PENGARUH VARIASI KADAR POLIMER OPAQUE DAN NATRIUM ALUMINOSILIKAT SEBAGAI PENGGANTI PIGMEN PUTIH TITANIUM DIOKSIDA DALAM CAT

EMILY PRISCILLIA, . (2023) PENGARUH VARIASI KADAR POLIMER OPAQUE DAN NATRIUM ALUMINOSILIKAT SEBAGAI PENGGANTI PIGMEN PUTIH TITANIUM DIOKSIDA DALAM CAT. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text COVER.pdf Download (2MB)
	Text BAB 1.pdf Download (217kB)
	Text BAB 2.pdf Restricted to Registered users only Download (539kB) | Request a copy
	Text BAB 3.pdf Restricted to Registered users only Download (285kB) | Request a copy
	Text BAB 4.pdf Restricted to Registered users only Download (1MB) | Request a copy
	Text BAB 5.pdf Restricted to Registered users only Download (189kB) | Request a copy
	Text DAFTAR PUSTAKA.pdf Download (239kB)
	Text LAMPIRAN.pdf Restricted to Registered users only Download (571kB) | Request a copy

Abstract

Natrium aluminosilikat dan polimer opaque merupakan fillers yang apabila kadarnya divariasikan dengan titanium dioksida (TiO2) dalam cat, berpotensi menggantikan kadar penggunaan TiO2 yang bersifat karsinogenik. Pada penelitian ini, untuk mengidentifikasi pengaruh variasi kadar TiO2 dan fillers terhadap kinerja cat yang dihasilkan, maka dilakukan pembuatan cat melalui proses penggilingan dan kemudian diuji kinerjanya berdasarkan pada Connell (In-house) Testing Method. Variasi kadar penggantian TiO2 yang digunakan sebesar 0%, 25%, 50%, 75% dan 100% penggantian dengan perbandingan fillers 1:1. Variasi kadar TiO2 dan fillers berpengaruh terhadap kinerja dari sampel cat yang dihasilkan, di mana sampel 3 (50% penggantian pigmen utama TiO2) menghasilkan cat matt dengan sifat optik terbaik, yakni warna (97,61) dan opacity (91,16%) serta ketahanan terhadap sinar UV yang baik dengan nilai perbedaan warna (∆E) sebesar 0,82 (tidak terlihat perbedaan warna baik sebelum maupun sesudah paparan sinar UV). Hal ini didasarkan atas hasil FTIR yang menunjukkan adanya ikatan Ti-O-Si dan hasil SEM yang menunjukkan partikel TiO2 yang teradsorpsi pada permukaan natrium aluminosilikat sehingga memberikan kemampuan penghamburan cahaya yang baik serta polimer opaque yang terdispersi secara merata pada pengikat, sehingga membantu meningkatkan opacity dari film cat. Hal ini membuktikan bahwa kombinasi penggunaan TiO2, natrium aluminosilikat dan polimer opaque dengan kadar penggantian pigmen utama TiO2 sebesar 50% mampu memberikan kinerja yang baik sebagai pigmen dalam cat. ***** Sodium aluminosilicate and opaque polymer are fillers which, if the levels are varied with titanium dioxide (TiO2) in paint, have the potential to replace TiO2 levels which are carcinogenic. In this study, to identify the effect of varying levels of TiO2 and fillers on the performance of the paint produced, then the paint was made through a grinding process and then its performance was tested based on the Connell (In-house) Testing Method. Variations of TiO2 replacement level used were 0%, 25%, 50%, 75% and 100% replacement with a fillers ratio of 1:1. Variations of TiO2 and fillers level affected the performance of the resulting paint samples, where the sample 3 (50% replacement of the main TiO2 pigment) produced matt paint with the best optical properties, including color (97.61) and opacity (91.16%) also good resistance to UV light with a color difference value (∆E) of 0.82 (no visible color difference either before or after exposure to UV light). This is based on the FTIR results which show the presence of Ti-O-Si bonds and SEM results which show TiO2 particles adsorbed on the surface of sodium aluminosilicate so as to provide good light scattering capabilities and opaque polymers which disperse evenly on the binder, thereby helping to increase the opacity of the paint film. This proves that the combination of using TiO2, sodium aluminosilicate and opaque polymer with a replacement level of the main TiO2 pigment of 50% is able to provide good performance as a pigment in paint.

Item Type:	Thesis (Sarjana)
Additional Information:	1). Dr. Yusmaniar, M.Si. ; 2). Dr. Nurudin Budiman, M.Si.
Subjects:	Sains > Sains, Ilmu Pengetahuan Alam Sains > Kimia
Divisions:	FMIPA > S1 Kimia
Depositing User:	Users 19192 not found.
Date Deposited:	01 Sep 2023 06:31
Last Modified:	01 Sep 2023 06:31
URI:	http://repository.unj.ac.id/id/eprint/40277

Actions (login required)

View Item