PENGARUH BENTUK NANOPARTIKEL EMAS YANG DISINTESIS DENGAN TEKNIK ELEKTRODEPOSISI TERHADAP AKTIVITAS ELEKTROOKSIDASI ETANOL

ANNISA AULIYA, . (2021) PENGARUH BENTUK NANOPARTIKEL EMAS YANG DISINTESIS DENGAN TEKNIK ELEKTRODEPOSISI TERHADAP AKTIVITAS ELEKTROOKSIDASI ETANOL. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text 04 BAB III.pdf Restricted to Registered users only Download (845kB)
	Text 03 BAB II.pdf Restricted to Registered users only Download (1MB)
	Text 01 COVER.pdf Download (1MB)
	Text 05 BAB IV.pdf Restricted to Registered users only Download (1MB)
	Text 02 BAB I.pdf Download (710kB)
	Text 07 DAFTAR PUSTAKA.pdf Download (827kB)
	Text 08 LAMPIRAN.pdf Restricted to Registered users only Download (949kB)
	Text 06 BAB V.pdf Restricted to Registered users only Download (580kB)

Abstract

Penggunaan katalis dalam elektrooksidasi etanol mendapat perhatian yang luas karena potensi aplikasinya untuk menghasilkan tenaga listrik melalui sel bahan bakar etanol. Dalam hal ini, Au menyajikan aktivitas katalisis yang baik dalam kondisi basa, dan yang terpenting, katalis Au menunjukkan ketahanan terhadap keracunan yang disebabkan oleh karbon monoksida yang teradsorpsi. Modifikasi bentuk partikel Au penting untuk meningkatkan efisiensi suatu katalis. Oleh karena itu, penelitian ini bertujuan untuk menyintesis nanopartikel emas dengan berbagai bentuk melalui teknik elektrodeposisi. Teknik ini dipilih karena memiliki keunggulan dalam mengontrol morfologi partikel yang akan disintesis. Hasilnya, nanopartikel emas dengan bentuk bercabang dan bulat berhasil disintesis dengan teknik ini. uji aktivitas elektrokimia dengan EIS menunjukkan bahwa partikel Au/FTO 0,50 V dan Au/FTO 50 menit memiliki kinetika transfer elektron paling baik. Uji CV mengonfirmasi hasil EIS, di mana kedua partikel tersebut memang memiliki aktivitas elektrooksidasi etanol lebih tinggi, dengan nilai rapat arus 7,9 dan 8,0 mA/cm2 untuk masing-masing katalis. Di antara kedua katalis ini, rasio jb/jf yang menunjukkan ketahanan keracunan COads pada Au/FTO 0,50 V lebih baik dibandingkan Au/FTO 50 menit. Secara keseluruhan, Au/FTO 0,50 V merupakan katalis elektrooksidasi etanol terbaik di antara katalis lain yang disintesis pada penelitian ini, karena memiliki aktivitas elektrooksidasi etanol tertinggi dengan tingkat keracunan COads yang rendah. The use of catalysts in the electrooxidation of ethanol has received wide attention because of its potential application to generate electric power through direct ethanol fuel cells. In this case, Au presents good catalytic activity under base conditions. Importantly, the Au catalyst exhibits resistance to poisoning by adsorbed carbon monoxide. Therefore, this study aims to synthesize gold nanoparticles of various shapes through electrodeposition. This technique was chosen because it has the advantage of controlling the shape of the particles to be synthesized. The experimental results showed that Au/FTO with branched and spherical shape was successfully synthesized by this technique. Electrochemical activity test with EIS showed that Au/FTO 0.50 V and Au/FTO 50 minutes had the best electron transfer kinetics. The CV test confirmed the EIS results, where both particles had the highest ethanol electrooxidation catalytic activity, with a value of 7.9 and 8.1 mA/cm2 for each catalyst. Between these two catalysts, the ratio jb/jf which shows the resistance to COads poisoning at Au/FTO 0.50 V is better than Au/FTO 50 minutes. Overall, Au/FTO 0.50 V is the best catalyst for ethanol oxidation among other catalysts synthesized in this study, because it has the highest oxidation activity with lower COads toxicity.

Item Type:	Thesis (Sarjana)
Additional Information:	1)Dr. Setia Budi, M.Sc. 2)Assoc. Prof. Dr. Akrajas Ali Umar.
Subjects:	Sains > Kimia
Divisions:	FMIPA > S1 Kimia
Depositing User:	Users 14629 not found.
Date Deposited:	14 Jul 2022 01:26
Last Modified:	14 Jul 2022 01:26
URI:	http://repository.unj.ac.id/id/eprint/31757

Actions (login required)

View Item