PEMANFAATAN GGBFS SEBAGAI BAHAN TAMBAH PADA SELF COMPACTING CONCRETE

ADAM MUHAMMAD, . (2021) PEMANFAATAN GGBFS SEBAGAI BAHAN TAMBAH PADA SELF COMPACTING CONCRETE. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text COVER.pdf Download (1MB)
	Text BAB I.pdf Download (206kB)
	Text BAB II.pdf Restricted to Registered users only Download (416kB) | Request a copy
	Text BAB III.pdf Restricted to Registered users only Download (440kB) | Request a copy
	Text BAB IV.pdf Restricted to Registered users only Download (305kB) | Request a copy
	Text BAB V.pdf Restricted to Registered users only Download (127kB) | Request a copy
	Text DAFTAR PUSTAKA.pdf Download (262kB)
	Text LAMPIRAN.pdf Restricted to Registered users only Download (3MB) | Request a copy

Abstract

Penelitian ini bertujuan untuk mengetahui proporsi optimum penambahan GGBFS pada beton memadat mandiri atau Self Compacting Concrete dengan penggunaan superplasticizer jenis Sikament LN. Hasil penelitian didapatkan berdasarkan eksperimen yang telah dilakukan di Laboratorium Uji Bahan Fakultas Teknik Universitas Negeri Jakarta, yaitu dengan membuat campuran beton SCC menggunakan bahan tambah GGBFS dengan variasi 0%; 5%; 10%; 15%; 20%; 25%; 30% dan superplasticizer sebesar 1%. Data yang diperoleh dari penelitian ini yaitu hasil uji pendahuluan, hasil pengujian slump flow beton segar, hasil pengujian berat isi beton, hasil pengujian kuat tekan beton dengan umur 28 hari. Benda uji yang digunakan dalam penelitian ini berbentuk silinder dengan diameter 150 mm dan tinggi 300 mm dengan kuat tekan rencana fc' 35 MPa. Pengujian slump flow beton menggunakan kerucut Abrams dan pengujian kuat tekan beton menggunakan alat Crushing Test Machine. Dalam hal ini nilai slump flow yang dihasilkan benda uji beton pada variasi 0%; 5%; 10%; 15%; 20%; 25%; 30% yaitu 600 mm, 590 mm, 580 mm, 570 mm, 570 mm, 550 mm, dan 550 mm, sedangkan nilai kuat tekan beton adalah 35,47 MPa;37,23 MPa; 36,66 MPa; 37,67 MPa; 38,08 MPa; 39,94 MPa; 36,34 MPa. Terlihat bahwa nilai kuat tekan rata-rata maksimum terdapat pada variasi 25% dan kuat tekan meningkat sebesar 12% dibandingkan beton tanpa bahan tambah GGBFS This study aims to find the optimal proportion on adding GGBFS as an added concrete material in Self Compacting Concrete using superplasticizer Sikament LN type. the results of this study are based on experiments that was conducted at Material Testing Laoratory, Faculty of Engineering, State University of Jakarta by making self compacting concrete mixture with variations 0%; 5%; 10%; 15%; 20%; 25%; 30% and superplasticizer by 1%. The data obtained from preliminary test, slump flow test for fresh concrete, weight of concrete contents, concrete compressive strength test at 28 days. The specimen used in this study is cylindrical test object with diameter of 150 mm and height of 300 mm and the target of quality plan is fc' 35 Mpa. The sample will be tested with Abrams cone to determine the slump flow and Universal Testing Machine (UTM) to determine the compressive strength test. The results showed with variations 0%; 5%; 10%; 15%; 20%; 25%; 30% are 600 mm, 590 mm, 580 mm, 570 mm, 570 mm, 550 mm, and 550 mm, whereas compressived strength values are 35,47 MPa;37,23 MPa; 36,66 MPa; 37,67 MPa; 38,08 MPa; 39,94 MPa; 36,34 MPa. It can be seen that the maximum average compressive strength value is present in the 25% and compressive strength increased by 12% compared to concrete without added GGBFS material.

Item Type:	Thesis (Sarjana)
Additional Information:	1). Sittati Musalamah, M.T ; 2). M. Agphin Ramadhan, M.Pd
Subjects:	Teknologi dan Ilmu Terapan > Konstruksi Bangunan
Divisions:	FT > S1 Pendidikan Teknik Bangunan
Depositing User:	Users 9910 not found.
Date Deposited:	04 Mar 2021 08:26
Last Modified:	22 Jan 2024 23:54
URI:	http://repository.unj.ac.id/id/eprint/14211

Actions (login required)

View Item