STUDI PENGARUH VARIASI PREKURSOR PADA NANOPARTIKEL ZnO MENGGUNAKAN EKSTRAK DAUN MORINGA OLEIFERA TERHADAP SIFAT STRUKTUR, MORFOLOGI, OPTIK, DAN GUGUS FUNGSI

ANNISA FEBY NUR RAHMASARI, . (2024) STUDI PENGARUH VARIASI PREKURSOR PADA NANOPARTIKEL ZnO MENGGUNAKAN EKSTRAK DAUN MORINGA OLEIFERA TERHADAP SIFAT STRUKTUR, MORFOLOGI, OPTIK, DAN GUGUS FUNGSI. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text COVER.pdf Download (2MB)
	Text BAB I.pdf Download (2MB)
	Text BAB II.pdf Restricted to Registered users only Download (2MB) | Request a copy
	Text BAB III.pdf Restricted to Registered users only Download (2MB) | Request a copy
	Text BAB IV (PEMBAHASAN).pdf Restricted to Registered users only Download (2MB) | Request a copy
	Text BAB V.pdf Restricted to Registered users only Download (2MB) | Request a copy
	Text DAFTAR PUSTAKA.pdf Download (2MB)
	Text LAMPIRAN-DAFTAR RIWAYAT HIDUP.pdf Restricted to Registered users only Download (2MB) | Request a copy

Abstract

Nanopartikel ZnO telah berhasil disintesis menggunakan metode biosintesis dan teknik presipitasi dengan mencampurkan prekursor Zn(NO3)2.4H2O 0.4, 0.6 dan 0.8 M. dan 50 ml ekstrak cair daun kelor selama 30 menit pada suhu 80ºC selama proses pengadukan pada pH 10. Endapan hasil sintesis dikalsinasi pada suhu 450ºC selama 120 menit hingga menghasilkan serbuk ZnO. Nanopartikel ZnO hasil biosintesis dilakukan pengujian menggunakan teknik Difraksi Sinar – X (XRD), Scanning Electron Microscope-Energy Dispersive X-Ray (SEM-EDX), Spektrofotometer UV-Vis, dan Fourier Transform Infra Red (FTIR). Berdasarkan Inorganic Crystal Structure Database (ICSD) nomor #96-900-4181, nanopartikel ZnO 0.4, 0.6 dan 0.8 M memiliki struktur kristal heksagonal wurtzite dengan space group P63mc. seiring dengan peningkatan molaritas, terjadi penurunan ukuran kristalit pada nanopartikel ZnO. Ukuran kristalit nanopartikel ZnO 0.4, 0.6 dan 0.8 M secara berturut-turut adalah 50.68 nm, 43.30 nm dan 41.30 nm. Morfologi nanopartikel ZnO berbentuk bulat (spherical), homogen dan memiliki ukuran yang kurang seragam. Spektrum EDX mengidentifikasi bahwa bahan yang disintesis adalah ZnO. Puncak maksimum spektrum absorbansi nanopartikel ZnO berada pada panjang gelombang 250-400 nm dan nilai energi celah pita berada pada 2.70-2.90 eV. Semakin kecil ukuran kristal dapat menghasilkan nilai energi celah pita yang lebih rendah. Hasil karakterisasi FTIR mengkonfirmasi adanya vibrasi ikatan Zn-O pada panjang gelombang 511.53-510.46 cm-1 yang diakibatkan oleh nanopartikel ZnO. Pada spektrum Infra Red teramati adanya gugus hidroksil (-OH) pada bilangan gelombang 3599.37-3598.69 cm-1 dan gugus karbonil (C=O) pada bilangan gelombang 1679.66-1632.23 cm-1 yang menunjukkan keberadaan senyawa flavonoid sebagai senyawa penting dalam reduksi dan stabilisasi nanopartikel ZnO. Kata Kunci : Nanopartikel ZnO, Struktur Kristal, Ukuran Kristalit, Morfologi, Sifat Optik, Gugus Fungsi. ***** ZnO nanoparticles have been successfully synthesized using biosynthesis method and precipitation technique by mixing Zn(NO3)2.4H2O precursor 0.4, 0.6, and 0.8 M. and 50 ml of liquid extract of Moringa leaves for 30 minutes at 80ºC during stirring process at pH 10. The synthesized precipitate was calcined at 450ºC for 120 minutes to produce ZnO powder. The biosynthesized ZnO nanoparticles were tested using X-ray Diffraction (XRD), Scanning Electron Microscope-Energy Dispersive X-Ray (SEM-EDX), UV-Vis Spectrophotometer, and Fourier Transform Infra Red (FTIR) techniques. Based on Inorganic Crystal Structure Database (ICSD) number #96-900-4181, ZnO nanoparticles 0.4, 0.6 and 0.8 M have a hexagonal wurtzite crystal structure with space group P63mc. along with an increase in molarity, there is a decrease in the crystallite size of ZnO nanoparticles. The crystallite size of 0.4, 0.6 and 0.8 M ZnO nanoparticles are 50.68 nm, 43.30 nm and 41.30 nm, respectively. The morphology of ZnO nanoparticles is spherical, homogeneous and non-uniform in size. The EDX spectrum identifies that the synthesized material is ZnO. The maximum peak of the absorbance spectrum of ZnO nanoparticles is at a wavelength of 250-400 nm and the band gap energy value is at 2.70 - 2.90 eV. The smaller the crystal size can produce lower band gap energy values. FTIR characterization results confirmed the presence of Zn-O bond vibrations at a wavelength of 511.53-510.46 cm-1 caused by ZnO nanoparticles. In the Infra Red spectrum, hydroxyl groups (-OH) at wavelengths 3599.37-3598.69 cm-1 and carbonyl groups (C=O) at wavelengths 1679.66-1632.23 cm-1 were observed, indicating the presence of flavonoid compounds as important compounds in the reduction and stabilization of ZnO nanoparticles. Keywords: ZnO nanoparticles, crystal structure, crystal size, morphology, optical properties, functional groups. *****

Item Type:	Thesis (Sarjana)
Additional Information:	1). Prof. Dr. Iwan Sugihartono, M.Si 2). Dr. Nurfina Yudasari, M.Sc
Subjects:	Sains > Fisika
Divisions:	FMIPA > S1 Fisika
Depositing User:	Users 24793 not found.
Date Deposited:	13 Aug 2024 05:49
Last Modified:	13 Aug 2024 05:49
URI:	http://repository.unj.ac.id/id/eprint/49893

Actions (login required)

View Item