ANALISA PENGARUH KETEBALAN LAPISAN 3D PRINTING TERHADAP KEKUATAN TEKAN MENGGUNAKAN BAHAN ABS DAN PLA

NANDI PINTO, . (2022) ANALISA PENGARUH KETEBALAN LAPISAN 3D PRINTING TERHADAP KEKUATAN TEKAN MENGGUNAKAN BAHAN ABS DAN PLA. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text COVER.pdf Download (974kB)
	Text BAB 1.pdf Download (205kB)
	Text BAB 2.pdf Restricted to Registered users only Download (407kB) | Request a copy
	Text BAB 3.pdf Restricted to Registered users only Download (747kB) | Request a copy
	Text BAB 4.pdf Restricted to Registered users only Download (466kB) | Request a copy
	Text BAB 5.pdf Restricted to Registered users only Download (121kB) | Request a copy
	Text DAFTAR PUSTAKA.pdf Download (247kB)
	Text LAMPIRAN.pdf Restricted to Registered users only Download (1MB) | Request a copy

Abstract

*ABSTRAK* 3D printing adalah salah satu proses additive manufacturing, dengan konsep mengubah desain digital tiga dimensi dari CAD (Computer Aided Design) dan selanjutnya dicetak dengan menambahkan lapis demi lapis material hingga membentuk suatu produk padat tiga dimensi. Penelitian ini bertujuan untuk mengetahui kekuatan tekan rata-rata dari spesimen hasil pencetakan 3D printing dengan menggunakan filamen ABS (acrylonitrile butadiene styrene) dan PLA (polyatic acid) dengan variasi ketebalan layer thickness 0.15 mm, 0.25 mm, dan 0.35 mm. Metode penelitian yang digunakan dalam penelitian ini adalah metode eksperimen dengan membuat beberapa variasi spesimen dari material ABS dan material PLA sesuai dengan standar ASTM D695 menggunakan mesin 3D printer dengan parameter layer thickness dan setelah itu dilakukan pengujian tekan untuk mengetahui kekuatan tekan dari benda hasil eksperimen. Berdasarkan data hasil pengujian yang telah didapatkan, spesimen yang dicetak menggunakan filamen polylatic acid (PLA) memiliki kekuatan tekan lebih besar dari spesimen yang dicetak menggunakan filament acrylonitrile butadine styrene (ABS) yang terdapat pada spesimen dengan layer thickness 0.15 mm sebesar 72.19 Mpa. Sedangkan untuk proses pencetakan yang efisien dari kedua filamen ada pada layer thickness 0.35 mm dengan waktu pencetakan selama 21.3 menit. Jadi, penggunaan filamen polylatic acid (PLA) lebih efektif dibandingkan filamen acrylonitrile butadine styrene (ABS). Kata Kunci: 3D Printing, Layer Thickness, ABS, PLA, Uji Tekan. *ABSTRACT* 3D printing is one of the additive manufacturing processes, with the concept of changing the three-dimensional digital design of CAD (Computer Aided Design) and then printing by adding layer by layer of material to form a three-dimensional solid product. This study aims to determine the average compressive strength of 3D printing specimens using ABS (acrylonitrile butadiene styrene) and PLA (polyatic acid) filaments with variations in layer thicknesses of 0.15 mm, 0.25 mm, and 0.35 mm. The research method used in this study is an experimental method by making several specimen variations of ABS material and PLA material in accordance with ASTM D695 standards using a 3D printer machine with layer thickness parameters and after that a press test is carried out to determine the compressive strength of the experimental object. Based on the test data that has been obtained, specimens printed using polylatic acid (PLA) filaments have a greater compressive strength than specimens printed using acrylonitrile butadine styrene (ABS) filaments found in specimens with a thickness layer of 0.15 mm of 72.19 Mpa. As for the efficient printing process of the two filaments, it is on a thickness layer of 0.35 mm with a printing time of 21.3 minutes. So, the use of polylatic acid (PLA) filaments is more effective than acrylonitrile butadine styrene (ABS) filaments. Keywords: 3D Printing, Layer Thickness, ABS, PLA, Press Test.

Item Type:	Thesis (Sarjana)
Additional Information:	1) Ahmad Kholil,S.T.,M.T. 2) Dr.Eko Arif Syaefudin,M.T.
Subjects:	Sains > Fisika Teknologi dan Ilmu Terapan > Teknologi (umum) Teknologi dan Ilmu Terapan > Teknik Mesin, Mekanika Teknik Teknologi dan Ilmu Terapan > Teknik Energi
Divisions:	FT > S1 Pendidikan Teknik Mesin
Depositing User:	Users 15285 not found.
Date Deposited:	29 Aug 2022 06:08
Last Modified:	29 Aug 2022 06:08
URI:	http://repository.unj.ac.id/id/eprint/33590

Actions (login required)

View Item