users only Download (674kB) | Request a copy
	Text BAB 4.pdf Restricted to Registered users only Download (446kB) | Request a copy
	Text BAB 5.pdf Restricted to Registered users only Download (173kB) | Request a copy
	Text DAFTAR PUSTAKA.pdf Download (1MB)
	Text LAMPIRAN.pdf Restricted to Registered users only Download (7MB) | Request a copy

Abstract

Penelitian ini bertujuan untuk mengetahui kuat lentur optimum pada beton ringan struktural dengan menggunakan kadar persentase agregat kasar ringan buatan FAPET 0%, 25%, 50%, 75%, dan 100% sebagai subtitusi agregat batu apung. Target kuat lentur beton ringan yang direncanakan sesuai dengan SNI 03-2847-2019 sebesar 2,188 MPa serta menggunakan nilai faktor air semen (FAS) 0,48. Agregat kasar ringan buatan FAPET terbuat dari limbah plastik jenis PET dengan penambahan fly ash menjadi agregat kasar ringan buatan dalam campuran beton ringan. Metode penelitian yang digunakan dalam penelitian ini yaitu mengguanakan metode eksperimen dengan benda uji balok yang berdimensi lebar 10 cm, tebal 10 cm, dan panjang 40 cm untuk sampel lentur. Pada masing-masing variasi memiliki 3 sampel dan pembuatan campuran beton ringan mengacu pada SNI 03-3449-2002. Hasil yang didapatkan pada penelitian ini menunjukkan penggunaan agregat kasar ringan buatan FAPET pada beton ringan dapat meningkatkan kuat lentur beton. Nilai kuat lentur pada umur beton 28 hari dengan kadar persentase agregat kasar ringan buatan FAPET 0%, 25%, 50%, 75%, dan 100% berturut-turut sebesar 0,548 MPa; 0,609 MPa; 0,803 MPa; 0,836 MPa; dan 1,006 MPa. Nilai kuat lentur beton yang maksimum terjadi di persentase variasi agregat kasar ringan buatan FAPET 100%. This research is aimed to find out the optimum flexural strength in structural lightweight concrete by using the percentage rate of artificial lightweight aggregate made by FAPET 0%, 25%, 50%, 75%, and 100% as a subtitute of pumice aggregates. The flexural strength target of lightweight concrete planned in accordance with SNI 03-2847-2019 at 2,188 MPa and uses a cement water factor value (FAS) of 0.48. FAPET's lightweight aggregates are made from PET-type plastic waste with the addition of fly ash to artificial lightweight coarse aggregates in a lightweight concrete mixture. The research method is experimental method that use beam specimens with dimension; 10 cm wide, 10 cm thick, and 40 cm long for flexural samples. Each variation has 3 samples, and the manufacture of a lightweight concrete mixture refers to SNI 03-3449-2002. The results obtained in this research showed the use of FAPET aggregates in lightweight concrete could increase the flexural strength of the concrete. The flexural strength value at 28 days concrete with a percentage rate of lightweight aggregate made by FAPET 0%, 25%, 50%, 75%, and 100% consecutively amounting to 0.548 MPa; 0,609 MPa; 0,803 MPa; 0,836 MPa; and 1,006 MPa. The maximum flexural strength value of lightweight concrete occurs in the variation percentage of 100% FAPET lightweight aggregate.

Item Type:	Thesis (Sarjana)
Additional Information:	DR. SANTOSO SRI HANDOYO, MT SITTATI MUSALAMAH, MT
Subjects:	Teknologi dan Ilmu Terapan > Teknik Sipil Teknologi dan Ilmu Terapan > Konstruksi Bangunan
Divisions:	FT > S1 Pendidikan Teknik Bangunan
Depositing User:	Users 13546 not found.
Date Deposited:	21 Mar 2022 05:32
Last Modified:	21 Mar 2022 05:32
URI:	http://repository.unj.ac.id/id/eprint/24385

Actions (login required)

View Item