SINTESIS DAN UJI SIFAT KATALITIK NIKEL FERIT (NiFe2O4) UNTUK MEMECAH UAP PERTAMAX PLUS PADA HIDROCARBON CRACK SYSTEM (HCS)

ZENTIKA MAODI, . (2017) SINTESIS DAN UJI SIFAT KATALITIK NIKEL FERIT (NiFe2O4) UNTUK MEMECAH UAP PERTAMAX PLUS PADA HIDROCARBON CRACK SYSTEM (HCS). Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

Text Zentika Maodi 3325130967.pdf Download (2MB)

Abstract

Penelitian ini bertujuan untuk mensintesis Nikel Ferit dan mengetahui sifat katalitik Nikel Ferit (NiFe2O4) untuk memecah uap pertamax plus pada Hydrocarbon Crack System (HCS)). Dalam penelitian ini digunakan Natrium Hidroksida yang berperan sebagai agen presipitasi. Hasil karakterisasi XRD menunjukkan bahwa Nikel Ferit (NiFe2O4) bersifat kristalin dengan nilai 2θ di sudut 30,29o ; 35,67o ; 43,36o ; 62,99o ; 71,48o dan 74,55o . Hasil karakterisasi SAA menunjukkan bahwa Nikel Ferit (NiFe2O4) memiliki pola isoterm adsorpsi tipe IV bersifat mesopori. Uji sifat katalitik Nikel Ferit (NiFe2O4) dilakukan dengan dua cara yaitu pengujian dynotest dan uji emisi gas buang. Hasil pengujian menunjukkan bahwa menggunakan HCS dapat meningkatkan daya dan torsi dibandingkan tanpa menggunakan. Hasil pengujian emisi gas buang menunjukkan bahwa penurunan kandungan CO2 dan HC setelah menggunakan HCS. The study of these research is purpose to synthesis Nickel Ferrite and knows the catalytic properties of Nickel Ferrite (NiFe2O4) to break up the pertamax plus vapor in the Hydrocarbon Crack System (HCS). In this study, sodium hydroxide was act as precipitation agent. The XRD characterization results show that Nickel Ferrite (NiFe2O4) is crystalline with a value of 2θ at an angle of 30,29o ; 35,67o ; 43,36o ; 62,99o ; 71,48o dan 74,55o . The SAA characterization result show that Nickel Ferrite (NiFe2O4) has a mesoporous type IV adsorption isoterm pattern. Testing of catalytic properties of Nickel Ferrite (NiFe2O4) is done in two ways, namely dynotest test and exhaust gas emission test. The test results show that using HCS can increase power and torque compared without using HCS. Test of exaust gas emission test results show that by decreasing CO2 and HC content after using HCS.

Item Type:	Thesis (Sarjana)
Additional Information:	1) Prof. Dr. Erdawati, M.Sc 2) Drs. Darsef, M.Si
Subjects:	Sains > Kimia
Divisions:	FMIPA > S1 Kimia
Depositing User:	sawung yudo
Date Deposited:	20 Apr 2022 06:00
Last Modified:	20 Apr 2022 06:00
URI:	http://repository.unj.ac.id/id/eprint/27241

Actions (login required)

View Item