PENGARUH HEAT TREATMENT DENGAN MEDIA QUENCHING CAMPURAN PELUMAS DAN BENSIN TERHADAP KEKERASAN PERMUKAAN SERTA STRUKTUR MIKRO BAJA SKD 11

ERLANGGA ADITYA PUTRA PERDANA, . (2026) PENGARUH HEAT TREATMENT DENGAN MEDIA QUENCHING CAMPURAN PELUMAS DAN BENSIN TERHADAP KEKERASAN PERMUKAAN SERTA STRUKTUR MIKRO BAJA SKD 11. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text COVER.pdf Download (4MB)
	Text BAB I.pdf Download (216kB)
	Text BAB 2.pdf Restricted to Registered users only Download (452kB) | Request a copy
	Text BAB 3.pdf Restricted to Registered users only Download (415kB) | Request a copy
	Text BAB 4.pdf Restricted to Registered users only Download (558kB) | Request a copy
	Text BAB 5.pdf Restricted to Registered users only Download (197kB) | Request a copy
	Text Daftar Pustaka.pdf Download (174kB)
	Text Lampiran dan Daftar Riwayat Hidup.pdf Restricted to Registered users only Download (903kB) | Request a copy

Abstract

Penelitian ini membahas pengaruh media quenching campuran pelumas dan bensin terhadap transformasi fasa, untuk meningkatan kekerasan pada material baja SKD 11 atau Baja AISI D2. Spesimen diproses melalui perlakuan panas dengan metode pendinginan cepat menggunakan campuran pelumas SAE 15W – 40 dan Bensin RON 90 pada tiga konsentrasi, yaitu 10%, 20%, dan 30% dengan suhu 1000°C kemudian ditahan selama 60 menit. Proses ini memiliki tujuan untuk memacu pembentukan struktur mikro sehingga meningkatkan kekerasan. Pengamatan struktur mikro menggunakan mikroskop optik. Sedangkan uji kekerasan mengunakan metode vickers. Pengujian titik didih menggunakan alat termokopel. Hasil penelitian menunjukan penambahan media bensin pada proses pendinginan cepat dapat meningkatkan laju pendinginan media quenching sehingga martensit bertambah dan kekerasan meningkat. Dengan demikian, penambahan bensin pada media quenching dapat meningkatkan laju pendinginan sehingga martensit bertambah dan kekerasan baja meningkat. Kata Kunci : kekerasan, Laju pendinginan, Media quenching, martensit, titik didih. ***** This study examines the effect of a quenching medium consisting of a mixture of lubricant and gasoline on phase transformation to increase the hardness of SKD 11 steel or AISI D2 steel. The specimens were heat treated using a rapid cooling method using a mixture of SAE 15W-40 lubricant and RON 90 gasoline at three concentrations: 10%, 20%, and 30%, at a temperature of 1000°C and held for 60 minutes. This process aims to stimulate microstructure formation, thereby increasing hardness. Microstructure observations were performed using an optical microscope. Hardness testing was performed using the Vickers method. Boiling point testing was performed using a thermocouple. The results showed that adding gasoline to the rapid cooling process increased the cooling rate of the quenching medium, resulting in increased martensite formation and increased hardness. Therefore, adding gasoline to the quenching medium increased the cooling rate, resulting in increased martensite formation and increased steel hardness. Keywords: hardness, cooling rate, quenching medium, martensite, boiling point.

Item Type:	Thesis (Sarjana)
Additional Information:	1). Dr. Sugeng Priyanto,M.Sc.; 2). Dr. Siska Titik Dwiyati, M.T.
Subjects:	Teknologi dan Ilmu Terapan > Teknik Mesin, Mekanika Teknik Teknologi dan Ilmu Terapan > Teknik Pertambangan, Metalurgi Teknologi dan Ilmu Terapan > Teknik Kimia Teknologi dan Ilmu Terapan > Manufaktur
Divisions:	FT > D IV Teknologi Rekayasa Manufaktur
Depositing User:	Erlangga Aditya Putra Perdana .
Date Deposited:	30 Jan 2026 07:56
Last Modified:	30 Jan 2026 07:56
URI:	http://repository.unj.ac.id/id/eprint/64423

Actions (login required)

View Item