ANALISIS PENGARUH SUHU HEATED CHAMBER PADA MESIN 3 DIMENSI (3D) PRINTING TERHADAP UJI TEKAN DENGAN BAHAN POLYLACTIC ACID (PLA)

KHARISMA HANDAYANI, . (2024) ANALISIS PENGARUH SUHU HEATED CHAMBER PADA MESIN 3 DIMENSI (3D) PRINTING TERHADAP UJI TEKAN DENGAN BAHAN POLYLACTIC ACID (PLA). Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text COVER.pdf Download (2MB)
	Text BAB 1.pdf Download (352kB)
	Text BAB 2.pdf Restricted to Registered users only Download (827kB) | Request a copy
	Text BAB 3.pdf Restricted to Registered users only Download (1MB) | Request a copy
	Text BAB 4.pdf Restricted to Registered users only Download (1MB) | Request a copy
	Text BAB 5.pdf Restricted to Registered users only Download (378kB) | Request a copy
	Text DAFTAR PUSTAKA.pdf Download (344kB)
	Text LAMPIRAN.pdf Restricted to Registered users only Download (1MB) | Request a copy

Abstract

ANALISIS PENGARUH SUHU HEATED CHAMBER PADA MESIN 3 DIMENSI (3D) PRINTING TERHADAP UJI TEKAN DENGAN BAHAN POLYLACTIC ACID (PLA) Kharisma Handayani Dosen Pembimbing : Ahmad Kholil, S.T., M.T., dan Dr. Eko Arif Syaefudin, M.T. ABSTRAK Tujuan dilakukan penelitian ini adalah untuk mencari tahu pengaruh suhu heated chamber atau pemanasan suhu ruang pada mesin 3D printing terhadap nilai uji tekan. Penelitian ini dimulai dengan studi literatur dan tinjauan pustaka untuk memahami dasar teori serta penelitian terkait yang pernah dilakukan sebelumnya. Alat dan bahan penelitian ini menggunakan mesin 3D printing merk Creality Ender 5 Plus yang sudah di modifikasi dengan heated chamber atau pemanas ruang, serta filamen yang digunakan adalah Polylactic Acid (PLA). Desain spesimen dibuat sesuai dengan standar ASTM D695. Proses pencetakan dilakukan dengan mesin 3D printing menggunakan empat variasi suhu inlet yaitu 40°C, 55°C, 60°C, dan non heater. Berdasarkan hasil penelitian menunjukkan bahwa suhu inlet secara signifikan mempengaruhi kekuatan tekan produk, di mana suhu tertentu menghasilkan kekuatan maksimal. Nilai gaya luluh pada suhu non heater sebesar 4,51 kN. Nilai gaya luluh pada suhu 40°C sebesar 4,40 kN. Nilai gaya luluh pada suhu 55°C sebesar 4,07 kN. Dan nilai gaya luluh tertinggi terjadi pada suhu 60°C sebesar 5,01 kN. Nilai tegangan luluh pada suhu non heater adalah sebesar 94,02 MPa. Nilai tegangan luluh pada suhu 40°C sebesar 91,80 MPa. Nilai tegangan luluh pada suhu 55°C sebesar 84,86 MPa. Sedangkan nilai tegangan luluh tertinggi terjadi pada suhu 60°C sebesar 104,38 MPa. Pengaruh temperatur heated chamber berdampak signifikan terhadap nilai gaya luluh (kN) dan tegangan luluh (MPa). Kata Kunci: 3D Printing, Polylactic Acid, Heated Chamber, Uji Tekan ANALYSIS OF THE EFFECT OF HEATED CHAMBER TEMPERATURE ON 3 DIMENSION (3D) PRINTING MACHINE ON COMPRESSION TEST WITH POLYLACTIC ACID (PLA) MATERIAL Kharisma Handayani Supervising Professor : Ahmad Kholil, S.T., M.T., and Dr. Eko Arif Syaefudin, M.T. ABSTRACT The purpose of this study is to determine the effect of temperature variations in a heated chamber or room heating on a 3D printing machine on the compressive test values. The research begins with a literature review to understand the theoretical basis and related previous studies. The tools and materials used in this study include a Creality Ender 5 Plus 3D printing machine that has been modified with a heated chamber, and the filament used is Polylactic Acid (PLA). The specimen design follows the ASTM D695 standard. The printing process is carried out using a 3D printing machine with four inlet temperature variations: 40°C, 55°C, 60°C, and non heater. The research results show that inlet temperature variations significantly affect the compressive strength of the product, with certain temperatures yielding maximum strength. The yield strength at the non heater temperature is 4.51 kN. The yield strength at 40°C is 4.40 kN. The yield strength at 55°C is 4.07 kN. The highest yield strength occurs at 60°C with a value of 5.01 kN. The yield stress at the non heater temperature is 94.02 MPa. The yield stress at 40°C is 91.80 MPa. The yield stress at 55°C is 84.86 MPa. The highest yield stress occurs at 60°C with a value of 104.38 MPa. The effect of heated chamber temperature has a significant impact on the value of yield force (kN) and yield stress (MPa). Keywords: 3D Printing, Polylactic Acid, Heated Chamber, Compression Test

Item Type:	Thesis (Sarjana)
Additional Information:	1). Ahmad Kholil, S.T., M.T. 2). Dr. Eko Arif Syaefudin, M.T.
Subjects:	Pendidikan > Pendidikan Teknologi dan Ilmu Terapan > Teknik Mesin, Mekanika Teknik Teknologi dan Ilmu Terapan > Manufaktur
Divisions:	FT > S1 Pendidikan Teknik Mesin
Depositing User:	Kharisma Handayani .
Date Deposited:	25 Jul 2024 00:17
Last Modified:	25 Jul 2024 00:17
URI:	http://repository.unj.ac.id/id/eprint/46222

Actions (login required)

View Item