PENGARUH KUAT ARUS DAN DIRECT QUENCHING PADA PENGELASAN SMAW TERHADAP KEKERASAN DAN LAJU KOROSI PADA BAJA KARBON RENDAH MENGGUNAKAN ELEKTRODA HV 800

AHMAD NUR HISYAM, . (2025) PENGARUH KUAT ARUS DAN DIRECT QUENCHING PADA PENGELASAN SMAW TERHADAP KEKERASAN DAN LAJU KOROSI PADA BAJA KARBON RENDAH MENGGUNAKAN ELEKTRODA HV 800. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text COVER.pdf Download (1MB)
	Text BAB 1.pdf Download (195kB)
	Text BAB 2.pdf Restricted to Registered users only Download (511kB) | Request a copy
	Text BAB 3.pdf Restricted to Registered users only Download (903kB) | Request a copy
	Text BAB 4.pdf Restricted to Registered users only Download (459kB) | Request a copy
	Text BAB 5.pdf Restricted to Registered users only Download (180kB) | Request a copy
	Text DAFTAR PUSTAKA.pdf Download (251kB)
	Text LAMPIRAN.pdf Restricted to Registered users only Download (902kB) | Request a copy

Abstract

Penelitian ini berfungsi untuk mengetahui pengaruh perbedaan kuat arus dan Direct quenching pada pengelasan dengan menggunakan elektroda HV-800 dan menggunakan metode pendinginan quenching tehadap nilai kekerasan Vickers, dan korosi. Penelitian ini menggunakan metode Experimental yang dilakukan di Laboratorium Universitas Negeri Jakarta, pada bulan Oktober 2024 sampai Januari 2025 dengan tujuan untuk mengetahui dampak dari 3 variasi arus dan 2 metode pendinginan pada (SMAW) baja karbon rendah tehadap nilai kekerasan dan laju korosi. Dari hasil pengelasan yag sudah dilakukan tedapat perbedaan kekerasan dan laju korosi, hal ini mengindikasikan perbedaan sifat mekanik antara kedua tipe material tersebut, yang disebabkan oleh proses pendinginan yang berbeda dapat mempengaruhi kekerasan material. Secara keseluruhan, dari data perhitungan yang tertera mengindikasikan bahwa kuat arus yang lebih tinggi dan penggunaan media pendingin udara cenderung menghasilkan laju korosi yang lebih tinggi dan nilai kekerasan yang lebih rendah, terlihat pada spesimen yang memiliki laju korosi tetinnggi adalah BNU 21,438 mpy dan specimen dengan kekerasan terendah adalah BNU 90 dengan nilai kekerasan 469,32 VHN, sedangkan media pendingin air dan kuat arus yang lebih tinggi cenderung lebih efektif dalam mengurangi tingkat korosi dan meningkatkan nilai kekerasan, terlihat pada spesimen BNA 90 dengan laju korosi terendah 6,432 mpy dan pesimen dengan nilai kekerasan tertinngi BNA 667,08 VHN. Kata kunci : Kuat arus, Quenching, Vickers, Korosi, Elektroda HV-800. *********** This study aims to knowing the effect of different current strengths and direct quenching on welding using HV-800 electrodes and the quenching cooling method on Vickers hardness and corrosion rate. The research adopts an experimental method conducted at the Laboratory of Universitas Negeri Jakarta from October 2024 to January 2025 to determine the impact of three current variations and two cooling methods on the hardness and corrosion rate of lowcarbon steel in Shielded Metal Arc Welding (SMAW). The welding results indicate differences in hardness and corrosion rate, suggesting variations in mechanical properties due to different cooling processes affecting material hardness. Overall, the calculated data indicate that higher current strength and air cooling tend to result in a higher corrosion rate and lower hardness. This is evident in the specimen with the highest corrosion rate, BNU 21.438 mpy, and the specimen with the lowest hardness, BNU 90, with a hardness value of 469.32 VHN. Meanwhile, water cooling and higher current strength tend to be more effective in reducing corrosion rates and increasing hardness, as seen in the BNA 90 specimen with the lowest corrosion rate of 6.432 mpy and the specimen with the highest hardness, BNA, with a hardness value of 667.08 VHN.

Item Type:	Thesis (Sarjana)
Additional Information:	1). Drs. Sopiyan, M.Pd. ; 2). Drs. Syaripuddin, M.Pd.
Subjects:	Teknologi dan Ilmu Terapan > Teknik Mesin, Mekanika Teknik
Divisions:	FT > S1 Pendidikan Teknik Mesin
Depositing User:	Users 26205 not found.
Date Deposited:	20 Feb 2025 07:41
Last Modified:	20 Feb 2025 07:41
URI:	http://repository.unj.ac.id/id/eprint/53196