Pengaruh Variasi Kuat Arus Terhadap Kekuatan Tarik, Kekerasan dan Ketahanan Kebocoran Hasil Sambungan Las SMAW Pada Baja Mild Steel Ketebalan 8 mm

NAZMA AULIANI, . (2026) Pengaruh Variasi Kuat Arus Terhadap Kekuatan Tarik, Kekerasan dan Ketahanan Kebocoran Hasil Sambungan Las SMAW Pada Baja Mild Steel Ketebalan 8 mm. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text Cover.pdf Download (1MB)
	Text Bab I.pdf Download (268kB)
	Text Bab II.pdf Restricted to Registered users only Download (478kB) | Request a copy
	Text Bab III.pdf Restricted to Registered users only Download (1MB) | Request a copy
	Text Bab IV.pdf Restricted to Registered users only Download (858kB) | Request a copy
	Text Bab V.pdf Restricted to Registered users only Download (255kB) | Request a copy
	Text Daftar Pustaka.pdf Download (239kB)
	Text Lampiran.pdf Restricted to Registered users only Download (501kB) | Request a copy

Abstract

Pengelasan Shielded Metal Arc Welding (SMAW) merupakan metode penyambungan logam yang banyak digunakan pada konstruksi baja. Kualitas sambungan las dipengaruhi oleh berbagai parameter, salah satunya adalah kuat arus pengelasan yang berpengaruh terhadap kekuatan tarik, kekerasan, dan ketahanan kebocoran. Penelitian ini bertujuan untuk mengetahui pengaruh variasi kuat arus terhadap ketiga karakteristik tersebut pada baja ASTM A36 ketebalan 8 mm serta menentukan kuat arus yang menghasilkan kualitas sambungan las terbaik.Metode penelitian yang digunakan adalah metode eksperimen menggunakan material baja ASTM A36 ketebalan 8 mm dengan variasi kuat arus pengelasan sebesar 90 A, 100 A, dan 110 A menggunakan elektroda E6013 diameter 3,2 mm. Pengujian kebocoran dan tarik dilakukan pada sambungan dengan kampuh I, sedangkan pengujian kekerasan dan mikrostruktur dilakukan pada sambungan dengan kampuh V. Hasil penelitian menunjukkan bahwa variasi kuat arus memberikan pengaruh terhadap kualitas sambungan las. Pada pengujian kebocoran, spesimen dengan arus 110 A tidak menunjukkan adanya gelembung pada tekanan -0,2 bar, -0,4 bar, maupun -0,6 bar selama waktu penahanan 10 detik, sedangkan spesimen 90 A dan 100 A masih menunjukkan indikasi kebocoran. Hasil uji tarik menunjukkan nilai Ultimate Tensile Strength meningkat seiring bertambahnya arus pengelasan, yaitu sebesar 135,84 MPa pada 90 A, 167,38 MPa pada 100 A, dan 181,02 MPa pada 110 A. Pada kampuh V, nilai kekerasan weld metal cenderung menurun seiring peningkatan arus, sedangkan HAZ dan base metal menunjukkan peningkatan nilai kekerasan. Hasil pengamatan mikrostruktur menunjukkan keberadaan ferrite dan pearlite pada daerah weld metal, HAZ, dan base metal sebagai karakteristik struktur utama. Berdasarkan hasil tersebut, arus 110 A memberikan performa terbaik pada pengujian kebocoran dan tarik dengan kampuh I, sedangkan pengujian kekerasan dan mikrostruktur menunjukkan adanya perubahan karakteristik material akibat variasi siklus termal pengelasan. ***** Shielded Metal Arc Welding (SMAW) is a metal joining method widely used in steel construction. The quality of a welded joint is influenced by various parameters, one of which is the welding current, which affects tensile strength, hardness, and leak resistance. This study aims to determine the effect of varying welding current on these three characteristics in 8-mm-thick ASTM A36 steel and to identify the welding current that produces the best weld joint quality.The research method employed was an experimental approach using 8 mm thick ASTM A36 steel with welding current variations of 90 A, 100 A, and 110 A, utilizing a 3.2 mm diameter E6013 electrode. Leak and tensile tests were conducted on I-groove joints, while hardness and microstructure tests were conducted on V-groove joints. The research results show that variations in welding current affect the quality of the weld joint. In the leak test, the specimen welded at 110 A showed no bubbles at pressures of -0.2 bar, -0.4 bar, or -0.6 bar during a 10-second hold time, whereas the 90 A and 100 A specimens still showed signs of leakage. Tensile test results show that the Ultimate Tensile Strength increases with increasing welding current, namely 135.84 MPa at 90 A, 167.38 MPa at 100 A, and 181.02 MPa at 110 A. In the V-groove, the hardness of the weld metal tended to decrease with increasing current, while the HAZ and base metal showed an increase in hardness. Microstructural observations revealed the presence of ferrite and pearlite in the weld metal, HAZ, and base metal as the primary structural characteristics. Based on these results, a current of 110 A provided the best performance in the leak and tensile tests for joint I, while the hardness and microstructure tests indicated changes in material characteristics due to variations in the welding thermal cycle.

Item Type:	Thesis (Sarjana)
Additional Information:	1). Drs. Syamsuir, M.T; 2). Dr. Siska Titik Dwiyati, M.T.
Subjects:	Teknologi dan Ilmu Terapan > Teknik Mesin, Mekanika Teknik
Divisions:	FT > D IV Teknologi Rekayasa Manufaktur
Depositing User:	Nazma Auliani .
Date Deposited:	18 Aug 2026 06:53
Last Modified:	18 Aug 2026 06:53
URI:	http://repository.unj.ac.id/id/eprint/71390