PEMANFAATAN LIMBAH CANGKANG KERANG HIJAU DAN LIMBAH PLASTIK POLYPROPYLENE SEBAGAI AGREGAT HALUS BUATAN TERHADAP SIFAT MEKANIK PAVING BLOCK

RODO MANOGU, . (2026) PEMANFAATAN LIMBAH CANGKANG KERANG HIJAU DAN LIMBAH PLASTIK POLYPROPYLENE SEBAGAI AGREGAT HALUS BUATAN TERHADAP SIFAT MEKANIK PAVING BLOCK. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text COVER.pdf Download (780kB)
	Text BAB I.pdf Download (380kB)
	Text BAB II.pdf Restricted to Registered users only Download (800kB)
	Text BAB III.pdf Restricted to Registered users only Download (973kB)
	Text BAB IV.pdf Restricted to Registered users only Download (1MB)
	Text BAB V.pdf Restricted to Registered users only Download (304kB)
	Text DAFTAR PUSTAKA.pdf Download (278kB)
	Text LAMPIRAN.pdf Restricted to Registered users only Download (1MB)

Abstract

Limbah plastik merupakan komposisi limbah terbanyak nomor 2 di Indonesia dan memberi dampak negatif terhadap lingkungan. Polypropylene (PP) adalah salah satu jenis plastik yang banyak digunakan dalam kemasan sekali pakai sehingga jumlah limbahnya terus meningkat. Selain itu, limbah cangkang kerang hijau yang dihasilkan dari konsumsi masyarakat belum dimanfaatkan secara optimal dan berpotensi menimbulkan pencemaran lingkungan. Penelitian ini bertujuan untuk memanfaatkan limbah plastik PP dan cangkang kerang hijau sebagai Artificial Lightweight Aggregate (ALWA) dalam pembuatan paving block guna mendukung program Sustainable Development Goals (SDG) nomor 11. Pada penelitian ini, limbah plastik PP diproses dan dicampur dengan serbuk cangkang kerang hijau untuk menghasilkan ALWA yang digunakan sebagai subtitusi sebagian hingga penuh pada pembuatan paving block. Komposisi PP : Cangkang kerang hijau yang digunakan dalam pembuatan ALWA adalah 5 : 1. Perbandingan campuran semen : pasir yang dipakai adalah 1 : 4 dan menggunakan fas 0,6. Pengujian dilakukan pada umur 28 hari berdasarkan SNI 03-0691-1996 dan dibandingkan dengan ASTM C 902 -09, meliputi uji kuat tekan, ketahanan aus, penyerapan air, dan ketahanan terhadap natrium sulfat. Hasil Penelitian menunjukkan bahwa pemanfaatan ALWA mampu meningkatkan ketahanan aus hingga 0,038 mm/ menit pada variasi 100%. Dari hasil penelitian variasi yang paling optimum adalah variasi 50% dengan nilai kuat tekan 4,06 Mpa, ketahanan aus 0,093 mm/ menit, penyerapan air 7,85% dan memenuhi uji ketahanan terhadap natrium sulfat. Hal ini menunjukkan bahwa pemanfaatan limbah plastik PP dan cangkang kerang hijau sebagai agregat halus buatan berpotensi sebagai alternatif material konstruksi yang ramah lingkungan dan berkelanjutan. ***** Plastic waste is the second-largest component of waste in Indonesia and has a negative impact on the environment. Polypropylene (PP) is one type of plastic widely used in single-use packaging, resulting in a continuously increasing volume of waste. In addition, green mussel shell waste generated from community consumption has not been optimally utilized and has the potential to cause environmental pollution. This study aims to utilize PP plastic waste and green mussel shell waste as Artificial Lightweight Aggregate (ALWA) in the production of paving blocks to support Sustainable Development Goal (SDG) number 11. In this study, PP plastic waste was processed and mixed with green mussel shell powder to produce ALWA, which was used as a partial to full substitute in the manufacture of paving blocks. The composition of PP to green mussel shell used in producing ALWA was 5:1. The cement-to-sand ratio applied was 1:4 with a water–cement ratio of 0.6. Testing was conducted at the age of 28 days based on SNI 03-0691-1996 and compared with ASTM C 902-09, including compressive strength, abrasion resistance, water absorption, and resistance to sodium sulfate. The results showed that the utilization of ALWA was able to improve abrasion resistance up to 0.038 mm/min at the 100% variation. Based on the results, the optimum variation was 50%, which achieved a compressive strength of 4.06 MPa, abrasion resistance of 0.093 mm/min, water absorption of 7.85%, and satisfied the sodium sulfate resistance test. These findings indicate that the utilization of PP plastic waste and green mussel shell waste as artificial fine aggregate has the potential to serve as an alternative, environmentally friendly, and sustainable construction material.

Item Type:	Thesis (Sarjana)
Additional Information:	1). Dr. Ririt Aprilin Sumarsono, S.T., M.Sc., Eng. ; 2). Anisah, M.T.
Subjects:	Teknologi dan Ilmu Terapan > Teknik Sipil
Divisions:	FT > S1 Pendidikan Teknik Bangunan
Depositing User:	Rodo Manogu .
Date Deposited:	09 Feb 2026 02:36
Last Modified:	09 Feb 2026 02:36
URI:	http://repository.unj.ac.id/id/eprint/65069

Actions (login required)

View Item