PENGARUH WAKTU FOTOPOLIMERISASI PADA METODE UV CURING TERHADAP KARAKTERISTIK SENYAWA POLIMER KOLESTERIL AKRILAT

FUJI LESTARI, . (2017) PENGARUH WAKTU FOTOPOLIMERISASI PADA METODE UV CURING TERHADAP KARAKTERISTIK SENYAWA POLIMER KOLESTERIL AKRILAT. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

Text 3325130958_Fuji Lestari.pdf Download (793kB)

Abstract

Fotopolimerisasi kolesteril akrilat menggunakan metode UV curing telah berhasil dilakukan hingga memperoleh fasa nematik kiral, yang memiliki struktur stabil pada suhu yang ditentukan. Fotopolimerisasi monomer akrilat dilakukan dengan pemaparan sinar UV bersumber dari lampu merkuri berdaya 55 watt selama 5, 10, 15, 20, dan 25 menit. Hasil karakterisasi FTIR menunjukkan fotopolimerisasi berlangsung sempurna setelah 10 menit yang ditandai hilangnya gugus C=C pada bilangan gelombang 1624.06 cm-1 . Difraktogram XRD menunjukkan pola difraksi XRD fasa nematik kiral (kolesterik) dengan sudut 2θ pada 15o -20o dan jumlah puncak difraksi berbeda-beda untuk perlakuan 5, 10 dan 15 menit. Data SEM menunjukkan struktur morfologi berbentuk balok dan memiliki arah orientasi yang sama, kecuali pada menit ke 15 arah orientasinya tidak beraturan. Data-data spektroskopi tersebut menunjukkan lamanya waktu pemaparan sinar UV pada proses fotopolimerisasi berpengaruh terhadap karakteristik polimer kolesteril akrilat. The photolymerisation of cholesteryl acrylate using UV curing method has been successfully performed to obtain a chiral nematic phase, which has a stable structure at a prescribed temperature. Photopolymerization of acrylic monomers was performed by UV exposure from 55 watt mercury lamps for 5, 10, 15, 20, and 25 minutes. The FTIR characterization results show that photopolymerization is complete after 10 minutes marked by loss of C = C bond at wave number 1624.06 cm-1 . Diffractogram XRD showed XRD diffraction pattern of chiral (cholesterolic) phenomenon with angle 2θ at 15o -20o and number of diffraction peaks varied for treatment 5, 10 and 15 minutes. The SEM data shows a morphological structure of bar shape and has the same orientation, except in the 15 minute the orientation direction is irregular. The spectroscopic data shows the duration of UV exposure time in the photopolimerization process has an effect on the characteristic of cholesterol polymer of acrylic.

Item Type:	Thesis (Sarjana)
Additional Information:	1) Dr. Afrizal, M.Si 2) Arif rahman, M.Sc
Subjects:	Sains > Kimia
Divisions:	FMIPA > S1 Kimia
Depositing User:	sawung yudo
Date Deposited:	06 Apr 2022 01:55
Last Modified:	06 Apr 2022 01:55
URI:	http://repository.unj.ac.id/id/eprint/25840

Actions (login required)

View Item