PENGARUH FRAKSI VOLUME SERAT DAN PERLAKUAN ALKOHOL ABSOLUTE TERHADAP KEKUATAN IMPAK KOMPOSIT SERAT BAMBU AMPEL (BAMBUSA VULGARIS)

HENI PRASUTIO, . (2012) PENGARUH FRAKSI VOLUME SERAT DAN PERLAKUAN ALKOHOL ABSOLUTE TERHADAP KEKUATAN IMPAK KOMPOSIT SERAT BAMBU AMPEL (BAMBUSA VULGARIS). Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text Pengaruh Fraksi Volume Serat dan Perlakuan Alkohol Absolute terhadap Kekuatan Impak Komposit Serat Bambu Ampel (Bambusa v~1.pdf Download (255kB)
	Text 3. LEMBAR PENGESAHAN(1).pdf Download (75kB)
	Text 4. KATA PENGANTAR(1).pdf Download (84kB)
	Text 9. BAB I(1).pdf Download (108kB)
	Text 10. BAB II(1).pdf Download (271kB)
	Text 13. BAB V.pdf Download (99kB)
	Text 12. BAB IV(1).pdf Download (191kB)
	Text 1. Cover(1).pdf Download (79kB)
	Text 5.DAFTAR ISI(1).pdf Download (83kB)
	Text 11. BAB III(1).pdf Download (222kB)

Abstract

Penelitian bertujuan untuk mengetahui pengaruh fraksi volume serat dan perlakuan perendaman alkohol absolute yang bervariasi terhadap kekuatan impak komposit serat bambu ampel (Bambusa vulgaris) yang dihasilkan melalui pengujian impak metode charpy. Penelitian ini dilakukan di Sentra Teknologi Polimer – BPPT PUSPITEK Tangerang pada tahun akademik 2011/2012. Metode penelitian adalah eksperimen dengan jumlah sampel sebanyak 42 sampel. Komposit yang dibuat menggunakan penguat serat bambu ampel dengan matrik polyester jenis (UPR) Yukalac 157 BQTN-EX dengan variasi komposisi fraksi volume serat 15%, 25%, dan 35% sedangkan variasi perlakuan perendaman serat dengan alkohol absolute 2 jam, 4 jam, dan 6 jam dengan komposisi fraksi volume 25%. Pengujian yang dilakukan pada komposit serat bambu yaitu pengujian impak metode charpy berdasarkan standar ISO 179. Hasil penelitian menunjukkan bahwa kekuatan impak tertinggi terdapat pada komposit dengan fraksi volume 35% sebesar 51,22 kJ/m2 sedangkan variasi perlakuan perendaman yang paling optimum terdapat pada komposit serat dengan perlakuan perendaman alkohol absolute selama 2 jam dengan fraksi volume 25% sebesar 34,52 kJ/m2. ***** The study aimed to investigate the effect of fiber volume fraction and absolute alcohol treatment that varies with the impact strength of bamboo fiber composite Ampel (Bambusa vulgaris) produced through testing Charpy impact method. The research was conducted at the Center for Polymer Technology - BPPT PUSPITEK Tangerang in the academic year 2011/2012. The method of research is an experiment with a sample of as many as 42 samples. Composites made using bamboo fibers Ampel with polyester matrix type (UPR) Yukalac 157 BQTN-EX with the composition variation of fiber volume fraction of 15%, 25%, and 35%, while the variation of fiber submersion treatment with absolute alcohol 2 hours, 4 hours, and 6 hours with 25% volume fraction composition. Tests were performed on the bamboo fiber composite method of Charpy impact test according to standard ISO 179. Research results show that the highest impact strength contained in the composite with 35% volume fraction amounted 51.22 kJ/m2 whereas the submersion treatment variations found in most optimum fiber composites with absolute alcohol submersion treatment for 2 hours with 25% volume fraction amounted to 34.52 kJ/m2.

Item Type:	Thesis (Sarjana)
Additional Information:	1). Siska Titik Dwijayati, M. T. ; 2). Drs. Agus Dudung R, M. Pd.
Subjects:	Teknologi dan Ilmu Terapan > Teknik Mesin, Mekanika Teknik
Divisions:	FT > S1 Pendidikan Teknik Mesin
Depositing User:	Users 14685 not found.
Date Deposited:	29 Aug 2022 01:48
Last Modified:	29 Aug 2022 01:48
URI:	http://repository.unj.ac.id/id/eprint/33669

Actions (login required)

View Item