SINTESIS Ba(Fe,Zn,Co,Ti)12O19 DENGAN METODE SOL – GEL UNTUK APLIKASI MATERIAL MAGNETIK PENYERAP GELOMBANG RADAR

GILANG WIDIANTORO, . (2017) SINTESIS Ba(Fe,Zn,Co,Ti)12O19 DENGAN METODE SOL – GEL UNTUK APLIKASI MATERIAL MAGNETIK PENYERAP GELOMBANG RADAR. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text SKRIPSI_Gilang Widiantoro_3225130900.pdf Download (2MB)
	Text COVER _GILANG.pdf Download (90kB)

Abstract

Telah dilakukan proses sintesis material magnetik BaFe12-2x(ZnCo)xTixO19 dengan metode sol gel untuk x = 0; 0.5; 1. Diawali dengan pelarutan serbuk Fe2O3 (99.9%) pada HNO3 (60%) lalu ditambahkan serbuk BaCO3 (99%), ZnO (99%), Co3O4 (99%) dan TiO2.(99%) sehingga diperoleh larutan pembentuk material magnet. Proses homogenisasi larutan dilakukan dengan magnetic stirrer dan hot plate pada suhu 90 oC selama 3 jam dan dilanjutkan pengeringan larutan. Kristalisasi pada suhu 1100oC selama 1 jam telah diperoleh fasa barium heksaferrit diikuti dengan keberadaan fasa kedua (hematite) dalam jumlah yang cukup besar berdasarkan pengukuran difraksi sinar-X. Dari kurva histerisis hasil Permagraph diperoleh bahwa nilai koersivitas mengalami penurunan pada peningkatan jumlah substitusi. Nilai serapan material BaFe12-2x(ZnCo)xTixO19 yang paling optimum terbentuk saat x=1 dengan nilai Reflection Loss sebesar - 20.93 dB dan koefisien refleksi sebesar 8.98 % pada frekuensi 9.74 GHz. Magnetic material BaFe12-2x(ZnCo)xTixO19 for x = 0; 0.5; 1 have been synthesized by sol-gel method. As starting materials, Fe2O3 powders (99.9 %) were dissolved in HNO3 (60 %) and BaCO3 (99%), ZnO (99%), Co3O4 (99%), TiO2.(99%) powders was then added, magnetic material solution forming were produced. Homogenizatiton process performed by hot plate and magnetic stirrer at 90 oC for 3 h and continued drying solution. Based on the data from X-Ray Diffractometer obtained barium hexaferrite phase followed by second phase (hematite) with crystallization at 1100oC during 1 h. Hystherisis loop from Permagraph show that coercivity (Hc) decrease with increasing number of substitution. The most optimum value of absorption material’s BaFe12-2x(ZnCo)xTixO19 formed when x=1 with Reflection Loss -20.93 dB and reflection coefficient 8.98 % at 9.74 GHz.

Item Type:	Thesis (Sarjana)
Additional Information:	1) Dr. Erfan Handoko, M.Si 2) Dr. Iwan Sugihartono, M.Si
Subjects:	Sains > Fisika
Divisions:	FMIPA > S1 Fisika
Depositing User:	sawung yudo
Date Deposited:	06 Apr 2022 02:28
Last Modified:	06 Apr 2022 02:28
URI:	http://repository.unj.ac.id/id/eprint/25851

Actions (login required)

View Item