PROSES ANODISASI PADA MAGNESIUM DENGAN ALAT BARRELING

FADILLAH RAMADHAN, . (2025) PROSES ANODISASI PADA MAGNESIUM DENGAN ALAT BARRELING. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

[img] Text
COVER.pdf

Download (1MB)
[img] Text
BAB 1.pdf

Download (265kB)
[img] Text
BAB 2.pdf
Restricted to Registered users only

Download (783kB) | Request a copy
[img] Text
BAB 3.pdf
Restricted to Registered users only

Download (381kB) | Request a copy
[img] Text
BAB 4.pdf
Restricted to Registered users only

Download (458kB) | Request a copy
[img] Text
BAB 5.pdf
Restricted to Registered users only

Download (247kB) | Request a copy
[img] Text
Daftar Pustaka.pdf

Download (205kB)
[img] Text
Lampiran.pdf
Restricted to Registered users only

Download (1MB) | Request a copy

Abstract

Magnesium merupakan logam ringan yang memiliki kekuatan spesifik tinggi, namun memiliki kelemahan utama yaitu rendahnya ketahanan terhadap korosi. Untuk mengatasi hal tersebut, dilakukan perlakuan permukaan berupa anodisasi yang bertujuan membentuk lapisan oksida pelindung. Penelitian ini menggunakan metode anodisasi dengan bantuan alat barreling untuk meningkatkan efisiensi dan keseragaman pelapisan, terutama pada komponen kecil. Proses anodisasi dilakukan dalam larutan elektrolit NaOH 1 M sebanyak 350 ml selama 20 menit, dengan arus listrik sebesar 0,5 A, 1 A, dan 2 A, serta kecepatan putar barrel sebesar 0, 50, dan 100 rpm. Pengujian yang dilakukan meliputi pengujian komposisi kimia lapisan, pengukuran kekasaran permukaan (Ra), pengukuran perubahan massa dan ketebalan lapisan spesimen setelah proses anodisasi. Hasil penelitian menunjukkan bahwa peningkatan kecepatan putar barrel menyebabkan nilai kekasaran permukaan menurun, menandakan terbentuknya lapisan oksida yang lebih merata dan halus. Sementara itu, Perbedaam arus yang digunakan menunjukkan bahwa arus terlalu besar dapat menyebabkan lapisan menjadi lebih tipis akibat over-oxidation. Metode barreling terbukti mampu menghasilkan proses anodisasi yang lebih merata dan efektif secara massal untuk logam magnesium. ***** Magnesium is a lightweight metal with a high specific strength, but it suffers from a major drawback—poor corrosion resistance. To overcome this limitation, surface treatment through anodizing was carried out to form a protective oxide layer. This study employed the anodizing process using a barreling system to improve the efficiency and uniformity of coating, particularly for small components. The anodizing process was conducted in a 1 M NaOH electrolyte solution (350 ml) for 20 minutes with varying current levels of 0.5 A, 1 A, and 2 A, and barrel rotation speeds of 0, 50, and 100 rpm. The tests carried out included chemical composition analysis of the anodized layer, surface roughness (Ra) measurement, and measurement of mass change and coating thickness of the specimens after the anodizing process. The results showed that increasing the barrel rotation speed led to a decrease in surface roughness values, indicating the formation of a smoother and more uniform oxide layer. On the other hand, excessive current resulted in thinner oxide layers due to over-oxidation. The barreling method proved effective in producing uniform and mass-processable anodized surfaces for magnesium.

Item Type: Thesis (Sarjana)
Additional Information: 1). Dr. Siska Titik Dwiyati, M.T. ; 2). Drs. Syaripudin, M.Pd.
Subjects: Teknologi dan Ilmu Terapan > Teknik Mesin, Mekanika Teknik
Divisions: FT > S1 Pendidikan Teknik Mesin
Depositing User: Fadillah Ramadhan .
Date Deposited: 04 Aug 2025 04:32
Last Modified: 04 Aug 2025 04:32
URI: http://repository.unj.ac.id/id/eprint/57619

Actions (login required)

View Item View Item