SINTESIS POLIANILIN DENGAN METODE POLIMERISASI OKSIDATIF SEBAGAI ELEKTRODA UNTUK PROSES ADSORPSI-DESORPSI ION Na+ DAN Cl

AHMAD RAFLY JULIANA, . (2017) SINTESIS POLIANILIN DENGAN METODE POLIMERISASI OKSIDATIF SEBAGAI ELEKTRODA UNTUK PROSES ADSORPSI-DESORPSI ION Na+ DAN Cl. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

Text SKRIPSI_AHMAD RAFLY JULIANA_3325130964.pdf Download (1MB)

Abstract

Penelitian ini bertujuan untuk mengetahui karakteristik dari polianilin yang disintesis dengan metode polimerisasi oksidatif dengan variasi penetesan oksidan APS, rasio molar APS/Anilin pada suhu ruang dan 0°C serta membuat elektroda untuk sistem capasitive deionization (CDI) dari film polianilin. Serbuk polianilin jenis garam emeraldin telah berhasil disintesis baik pada suhu rendah (0°C) maupun pada suhu ruang yang dibuktikan dengan pita serapan utama khas pada analisis spektra FTIR, yaitu C=C stretching pada cincin quinoid, C=C stretching pada cincin benzenoid, C-N stretching dan stretching Q=NH+ -B. Analisis pola difraksi XRD juga mengkonfirmasi karakteristik pola diffraksi dari polianilin pada 2θ ~25°. Mikrograf polianilin dianalisis menggunakan SEM menunjukkan bahwa sampel polianilin hasil sintesis memiliki morfologi fiber dan granular. Berdasarkan hasil analisis luas permukaan dengan SAA, polianilin yang berhasil disintesis memiliki luas permukaan yang tinggi, mencapai 42,13 m2 /g. Hasil analisis konduktivitas tertinggi dengan sebesar 1,79 x 10-1 S/cm, dengan persen penghilangan garam sebesar ~1%. Berdasarkan studi literatur yang telah dilakukan, hasil sintesis merupakan karakteristik polianilin murni dengan luas area tertinggi. Berdasarkan hasil penelitian, pengaruh suhu reaksi terhadap luas permukaan yaitu pada suhu 0°C nilai luas permukaan lebih tinggi dari suhu ruang, sedangkan nilai konduktivitas suhu ruang lebih tinggi dari pada suhu 0°C. Semakin tinggi rasio molar APS/Anilin nilai luas permukaan dan konduktivitas cenderung meningkat, dan semakin lamanya dropping time oksidan APS, nilai luas permukaan dan konduktivitas semakin menurun. The objective of this research is to know the characteristic of polyaniline synthesized by oxidative polymerization method with variation of dropping time APS, APS/Aniline molar ratio at room temperature and 0°C and to make an electrode for capasitive deionization (CDI) system from polyaniline film. The polyaniline powder of the emeraldin salt type has been successfully synthesized both at low temperatures (0°C) and at room temperature as evidenced by typical main absorption bands in FTIR spectra analysis, C=C stretching on quinoid rings, C=C stretching on benzenoid rings, C-N stretching and stretching Q=NH+ -B. The XRD pattern diffraction analysis also confirmed the characteristic of the diffraction pattern of polyaniline at 2θ ~25°. The polyaniline micrographs analyzed using SEM showed that the polyaniline synthesized samples had fiber and granular morphology. Based on the results of surface area analysis with SAA, polyaniline successfully synthesized has a high surface area, reaching 42.13 m2 /g. Result of highest conductivity analysis with four point probe equal to 1,79 x 10-1 S/cm, with percentage of salt removal equal to ~1%. Based on literature studies that have been done, the synthesis results are characteristic of pure polyaniline with the highest area. Based on the result of research, the effect of reaction temperature on the surface area at 0°C, the value of surface area is higher than at room temperature, whereas the conductivity value at room temperature is higher than 0°C. The higher molar ratio of APS/Anilin, the value of surface area and conductivity tends to increase, and the longer dropping time of APS oxidant, the value of the surface area and the conductivity decreases.

Item Type:	Thesis (Sarjana)
Additional Information:	1) Dr. Setia Budi, M.Sc 2) Dr. Yusmaniar, M.Si
Subjects:	Sains > Kimia
Divisions:	FMIPA > S1 Kimia
Depositing User:	sawung yudo
Date Deposited:	04 Apr 2022 02:55
Last Modified:	04 Apr 2022 02:55
URI:	http://repository.unj.ac.id/id/eprint/25730

Actions (login required)

View Item