PEMANFAATAN LIMBAH BETON SEBAGAI PENGGANTI AGREGAT DAN PENAMBAHAN SERAT KAIN DENIM TERHADAP KUAT TEKAN DAN KUAT LENTUR BETON (SEBAGAI IMPLEMENTASI MATA KULIAH TEKNOLOGI BETON)

FARID MUHAMAD HARAHAP, . (2025) PEMANFAATAN LIMBAH BETON SEBAGAI PENGGANTI AGREGAT DAN PENAMBAHAN SERAT KAIN DENIM TERHADAP KUAT TEKAN DAN KUAT LENTUR BETON (SEBAGAI IMPLEMENTASI MATA KULIAH TEKNOLOGI BETON). Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text COVER.pdf Download (3MB)
	Text BAB I.pdf Download (930kB)
	Text BAB II.pdf Restricted to Registered users only Download (3MB) | Request a copy
	Text BAB III.pdf Restricted to Registered users only Download (1MB) | Request a copy
	Text BAB IV.pdf Restricted to Registered users only Download (1MB) | Request a copy
	Text BAB V.pdf Restricted to Registered users only Download (1MB) | Request a copy
	Text DAFTAR PUSTAKA.pdf Download (1MB)
	Text LAMPIRAN.pdf Restricted to Registered users only Download (2MB) | Request a copy

Abstract

Beton merupakan salah satu material konstruksi yang digunakan pada konstruksi gedung, jembatan, jalan dan lain-lain. Material campuran penyusun beton terdiri dari agregat halus (pasir), agregat kasar (kerikil), air, dan semen. Akan tetapi kekurangan dari beton adalah kuat tarik yang rendah, berat, daya pantul suara yang besar, dan sulit merubah bentuk yang sebelumnya telah dibuat (Mufida, 2023). Untuk memperoleh sifat-sifat beton yang lebih baik, banyak hal yang dapat dilakukan mulai dari peningkatan mutu material beton sampai dengan memasukkan zat aditif berupa cairan maupun serat. Penambahan serat merupakan salah satu cara menaikkan kuat tekan beton (Anwar Chaeril et al., 2019). Penelitian ini bertujuan untuk mengetahui pemanfaatan limbah beton dan penambahan serat kain denim dalam meningkatkan nilai kuat tekan dan kuat lentur beton dengan ukuran serat panjang 100 mm dan lebar 5 mm dengan variasi penambahan serat 1% dan 2%. Kuat tekan rencana yaitu 40 MPa. Benda uji berbentuk silinder ukuran diameter 82 mm dan tinggi 150 mm dan benda uji balok ukuran 100 x 100 x 300 mm. Serta menganalisis pola retak hasil pengujian. Penelitian dilakukan di Laboratorium Uji Bahan Fakultas Teknik Universitas Negeri Jakarta dan dengan bantuan Laboratorium uji kain denim serta uji kuat lentur. Hasil pengujian pada umur 28 hari, didapatkan nilai kuat tekan beton kontrol, beton dengan proporsi serat 1% dan 2% secara berturut-turut adalah 10,27 MPa, 8,43 MPa, dan 5,44 MPa dengan nilai kuat tekan optimum sebesar 10,27 MPa pada beton kontrol. Sehingga dari keseluruhan nilai kuat tekan yang didapat, tidak ada yang mencapai kuat tekan rencana. Nilai kuat lentur hasil uji secara berturut-turut adalah 3,52 MPa, 4,32 MPa, dan 2,98 MPa dengan nilai kuat lentur optimum sebesar 4,32 MPa pada proporsi serat 1%. Nilai kuat lentur berkisar antara 34,27 – 54,77% dari nilai kuat tekannya. Kata Kunci: Beton Limbah, Kain Denim, Kuat Lentur. Kuat Tekan, Serat ***** Concrete is one of the construction materials used in the construction of buildings, bridges, roads, and others. The mixture materials that make up concrete consist of fine aggregate (sand), coarse aggregate (gravel), water, and cement. However, concrete has some drawbacks, such as low tensile strength, heaviness, high sound reflection, and difficulty in reshaping once it has set (Mufida, 2023). To improve the properties of concrete, various methods can be applied, ranging from improving the quality of concrete materials to incorporating additives in the form of liquids or fibers. Adding fibers is one way to increase concrete's compressive strength (Anwar Chaeril et al., 2019). This study aims to evaluate the use of concrete waste and the addition of denim fabric fibers in improving the compressive and flexural strength of concrete with fiber lengths of 100 mm and width of 5 mm, with variations in fiber content of 1% and 2%. The target compressive strength is 40 MPa. The test specimens are cylindrical with a diameter of 82 mm and a height of 150 mm, and beam specimens measuring 100 x 100 x 300 mm. The research also analyzes the crack patterns from the tests. The study was conducted at the Material Testing Laboratory of the Faculty of Engineering, State University of Jakarta, with the support of the Denim Fabric Testing Laboratory and Flexural Strength Testing. The results of testing at 28 days, with the addition of denim fabric fibers to the compressive strength of control concrete, concrete with 1% fiber, and concrete with 2% fiber, were 10.27 MPa, 8.43 MPa, and 5.44 MPa, respectively, with the optimum compressive strength value being 10.27 MPa for control concrete. Therefore, none of the mixtures achieved the target compressive strength. The flexural strength values from the tests were 3.52 MPa, 4.32 MPa, and 2.98 MPa, with the optimum flexural strength value being 4.32 MPa at the 1% fiber proportion. The flexural strength ranged between 34.27% and 54.77% of the compressive strength values. Keywords: Concrete Waste, Compressive Strength, Denim Fabric, Fibers, Flexural Strength

Item Type:	Thesis (Sarjana)
Additional Information:	1). Anisah, M.T. ; 2). Dr. Ririt Aprilin S., M.Sc., Eng.
Subjects:	Teknologi dan Ilmu Terapan > Teknik Sipil
Divisions:	FT > S1 Pendidikan Teknik Bangunan
Depositing User:	Farid Muhamad Harahap .
Date Deposited:	03 Mar 2025 03:31
Last Modified:	03 Mar 2025 03:31
URI:	http://repository.unj.ac.id/id/eprint/53664

Actions (login required)

View Item