PENGARUH PENAMBAHAN MAGNESIUM (Mg) TERHADAP STRUKTUR MIKRO DAN KEKERASAN PADA ALUMUNIUM (Al) MELALUI PROSES HOMOGENISASI

AHMAD ARIFUDIN, . (2024) PENGARUH PENAMBAHAN MAGNESIUM (Mg) TERHADAP STRUKTUR MIKRO DAN KEKERASAN PADA ALUMUNIUM (Al) MELALUI PROSES HOMOGENISASI. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text COVER.pdf Download (1MB)
	Text BAB I.pdf Download (159kB)
	Text BAB II.pdf Restricted to Registered users only Download (414kB) | Request a copy
	Text BAB III.pdf Restricted to Registered users only Download (249kB) | Request a copy
	Text BAB IV.pdf Restricted to Registered users only Download (875kB) | Request a copy
	Text BAB V.pdf Restricted to Registered users only Download (135kB) | Request a copy
	Text DAFTAR PUSTAKA.pdf Download (316kB)
	Text LAMPIRAN.pdf Restricted to Registered users only Download (1MB) | Request a copy

Abstract

Aluminium merupakan unsur logam yang banyak digunakan dalam berbagai bidang di industri, diantaranya yaitu industri transportasi, industri pabrikasi, dan juga industri manufaktur. Tujuan penelitian ini adalah untuk menyelidiki pengaruh dari penambahan unsur magnesium (Mg) terhadap kekerasan dan struktur mikro pada aluminium (Al) dengan komposisi Al + dengan variasi penambahan (2Mg, 5Mg, dan 10Mg) melalui proses Homogenisasi. Proses pengecoran dilakukan menggunakan metode pengecoran gravitasi dengan temperatur suhu 800oC lalu selanjutnya dilakukan proses homogenisasi dengan temperatur suhu 400oC dan waktu penahanan selama 2 jam. Spesimen yang sudah dilakukan homogenisasi selanjutnya dilakukan pengujian OES, kekerasan vickers, dan juga struktur mikro. Adapun pengaruh dari penambahan unsur Magnesium dengan variasi 2wt%, 5wt%, dan 10wt% terhadap Aluminium dapat dilihat dari analisa pengujian kekerasan vickers yaitu nilai kekerasan pada raw material alumunium sebesar 36,06 VHN, paduan Al-2Mg sebesar 40,98 VHN, paduan Al-5Mg sebesar 52,62 VHN, dan paduan Al-10Mg sebesar 58,58 VHN. Dan juga dari hasil pengujian struktur mikro menunjukkan bahwa semakin banyak penambahan unsur magnesium pada aluminium maka ukuran butirnya semakin mengecil dan terbentuknya fasa α-Al dan β-Mg. Aluminum is a metal element widely used in various fields in industry, including transportation, manufacturing, and manufacturing industries. The purpose of this study was to investigate the effect of the addition of magnesium (Mg) on the hardness and microstructure of aluminum (Al) with Al + composition with alloy variations (2Mg, 5Mg, and 10Mg) through the homogenization process. The casting process is done using the gravity casting method with a temperature of 800oC and then the homogenization process with a temperature of 400oC and a holding time of 2 hours. The homogenized specimens were then subjected to OES, Vickers hardness, and microstructure testing. As for the effect of the addition of Magnesium elements with variations of 2 wt%, 5 wt%, and 10 wt% to Aluminum can be seen from the analysis of vickers hardness testing, namely the value of hardness in raw aluminum material of 36,06 VHN, Al-2Mg alloy of 40,98 VHN, Al-5Mg alloy of 52,62 VHN, and Al-10Mg alloy of 58,58 VHN. And also from the results of microstructure testing shows that the more the addition of magnesium elements in aluminum, the smaller the grain size and the formation of α-Al and β-Mg phases.

Item Type:	Thesis (Sarjana)
Additional Information:	1). Drs. Syamsuir, M.T. 2). Ahmad Lubi, M.Pd., M.T
Subjects:	Teknologi dan Ilmu Terapan > Teknik Mesin, Mekanika Teknik Teknologi dan Ilmu Terapan > Teknik Pertambangan, Metalurgi Teknologi dan Ilmu Terapan > Manufaktur
Divisions:	FT > D IV Teknologi Rekayasa Manufaktur
Depositing User:	Users 23503 not found.
Date Deposited:	31 Jul 2024 04:34
Last Modified:	31 Jul 2024 04:34
URI:	http://repository.unj.ac.id/id/eprint/47570

Actions (login required)

View Item