PENGGUNAAN STYROFOAM COATING SEBAGAI VARIASI AGREGAT KASAR DENGAN BAHAN TAMBAH SUPERPLASTICIZER TERHADAP KUAT TEKAN DAN KUAT LENTUR BETON RINGAN

BUDI PRIANTORO, . (2020) PENGGUNAAN STYROFOAM COATING SEBAGAI VARIASI AGREGAT KASAR DENGAN BAHAN TAMBAH SUPERPLASTICIZER TERHADAP KUAT TEKAN DAN KUAT LENTUR BETON RINGAN. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text 1. COVER - 5415152014.pdf Download (369kB)
	Text 2. ABSTRAK.pdf Download (560kB)
	Text 3. LEMBAR PENGESAHAN.pdf Download (632kB)
	Text 4. LEMBAR ORISINALITAS.pdf Download (635kB)
	Text 5. SURAT PERNYATAAN PERSETUJUAN PUBLIKASI.pdf Download (305kB)
	Text 6. KATA PENGANTAR.pdf Download (519kB)
	Text 7. DAFTAR ISI.pdf Download (615kB)
	Text 8. BAB 1.pdf Download (672kB)
	Text 9. BAB 2.pdf Restricted to Registered users only Download (1MB) | Request a copy
	Text 10. BAB 3.pdf Restricted to Registered users only Download (1MB) | Request a copy
	Text 11. BAB 4.pdf Restricted to Registered users only Download (1MB) | Request a copy
	Text 12. BAB 5.pdf Download (637kB)
	Text 14. DAFTAR PUSTAKA.pdf Download (580kB)
	Text 15. LAMPIRAN.pdf Download (4MB)
	Text 16. DAFTAR RIWAYAT HIDUP.pdf Download (277kB)

Abstract

Beton adalah salah satu material yang banyak digunakan dalam konstruksi bangunan. Dalam kebutuhan non-struktural, penggunaan beton normal menyebabkan beban mati yang besar pada elemen. Salah satu upaya untuk mengatasi masalah ini adalah inovasi beton ringan, karena beton ringan memiliki berat jenis yang rendah yaitu 1900 kg/m3. Dalam hal ini pembuatan beton ringan dengan menggunakan agregat kasar dari bahan styrofoam. Agregat styrofoam dilakukan treatment coating dengan cara melapisi dengan pasta semen, fly ash dan air. Dalam penelitian ini direncanakan beberapa variasi styrofoam coating, yaitu: 0%, 10%, 20%, 30%, dan 40% terhadap agregat kasar dengan penambahan Superplasticizer Sikament LN dengan kadar 1% terhadap berat semen. Eksperimen ini dilakukan dengan membuat benda uji berbentuk silinder dengan ukuran 10 cm × 20 cm untuk kuat tekan dan benda uji berbentuk balok dengan ukuran 15 cm × 15 cm × 60 cm untuk kuat lentur. Hasil menunjukan berat isi beton semakin berkurang seiring dengan bertambahnya variasi agregat styrofoam coating ke dalam campuran beton. Hasil rata-rata kuat tekan masing-masing pada variasi 0%, 10%, 20%, 30% dan 40% secara berturut-turut adalah 14.96 MPa, 11.47 MPa, 10,44 MPa, 7.26 MPa dan 5.6 MPa. Sedangkan hasil rata-rata kuat lentur pada masing-masing pada variasi 0%, 10%, 20%, 30% dan 40% secara berturut-turut adalah 2.96 MPa, 2.22 MPa, 1.87 MPa, 1,69 MPa dan 1.51 MPa. Concrete is one material that is widely used in building construction. In non-structural needs, the use of normal concrete causes a large dead load on the element. One effort to overcome this problem is the innovation of lightweight concrete, because lightweight concrete has a low specific gravity of 1900 kg/m3. In this case the manufacture of lightweight concrete using coarse aggregate from styrofoam materials. Styrofoam aggregates are treated by coating them with cement paste, fly ash and water. In this research, several variations of styrofoam coating are planned, namely: 0%, 10%, 20%, 30%, and 40% based on coarse aggregate with the addition of Sikament Superplasticizer LN with 1% content based on cement weight. This experiment was carried out by making cylindrical specimens measuring 10 cm × 20 cm for pressure strength and beam-shaped specimens measuring 15 cm × 15 cm × 60 cm for flexural strength. The results show the concrete weight weight decreases along with the increasing variation of styrofoam coating aggregates into the concrete mixture. The results of the average compressive strength of each variation 0%, 10%, 20%, 30% and 40% respectively are 14.96 MPa, 11.47 MPa, 10.44 MPa, 7.26 MPa and 5.6 MPa. While the results of the average flexural strength in each of the variations of%, 10%, 20%, 30% and 40% are 2.96 MPa, 2.22 MPa, 1.87 MPa, 1.69 MPa and 1.51 MPa.

Item Type:	Thesis (Sarjana)
Additional Information:	1.) Dra. Daryati, MT 2.) Kusno Adi Sambowo, ST, Ph.D
Subjects:	Teknologi dan Ilmu Terapan > Teknik Sipil Teknologi dan Ilmu Terapan > Konstruksi Bangunan
Divisions:	FT > S1 Pendidikan Teknik Bangunan
Depositing User:	Users 1071 not found.
Date Deposited:	27 Mar 2020 18:26
Last Modified:	27 Mar 2020 18:26
URI:	http://repository.unj.ac.id/id/eprint/4250