PENGARUH VARIASI ALUMINA PADA RESIN POLIESTER TERHADAP SIFAT MEKANIK DAN ELEKTROSTATIS MATERIAL CFRP (CARBON FIBER REINFORCED POLYMER)

NURFITRIANI KHARISMADEWI, . (2025) PENGARUH VARIASI ALUMINA PADA RESIN POLIESTER TERHADAP SIFAT MEKANIK DAN ELEKTROSTATIS MATERIAL CFRP (CARBON FIBER REINFORCED POLYMER). Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text COVER.pdf Download (2MB)
	Text BAB 1.pdf Download (316kB)
	Text BAB 2.pdf Restricted to Registered users only Download (944kB) | Request a copy
	Text BAB 3.pdf Restricted to Registered users only Download (1MB) | Request a copy
	Text BAB 4.pdf Restricted to Registered users only Download (786kB) | Request a copy
	Text BAB 5.pdf Restricted to Registered users only Download (312kB) | Request a copy
	Text DAFTAR PUSTAKA.pdf Download (286kB)
	Text LAMPIRAN.pdf Restricted to Registered users only Download (1MB) | Request a copy

Abstract

Carbon Fiber Reinforced Polymer (CFRP) merupakan komposit bermatriks polimer yang diperkuat serat karbon dengan susunan serat yang rapi dan kontinu, sehingga memberikan kekuatan yang tinggi dengan berat yang ringan. Material ini telah banyak digunakan dalam bidang transportasi darat, laut, maupun udara, khususnya pada struktur badan dan lantai pesawat terbang. Untuk mengembangkan bahan alternatif dengan performa lebih optimal, penelitian ini menambahkan partikel alumina (Al₂O₃) ke dalam matriks resin CFRP dengan variasi konsentrasi 1, 3, 5, 7, dan 9% berat. Pengujian kekuatan tarik menggunakan Universal Testing Machine (UTM) menunjukkan nilai tertinggi pada variasi 5%, yaitu 274,40 MPa. Uji kekerasan menggunakan Vickers Hardness Tester mencatat nilai maksimum sebesar 50,8 VHN pada variasi 9%. Adapun resistansi listrik tertinggi mencapai 1,205 × 10⁹ ohm pada konsentrasi yang sama. Hasil menunjukkan bahwa penambahan alumina mampu meningkatkan kekuatan tarik dan resistansi material, sehingga berpotensi menggantikan material komposit konvensional untuk lantai pesawat. Namun, peningkatan kekerasan belum sepenuhnya memenuhi kriteria sifat mekanik material yang biasa ditemukan untuk penggunaan sejenis. ***** This study investigates the enhancement of Carbon Fiber Reinforced Polymer (CFRP) composites through the incorporation of alumina (Al₂O₃) particles. CFRP, a polymer matrix composite reinforced with continuously arranged carbon fibers, is widely employed in land, sea, and aerospace transportation due to its high strength-to-weight ratio. In this research, alumina particles were introduced into the CFRP resin matrix at weight percentages of 1, 3, 5, 7, and 9%. Mechanical performance was assessed using tensile tests with a Universal Testing Machine (UTM), which revealed that a 5% alumina concentration produced the highest tensile strength of 274.40 MPa. Hardness evaluation using the Vickers Hardness Tester yielded a maximum of 50.8 VHN at 9% alumina, and electrical resistance measurements reached 1.205 × 10⁹ ohm at the same concentration. The findings indicate that the addition of alumina particles effectively enhances both tensile strength and electrical resistance, positioning the modified composite as a promising alternative to conventional materials for aircraft floor applications. Nevertheless, the observed increase in hardness does not fully satisfy the mechanical property criteria commonly required for materials employed in comparable applications.

Item Type:	Thesis (Sarjana)
Additional Information:	1). Dr. Himawan Hadi Sutrisno, M.T. ; 2). Dr. Siska Titik Dwiyati, M.T.
Subjects:	Teknologi dan Ilmu Terapan > Teknik Mesin, Mekanika Teknik Teknologi dan Ilmu Terapan > Otomotif, Astronotika Teknologi dan Ilmu Terapan > Manufaktur
Divisions:	FT > S1 Rekayasa Keselamatan Kebakaran
Depositing User:	Nurfitriani Kharismadewi .
Date Deposited:	31 Jul 2025 03:51
Last Modified:	31 Jul 2025 03:51
URI:	http://repository.unj.ac.id/id/eprint/57034

Actions (login required)

View Item