PENGARUH PENGGUNAAN KANJI DAN PERNIS TERHADAP KUALITAS DUSTEX SEBAGAI BAHAN BAKU PRODUK

FITRI YULIANTI, . (2017) PENGARUH PENGGUNAAN KANJI DAN PERNIS TERHADAP KUALITAS DUSTEX SEBAGAI BAHAN BAKU PRODUK. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

Text SKRIPSI fitri-yulianti.pdf Download (2MB)

Abstract

Penelitian bertujuan untuk mengetahui pengaruh penggunaan kanji dan pernis terhadap kualitas dustex. Adapun penelitian ini dilaksanakan di Fakultas Teknik, Universitas Negeri Jakarta pada bulan juni 2016 hingga Agustus 2017 Penelitian ini menggunakan metode eksperimen. Peneliti membuat produk daur ulang limbah kain yang disebut dengan dustex dan diharapkan dapat digunakan sebagai bahan baku berbagai macam produk dengan menerapkan treatment yang berbeda yaitu dua viskositas kanji yang berbeda dan penggunaan atau tanpa penggunaan pernis lalu dilakukan pengujian laboratorium terhadap aspek kekuatan tarik, daya serap air dan ketahanan luntur warnanya terhadap air. Perlakuan penelitian dilakukan melalui tahap penelitian dalam pemilihan bahan, tahap persiapan alat dan bahan, tahap pengolahan limbah kain, tahap eksperimen serta tahap pengujian.Teknik pengumpulan data dilakukan dengan mencatat semua hasil uji yang diperoleh dari pengujian laboratorium menurut standar nasional Indonesia pada lembar observasi. Hasil penelitian mengenai pengolahan limbah kain hingga menjadi dustex didapatkan hasil bahwa semakin besar viskositas kanji maka permukaan dustex semakin keras dan penggunaan pernis dapat melindungi serta menambah kilap permukaan dustex. Hasil pengujian menunjukkan bahwa semakin besar viskositas kanji maka kekuatan tarik semakin besar, daya serap air semakin kecil dan ketahanan luntur warna semakin buruk dan penggunaan pernis akan meningkatkan kekuatan tarik, menurunkan kemampuan daya serap air dan ketahanan luntur warna dustex terhadap air . Penelitian ini diharapkan dapat berguna untuk memberi informasi dan bahan rujukan untuk dapat menentukan produk yang ingin dibuat dengan menggunakan bahan dustex. Serta diharapkan dapat memberi motivasi mahasiswa maupun masyarakat agar terus berkreatifitas dan menciptakan suatu karya yang baik. The purpose of this research was to find out the influence of using kanji and varnish on dustex quality. This study was conducted at Engineering Faculty, State University of Jakarta during june 2016 to August 2017. The method of this research used is experiment. The researcher made recycling product from garment waste called dustex. It is expected to be used as raw material of various products by applying different treatment that is two different kanji viscosity and the use or without the use of varnish. Furthermore the researcher conducted laboratory testing to the aspect of tensile strength and its color fastness from water. The treatment started from made selection of materials, the preparation of tools and materials, the waste treatment, the experimental, and the final step was testing. Data collection techniques are conducted by recording all test results obtained from laboratory testing according to Indonesian National Standards on the observation sheet. The results of this study from processing of garment waste become to dustex obtained conclusion that the greater of kanji viscosity so dustex surface is harder and using of varnish can protect and dustex get more glossy. The test results show that greater viscosity of the kanji so greater the tensile strength, and the less water absorption and the worsening of the color fade and also the use of varnish will increase the tensile strength, decrease the water absorption capacity and the dustex color fastness from water. This research is expected to be useful to provide information and reference for determine what product could be made by using dustex materials. It also expected to motivate students and the community more creative to create a good work.

Item Type:	Thesis (Sarjana)
Additional Information:	1) Dra. Melly Prabawati M.Pd, 2) Dr. Dewi Suliyanthini, AT, MM
Subjects:	Desain Kostum, Tata Busana > Tata Busana
Divisions:	FT > S1 Pendidikan Tata Busana
Depositing User:	sawung yudo
Date Deposited:	15 Jun 2022 08:19
Last Modified:	15 Jun 2022 08:19
URI:	http://repository.unj.ac.id/id/eprint/30370

Actions (login required)

View Item