MUARIEF, . (2015) Sintesis Lapisan Tipis Komposit Ni-TiAlN Menggunakan Teknik Elektrodeposisi dalam Menurunkan Laju Korosi pada Substrat High Speed Steel (HSS), Galvanis dan Kuningan. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.
![]() |
Text
Skripsi_Muarief_3225111271.pdf Download (5MB) |
Abstract
Telah dilakukan kajian pensintesisan lapisan komposit elektrodeposisi Ni-TiAlN menggunakan parameter proses elektrodeposisi berdasarkan jenis bahan logam atau logam campuran yang digunakan sebagai substrat. Variasi jenis bahan substrat yang digunakan sebanyak 3 variasi yaitu High Speed Steel (HSS), Kuningan dan Galvanis. Pada penelitian ini komposisi larutan elektrolit terdiri dari 0.38 M Ni2SO4.6H2O, 0.17 M NiCl2.6H2O dan 0.49 M H3BO3 ditambah dengan serbuk TiN dan AlN masing-masing 6 gr/L serta sufraktan Dodecyl Sulfate Sodium (C12H25NaO4S) sebanyak 0.05 g/L. Penelitian dilakukan pada arus elektrodeposisi masing-masing sebesar 3.0 mA selama 15 menit. Hasil percobaan menunjukan bahwa lapisan komposit memiliki morfologi dan struktur kristal yang mengikuti pola dan kondisi substrat dasarnya. Sedangkan dari data hasil percobaan ketahanan laju korosi, efisiensi lapisan Ni-TiAlN pada substrat Galvanis sebesar 29,41% sedangkan pada HSS dan Kuningan sebesar 27,27% dan 25,57%. ********** Composite coating on metal is subjected to improve its wear and corrosion resistances. Electrodeposited Ni-TiAlN composite film using variations of metal or metal alloy type as substrate has been investigated. Variation of substrate type used amount 3 variations that are High Speed Steel (HSS), Brass and Galvanis. On this experiment, the electrolyte composition consist of 0.38 M Ni2SO4.6H2O, 0.17 M NiCl2.6H2O and 0.49 M H3BO3 added with each 6 gr/liter amounts of TiN and AlN powders and Dodecyl Sulfate Sodium (C12H25NaO4S) 0.5 gr/liter as sufraktan. The experiment was performed at electrodeposition current of 3.0 mA for about 15 minutes. The results show that the composite film morphology and crystal structure are following raw substrate. The result of this research corrosion resistance Ni-TiAlN film on the Galvanis substrate is 29,41%, meanwhile on the HSS and Brass substrate respectively are 27,27% and 25,57%
Item Type: | Thesis (Sarjana) |
---|---|
Additional Information: | 1). Dr. Esmar Budi, M.T. ; 2). Dr. Iwan Sugihartono, M.Si. |
Subjects: | Sains > Fisika |
Divisions: | FMIPA > S1 Fisika |
Depositing User: | Users 14614 not found. |
Date Deposited: | 27 May 2022 05:51 |
Last Modified: | 27 May 2022 05:51 |
URI: | http://repository.unj.ac.id/id/eprint/29188 |
Actions (login required)
![]() |
View Item |