PENGARUH KADAR PEREKAT PHENOL FORMALDEHIDA PADA PEMBUATAN PAPAN PARTIKEL BAMBU SEMBILANG`TERHADAP SIFAT FISIS DAN MEKANIS SESUAI SNI 03-2105-2006

PONCO YULISTIO, . (2013) PENGARUH KADAR PEREKAT PHENOL FORMALDEHIDA PADA PEMBUATAN PAPAN PARTIKEL BAMBU SEMBILANG`TERHADAP SIFAT FISIS DAN MEKANIS SESUAI SNI 03-2105-2006. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text Abstrak Inggrs.pdf Download (53kB)
	Text Abstrak Ind.pdf Download (38kB)
	Text BAB II.pdf Download (159kB)
	Text BAB III.pdf Download (1MB)
	Text BAB IV.pdf Download (359kB)
	Text Daftar Isi.pdf Download (118kB)
	Text Cover Ponco.pdf Download (18kB)
	Text Halaman pengesahan.pdf Download (31kB)
	Text Kata pengantar.pdf Download (70kB)
	Text BAB I.pdf Download (117kB)
	Text BAB V.pdf Download (100kB)

Abstract

Tujuan penelitian ini adalah untuk mengetahui perbedaan sifat fisis dan mekanis papan partikel bambu yang menggunakan kadar perekat dengan persentase sebesar 6%, 8%, 10% dan 12%. Penelitian ini juga untuk mengetahui apakah nilai pengujian papan partikel bambu memenuhi standar papan partikel, dengan berdasarkan standar pengujian SNI 03-2105-2006. Penelitian ini dilaksanakan di Laboratorium UPT Balai Litbang Biomaterial LIPI Cibinong Bogor. Waktu penelitian ini dilaksanakan pada bulan Mei sampai Juli 2012. Bahan baku yang digunakan pada penelitian ini adalah bambu sembilang dan perekat Phenol Formaldehyde untuk pembuatan papan partikel dengan kadar perekat 6%, 8%, 10% dan 12%. Pada pengujian ini dilakukan pengujian fisis yaitu kadar air, dan kerapatan, penyerapan air dan pengembangan tebal. Pada pengujian mekanis terdiri dari pengujian MOE, MOR, kuat rekat internal dan kuat cabut sekrup. Digunakan sampel sebanyak 4 buah setiap pengujian dan berjumlah 144 sampel untuk semua pengujian. Kesimpulan dari penelitian ini adalah nilai optimum yang dihasilkan dari pengujian berdasarkan SNI 03-2105-2006 yaitu: kadar air 8,21% dengan kadar perekat 10%, kerapatan 0,67 g/cm³ dengan kadar perekat 12%, penyerapan air 7,23% dengan kadar perekat 10%, pengembangan tebal 9,00% dengan kadar perekat 12% MOE 11904,50 kg/cm² dengan kadar perekat 12%, MOR 145,683 kg/cm² dengan kadar perekat 12%, Internal Bond 5,07 kg/cm² dengan kadar perekat 12%, kuat cabut sekrup 38,22 kgf dengan kadar perekat 12%. Nilai-nilai papan partikel bambu yaitu kadar air, kerapatan, pengembangan tebal, MOR, kuat rekat internal dan kuat cabut sekrup memenuhi standar SNI 03-2105-2006: Papan Partikel. ***** The purpose of this study is to determine the differences in physical and mechanical properties of bamboo particleboard using adhesive levels with the percentage of 6%, 8%, 10% and 12%. This study is also to determine whether the value of testing bamboo particleboard included in the standard particleboard, based on standard testing SNI 03-2105-2006. This research was conducted in the Laboratory of Research and Development Unit For Biomaterials LIPI Cibinong Bogor. The study was conducted in May and July 2012. Raw materials used in this study are bamboo Sembilang and Phenol Formaldehyde adhesive for manufacturing particleboard adhesive levels 6%, 8%, 10% and 12%. The Physical properties tests were moisture content, thickness swelling, water absortion and density ; while the mechanical properties test were bending (MOE and MOR), internal bond, screw withdrawal. Each test was used 4 samples and total of 144 samples for all test. The conclusion of this study is the optimum value resulting from testing by SNI 03-2105-2006 namely: moisture content of 8.21% with 10% adhesive content, density of 0.67 g / cm ³ with 12% adhesive content, water absorption of 7.23% with adhesive content of 10%, 9.00% Thicknes swelling with adhesive content of 12% MOE 22641.93 kg / cm ² with a adhesive content of 12%, MOR 145.683 kg / cm² with a adhesive content of 12%, Internal Bond 5.07 kg / cm ² with 12% adhesive content, Screw withdrawal 38.22 kgf adhesive content 12%. The values of bamboo particleboard that is moisture content, density, water absorption, Thickness swelling, MOE, MOR, internal bond and screw withdrawal of particle Board fulfil SNI standards.

Item Type:	Thesis (Sarjana)
Additional Information:	1). Drs. Prihantono, M.Eng. ; 2). Dra. Nira Nasution, M.Pd. ; 3). Prof. Dr. Subyakto, M.Sc.
Subjects:	Teknologi dan Ilmu Terapan > Teknik Sipil
Divisions:	FT > S1 Pendidikan Teknik Sipil
Depositing User:	Users 14685 not found.
Date Deposited:	29 Aug 2022 12:01
Last Modified:	29 Aug 2022 12:01
URI:	http://repository.unj.ac.id/id/eprint/33703

Actions (login required)

View Item