PENGARUH KONSENTRASI ASAM BORAT (H3BO3) TERHADAP LAPISAN TIPIS KOMPOSIT Ni-TiAlN DENGAN TEKNIK ELEKTRODEPOSISI

RENTHA THERESIA, . (2017) PENGARUH KONSENTRASI ASAM BORAT (H3BO3) TERHADAP LAPISAN TIPIS KOMPOSIT Ni-TiAlN DENGAN TEKNIK ELEKTRODEPOSISI. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

Text SKRIPSI_RENTHA THERESIA.pdf Download (3MB)

Abstract

Telah dilakukan penelitian pembentukan lapisan tipis Ni-TiAlN. Penelitian ini menggunakan titanium aluminium nitrida (TiAlN). Tujuan dari penelitian ini mengetahui pengaruh konsentrasi asam borat pada lapisan tipis komposit NiTiAlN terhadap struktur morfologi. Elektrodeposisi merupakan teknik proses pelapisan pada permukaan bahan logam. Elektrodeposisi pada substrat tungsten karbida (WC) dilakukan selama 15 menit, dan arus 3,0 mA dengan variasi asam borat 30 gr/L, 35 gr/L, 40 gr/L H3BO3. Ditambahkan kedalam larutan elektrolit 0,63 M Ni2SO4.6H2O; 0,09 M NiCl2.6H2O; 0,2 gr/L Sodium Dodecyl Sulfate (SDS); 4 gr/L TiN dan 4 gr/AIN. Hasil elektrodeposisi dianalisis menggunakan, Scanning Electron Microscopy (SEM). Hasil penelitian menunjukkan adanya pengaruh terhadap tungsten karbida pada morfologi dengan semakin besar konsentrasi maka aglomerat yang terbentuk semakin terlihat jelas, dan semakin kecil konsentrasi retakan semakin jelas. Has done the processingcoating thin composite Ni-TiAlN. This research uses titanium aluminum nitride (TiAlN). The purpose of this research is to know the influence of concentration boric acid on the thin layer composite Ni-TiAlN to morphological structure. Elektrodeposition is coating process to form metallic materials.. The electrodeposition of the tungsten carbide (WC) substrate was carried out for 15 min, and a current of 3.0 mA with a variation of boric acid 30 g / L, 35 g / L, 40 g / L H3BO3. Added to an electrolyte solution of 0.63 M Ni2SO4.6H2O; 0.09 M NiCl2.6H2O; 0.2 g / L Sodium Dodecyl Sulfate (SDS); 4 gr / L TiN and 4 gr / AIN. Electrodeposition results were analyzed using Scanning Electron Microscopy (SEM). The result from tungsten carbide on morphology with bigger concentration, the agglomerates formed become more smotter, and the smaller the crack concentration becomes clearly.

Item Type:	Thesis (Sarjana)
Additional Information:	1) Dr.Esmar Budi, M.T 2) Dr.Iwan Sugihartono,M.Si
Subjects:	Sains > Fisika
Divisions:	FMIPA > S1 Fisika
Depositing User:	sawung yudo
Date Deposited:	14 Apr 2022 01:36
Last Modified:	14 Apr 2022 01:36
URI:	http://repository.unj.ac.id/id/eprint/26512

Actions (login required)

View Item