ANALISA PENGARUH VARIASI SUHU HEATED-CHAMBER 3D PRINTING TERHADAP KEKUATAN TEKAN DENGAN BAHAN ACRYLONITRILE BUTADINE STYRENE (ABS)

MUHAMAD KHOIRUL ROHIM, . (2023) ANALISA PENGARUH VARIASI SUHU HEATED-CHAMBER 3D PRINTING TERHADAP KEKUATAN TEKAN DENGAN BAHAN ACRYLONITRILE BUTADINE STYRENE (ABS). Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text COVER.pdf.pdf Download (1MB)
	Text BAB 1.pdf.pdf Download (230kB)
	Text BAB 2.pdf.pdf Restricted to Registered users only Download (981kB) | Request a copy
	Text BAB 3.pdf.pdf Restricted to Registered users only Download (645kB) | Request a copy
	Text BAB 4.pdf.pdf Restricted to Registered users only Download (787kB) | Request a copy
	Text BAB 5.pdf.pdf Restricted to Registered users only Download (153kB) | Request a copy
	Text DAFTAR PUSTAKA.pdf.pdf Download (284kB)
	Text LAMPIRAN.pdf.pdf Restricted to Registered users only Download (929kB) | Request a copy

Abstract

Tiga dimensi (3D) Printing fused deposition modeling (FDM) adalah salah satu proses additive manufacturing (AM) dengan konsep merubah desain digital tiga dimensi dari Computer Aided Design (CAD) dan kemudian mencetak lapis demi lapis material sampai membentuk suatu produk tiga dimensi dengan bentuk padat. Pada penelitian ini bertujuan untuk mengetahui pengaruh suhu ruangan terhadap nilai kekuatan tekan hasil dari proses pencetakan 3D printer dengan bahan Acrylonitrile Butadiene Styrene (ABS) menggunakan standar ASTM D695 dengan variasi Suhu ruangan dengan suhu inlet 80°C, 100°C, dan juga heater off. Pada metode penelitian ini merupakan metode eksperimen dengan membuat beberapa variasi spesimen dari bahan Acrylonitrile Butadiene Styrene (ABS) menggunakan 3D printer dengan menggunakan variasi suhu ruangan, setelah itu dilakukan pengujian struktur mikro dan dilakukan kekuatan tekan untuk mengetahui nilai kekuatan tekan dari hasil penelitian. Berdasarkan hasil penelitian, pengaruh dari suhu ruangan mempengaruhi ikatan antar layer pada spesimen, spesimen yang menggunakan heater off menghasilkan suhu ruangan sebesar 36°C sememiliki nilai kekuatan tekan sebesar 27,065 MPa dan spesimen yang menggunakan suhu inlet 80°C mengahsilkan suhu ruangan sebesar 57°C memiliki nilai kekuatan tekan sebesar 26,709 MPa. Sedangkan hasil pada spesimen yang menggunakan suhu inlet 100°C mengahsilkan suhu ruangan sebesar 63°C memiliki nilai kekuatan tekan sebesar 24,791 MPa. ***** Three dimension (3D) Printing fused deposition modeling (FDM) is one of the additive manufacturing (AM) processes with the concept of changing the three-dimensional digital design of Computer Aided Design (CAD) and then printing layer by layer of material until it forms a three-dimensional product with a solid shape. This study aims to determine the effect of room temperature on the compressive strength value as a result of the 3D printer printing process with Acrylonitrile Butadiene Styrene (ABS) material using ASTM D695 standard with room temperature variations with an inlet temperature of 80°C, 100°C, and also heater off. This research method is an experimental method by making several specimen variations from Acrylonitrile Butadiene Styrene (ABS) material using a 3D printer using room temperature variations, after which microstructure testing is carried out and compressive strength is carried out to determine the compressive strength value of the research results. Based on the results of the study, the influence of room temperature affects the bond between layers on the specimen, specimens using heater off produce a room temperature of 36°C with a compressive strength value of 27,065 MPa and specimens using an inlet temperature of 80°C produce a room temperature of 57°C have a compressive strength value of 26,709 MPa. Meanwhile, the results on specimens using an inlet temperature of 100°C resulted in a room temperature of 63°C having a compressive strength value of 24,791 MPa.

Item Type:	Thesis (Sarjana)
Additional Information:	1). Ahmad Kholil, S.T., M.T. ; 2). Dr. Eko Arif Syaefudin, M.T.
Subjects:	Teknologi dan Ilmu Terapan > Teknik Mesin, Mekanika Teknik
Divisions:	FT > S1 Pendidikan Teknik Mesin
Depositing User:	Users 17250 not found.
Date Deposited:	27 Feb 2023 02:26
Last Modified:	27 Feb 2023 02:26
URI:	http://repository.unj.ac.id/id/eprint/37268

Actions (login required)

View Item