SINTESIS NANOKRISTAL BARIUM HEKSAFERIT TERSUBTITUSI Co, Zn, Ti DENGAN METODE MECHANICAL ALLOYING UNTUK APLIKASI PENYERAP GELOMBANG RADAR

DONNA BELLINA SYA’BAN, . (2017) SINTESIS NANOKRISTAL BARIUM HEKSAFERIT TERSUBTITUSI Co, Zn, Ti DENGAN METODE MECHANICAL ALLOYING UNTUK APLIKASI PENYERAP GELOMBANG RADAR. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text lembar pernyataan.pdf Download (302kB)
	Text lembar persetujuan panitia skripsi.pdf Download (329kB)
	Text SKRIPSI.pdf Download (2MB)
	Text ABSTRAK.pdf Download (140kB)

Abstract

Sintesis material magnet BaFe12-2xCoxZnxO19 dan BaFe12-x(CoTiZn)x/3O19 ( x = 0,0; 0,2; 0,4; 0,6; 0,8; dan 1,0) telah berhasil dibuat melalui metode Mechanical Alloying. Proses pencampuran basah dengan High Energy Ball Mill selama 30 menit terhadap serbuk Fe2O3, BaCO3, Co3O4, TiO2 dan ZnO dilakukan sehingga diperoleh paduan yang homogen. Perlakuan panas dengan tahapan kalsinasi 750o C selama 3 jam dan sintering 1100o C selama 5 jam. Paduan kemudian dimilling selama 30 jam untuk menjadi nanokristal. Analisis struktur terhadap data difraksi sinar-X dengan program GSAS menunjukkan terbentuknya barium heksaferit fasa tunggal BaFe12-2xCoxZnxO19 pada x=0.2 dan BaFe12-x(CoTiZn)x/3O19 x=0.6 dan 1. Dengan ukuran kristal yang didapat adalah 1.06nm. Analisis sifat kemagnetan dengan pengujian Permagraph menunjukan terjadinya penurunan nilai koersivitas seiring dengan peningkatan komposisi x. Analisis sifat penyerap gelombang RADAR dengan VNA(Vector Network Analyzer) menunjukan Reflection Loss maksimum material BaFe12-2xCoxZnxO19 pada x=0.6 adalah -14.4 dB pada 8.78GHz dan BaFe12-x(CoTiZn)x/3O19 pada x=1 adalah -3.11 pada 11.76GHz. Synthesized material magnet BaFe12-2xCoxZnxO19 and BaFe12-x(CoTiZn)x/3O19 ( x = 0,0; 0,2; 0,4; 0,6; 0,8; dan 1,0) have been done by using Mechanical Alloying process. Wet milling method by using High Energy Ball Mill 30 minutes for Fe2O3, BaCO3, Co3O4, TiO2 dan ZnO powder had been done until homogen. Sampel was calcined at 750o C for 3 hours and sintered at 1100o C for 5 hours. Sampel were milled 30 hours to get nanocrystal material. Materials were characterized by using XRD, Permagraph and VNA. Analysis for crystalline structure from XRD with GSAS program show that BaFe12-2xCoxZnxO19 for x=0.2 and BaFe12-x(CoTiZn)x/3O19 for x=0.6;1 formed single phase barium hexaferrite. Analysis for magnetic properties by Permagraph show decreasing in coercitivity as increasing ion subtitution. Analysis material absorber from VNA show that Reflection Loss maximum material BaFe12-2xCoxZnxO19 for x=0.6 is -14.4 dB at 8.78GHz and BaFe12-x(CoTiZn)x/3O19 for x=1 is -3.11 at 11.76GHz.

Item Type:	Thesis (Sarjana)
Additional Information:	1) Dr. Erfan Handoko, M.Si 2) Dr. Iwan Sugihartono, M.Si
Subjects:	Sains > Fisika
Divisions:	FMIPA > S1 Fisika
Depositing User:	sawung yudo
Date Deposited:	21 Mar 2022 04:09
Last Modified:	21 Mar 2022 04:09
URI:	http://repository.unj.ac.id/id/eprint/25010

Actions (login required)

View Item