SINTESIS MATERIAL KOMPOSIT Fe3O4/SiO2 BERBAHAN BAKU LOKAL UNTUK APLIKASI SERAPAN GELOMBANG MILIMETER

NOVANA DWI ANGGARA PUTRI, . (2024) SINTESIS MATERIAL KOMPOSIT Fe3O4/SiO2 BERBAHAN BAKU LOKAL UNTUK APLIKASI SERAPAN GELOMBANG MILIMETER. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text COVER.pdf Download (1MB)
	Text BAB I.pdf Download (746kB)
	Text BAB II.pdf Restricted to Registered users only Download (404kB) | Request a copy
	Text BAB III.pdf Restricted to Registered users only Download (766kB) | Request a copy
	Text BAB IV.pdf Restricted to Registered users only Download (1MB) | Request a copy
	Text BAB V.pdf Restricted to Registered users only Download (297kB) | Request a copy
	Text DAFTAR PUSTAKA.pdf Download (880kB)
	Text Lampiran.pdf Restricted to Registered users only Download (1MB) | Request a copy

Abstract

Sifat magnetik Fe3O4 dan sifat dielektrik SiO2 dapat menyerap gelombang dengan baik pada frekuensi milimeter. Material Fe3O4/SiO2 disintesis menggunakan metode mechanical milling selama 10 jam dengan konsentrasi 0 wt%, 5 wt%, 10 wt%, 20 wt%, dan 30 wt%. Morfologi permukaan Fe3O4/SiO2 terlihat sangat jelas ketika menggunakan perbesaran 1300x. Setelah milling material Fe3O4/SiO2 memiliki permukaan yang lebih halus dan aglomerasi semakin berkurang. Sifat magnetik material berubah seiring bertambahnya konsentrasi Fe3O4/SiO2. Semakin banyak konsentrasi SiO2, nilai Ms dan Mr semakin menurun, sedangkan nilai Hc semakin meningkat tetapi tidak konstan. Berdasarkan nilai Hc yang didapatkan, Fe3O4/SiO2 termasuk material soft magnetic. Sebelum milling, konsentrasi material Fe3O4/SiO2 yang memiliki nilai RL minimum dan penyerapan paling optimum adalah Fe3O4/SiO2 20 wt% saat frekuensi 35 – 36 GHz dengan penyerapan sebesar 92%. Setelah dilakukan proses milling, material Fe3O4/SiO2 dapat menyerap dengan baik saat frekuensi 34 – 38 GHz pada konsentrasi SiO2 30 wt% dengan penyerapan sebesar 83%. Sedangkan material 0 wt% baru bisa menyerap gelombang milimeter dengan optimum saat frekuensi 39 – 40 GHz dengan penyerapan sebesar 93%. Kata kunci: Fe3O4/SiO2, mechanical milling, gelombang milimeter. ***** Fe3O4's magnetic properties and SiO2's dielectric properties can absorb waves well at millimeter frequencies. Fe3O4/SiO2 material was synthesized using the mechanical milling method for 10 hours with concentrations of 0 wt%, 5 wt%, 10 wt%, 20 wt%, and 30 wt%. The surface morphology of Fe3O4/SiO2 is very clear when viewed at 1300x magnification. After milling, the Fe3O4/SiO2 material has a smoother surface and reduced agglomeration. The magnetic properties of the material change as the concentration of Fe3O4/SiO2 increases. The more concentrations of SiO2, the values of Ms and Mr decrease, whereas the value of Hc increases but is not constant. Based on the Hc value obtained, Fe3O4/SiO2 includes soft magnetic material. Before milling, the Fe3O4/SiO2 material concentration that has the minimum RL value and the most optimal absorption is 20 wt% Fe3O4/SiO2 at a frequency of 35 – 36 GHz with an absorptions of 92%. After the milling process, Fe3O4/SiO2 material can absorb well at frequencies 34 – 38 GHz at a concentration of 30 Wt% SiO2, with absorbtions of 93%. Key word: Fe3O4/SiO2, mechanical milling, millimeter wave.

Item Type:	Thesis (Sarjana)
Additional Information:	1). Prof. Dr. Erfan Handoko, M.Si. ; 2). Prof. Dr. Mangasi Alion Marpaung, M.Si.
Subjects:	Sains > Fisika
Divisions:	FMIPA > S1 Fisika
Depositing User:	Users 24926 not found.
Date Deposited:	12 Aug 2024 05:48
Last Modified:	12 Aug 2024 05:48
URI:	http://repository.unj.ac.id/id/eprint/49797

Actions (login required)

View Item