STUDI PEMANFAATAN LIMBAH KARBIT SEBAGAI BAHAN PENGGANTI SEBAGIAN SEMEN TERHADAP KUAT TEKAN BETON

MUHAMMAD REZA ANUGRAH SAPUTRA, . (2017) STUDI PEMANFAATAN LIMBAH KARBIT SEBAGAI BAHAN PENGGANTI SEBAGIAN SEMEN TERHADAP KUAT TEKAN BETON. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text BAB 2.pdf Download (396kB)
	Text BAB 4.pdf Download (406kB)
	Text BAB 3.pdf Download (265kB)
	Text BAB 1.pdf Download (126kB)
	Text DAFTAR LAMPIRAN.pdf Download (5kB)
	Text DAFTAR ISI.pdf Download (21kB)
	Text BAB 5.pdf Download (114kB)
	Text DAFTAR GAMBAR.pdf Download (5kB)
	Text DAFTAR TABEL.pdf Download (6kB)
	Text HALAMAN JUDUL.pdf Download (26kB)
	Text GAMBAR DAN DOKUMENTASI.pdf Download (553kB)
	Text LAMPIRAN.pdf Download (1MB)
	Text KATA PENGANTAR.pdf Download (78kB)
	Text HALAMAN PERNYATAAN.pdf Download (505kB)
	Text ABSTRAK INGGRIS.pdf Download (242kB)
	Text ABSTRAK INDONESIA.pdf Download (259kB)
	Text DAFTAR PUSTAKA.pdf Download (13kB)
	Text RIWAYAT HIDUP.pdf Download (85kB)
	Text HALAMAN PENGESAHAN.pdf Download (330kB)

Abstract

Tujuan penelitian ini adalah untuk mengetahui limbah karbit dapat menggantikan sebagian semen pada pengujian kuat tekan dalam upaya untuk mengetahui kuat tekan maksimum pada beton. Penelitian ini mengganti sebagian semen dengan limbah karbit dengan variasi persentase 0%, 20%, 30%, dan 40% dari jumlah berat semen. Kuat tekan rencana f’c 20 MPa, W/C 0.55, dan slump 12 2 cm, dengan jumlah sampel 24 benda uji (3 benda uji untuk setiap variasi untuk umur beton 14 dan 28 hari). Hasil penelitian ini menunjukkan bahwa penggunaan variasi 20% limbah karbit diperoleh kuat tekan rata-rata yaitu 15,94 MPa; variasi 30% limbah karbit 13,58 MPa dan variasi 40% limbah karbit 11,6 MPa. Kuat tekan optimum terdapat pada variasi 20% dengan kuat tekan rata-rata 15,94 tetapi tidak lebih kuat dari beton kontrol yaitu 19,81 MPa. The purpose of this research is to determine the carbide waste can partially replace cement in compressive strength test in an effort to determine the maximum compressive strength of the concrete. This research was partially replacing cement with carbide waste with a variety of percentages 0%, 20%, 30%, and 40% of the total weight of cement. Concrete design f’c 20 MPa, W/C 0,55, 12 2 cm slump, amount of sample was 24 (3 samples for each variation for concrete life of 14 and 28 days). The results showed that 20% variation of carbide waste reached the average concrete compressive strength is 15,94 MPa; 30% variation of carbide waste is 13,58 MPa and 40% variation of carbide waste is 11,6 MPa. The maximum concrete compressive strength contained in 20% variation of carbide waste but not more stronger than the control concrete with average concrete compressive strength is 19,81 MPa.

Item Type:	Thesis (Sarjana)
Additional Information:	1) Anisah, MT 2) Drs. Prihantono, M. Eng
Subjects:	Teknologi dan Ilmu Terapan > Teknik Sipil
Divisions:	FT > S1 Pendidikan Teknik Bangunan
Depositing User:	sawung yudo
Date Deposited:	25 May 2022 06:17
Last Modified:	25 May 2022 06:17
URI:	http://repository.unj.ac.id/id/eprint/28955

Actions (login required)

View Item