SINTESIS DAN KARAKTERISASI MATERIAL SENSOR ELEKTROKIMIA BERBASIS NiFeOx UNTUK PENDETEKSIAN ZAT DOPAMIN

ANGGITA PUTRI YASIN, . (2023) SINTESIS DAN KARAKTERISASI MATERIAL SENSOR ELEKTROKIMIA BERBASIS NiFeOx UNTUK PENDETEKSIAN ZAT DOPAMIN. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text COVER.pdf Download (669kB)
	Text BAB I.pdf Download (201kB)
	Text BAB II.pdf Restricted to Registered users only Download (251kB) | Request a copy
	Text BAB III.pdf Restricted to Registered users only Download (202kB) | Request a copy
	Text BAB IV.pdf Restricted to Registered users only Download (311kB) | Request a copy
	Text BAB V.pdf Restricted to Registered users only Download (268kB) | Request a copy
	Text DAFTAR PUSTAKA.pdf Download (329kB)
	Text LAMPIRAN.pdf Restricted to Registered users only Download (299kB) | Request a copy
	Text DAFTAR RIWAYAT HIDUP.pdf Restricted to Registered users only Download (209kB) | Request a copy

Abstract

*ABSTRAK* ------- Telah dilakukan sintesis NiFeOx sebagai material sensor elektrokimia untuk pendeteksian molekul biomarker seperti dopamine, glucose, uric acid, dan ascorbic acid. Dopamin (DA), glukosa, asam urat (UA), dan asam askorbat (AA) masing-masing ada didalam tubuh manusia sebagai neurotransmitter, sumber energi, metabolisme protein, dan antioksidan. Tingkat abnormal dari biomarker tersebut dapat menyebabkan penyakit tertentu dan dapat diukur serta ditentukan dengan menggunakan sensor elektrokimia. Modifikasi elektroda dengan menggunakan NiFe untuk meningkatkan selektivitas dan sensitivitas terhadap pendeteksian biomarker. Sintesis material tersebut dilakukan dengan menggunakan metode hidrotermal dengan suhu 120o selama 12 jam lalu sampel tersebut dimodifikasi dengan menggunakan molten salt (lelehan garam) berupa KNO3 (Kalium Nitrat) dan KOH (Kalium Hidroksida). Karakterisasi dilakukan dengan menggunakan XRD, FESEM, dan BET. Dari data tersebut menunjukkan bahwa dengan penambahan molten salt khususnya KNO3 memiliki luas permukaan yang tinggi ditandai dengan luas permukaan sebesar 125.6 m2/g Hal ini juga menunjukkan bahwa semakin tinggi luas permukaan sampel maka semakin bagus performa dari sampel .Pengujian sensitivitas dan selektivitas digunakan dengan menggunakan metode elektrokimia yaitu dengan pengujian cyclic voltammetry (CV) dan Electrochemical Impedance Spectroscopy (EIS) didapatkan bahwa pada molekul dopamine dengan sampel GCE@NiFeOx_MS KNO3 memiliki arus puncak terbesar dibandingkan dengan sampel yang lain ditandai dengan puncak arus GCE@NiFeOx_MS KNO3 sebesar 15.3012 µA pada tegangan 0.3393 V. Hal ini dikarenakan sampel NiFeOx_MS KNO3 memiliki luas permukaan yang besar dan konduktivitas elektron yang sangat baik. Kata Kunci : NiFe, biomarker, molten salt, KNO3, dopamin. *ABSTRACT* Synthesis of NiFeOx has been carried out as an electrochemical sensor material for the detection of biomarker molecules such as dopamine, glucose, uric acid, and ascorbic acid. Dopamine (DA), glucose, uric acid (UA), and ascorbic acid (AA) each exist in the human body as neurotransmitters, energy sources, protein metabolism, and antioxidants. Abnormal levels of these biomarkers can cause certain diseases and can be measured and determined using electrochemical sensors. Electrode modification using NiFe to increase selectivity and sensitivity for biomarker detection. The synthesis of the material was carried out using the hydrothermal method at 120◦ for 12 hours and then the sample was modified using molten salt (salt melt) in the form of KNO3 (Potassium Nitrate) and KOH (Potassium Hydroxide). Characterization was carried out using XRD, FESEM, and BET. From these data it shows that with the addition of molten salt, especially KNO3 has a high surface area characterized by a surface area of 125.6 m2/g This also shows that the higher the surface area of the sample, the better the performance of the sample. Sensitivity and selectivity tests are used using electrochemical methods, namely by testing cyclic voltammetry (CV) and Electrochemical Impedance Spectroscopy (EIS) found that the dopamine molecule in the sample GCE@NiFeOx_MS KNO3 has the largest peak current compared to other samples marked by the peak current GCE@NiFeOx_MS KNO3 of 15.3012 µA at a voltage of 0.3393 V. This is due to the sample NiFeOx_MS KNO3 has a large surface area and excellent electron conductivity. Keywords: NiFe,biomarker, molten salt, KNO3, dopamine.

Item Type:	Thesis (Sarjana)
Additional Information:	1) Dr.Anggara Budi Susila, M.Si. ; 2) Angga Hermawan Ph.D.
Subjects:	Sains > Fisika
Divisions:	FMIPA > S1 Fisika
Depositing User:	Users 19267 not found.
Date Deposited:	07 Sep 2023 02:05
Last Modified:	07 Sep 2023 02:05
URI:	http://repository.unj.ac.id/id/eprint/41260

Actions (login required)

View Item