PENAMBAHAN TUMBUKAN BATU BATA TERHADAP KUAT TEKAN MORTAR

LISA DWI RUSGIANA, . (2021) PENAMBAHAN TUMBUKAN BATU BATA TERHADAP KUAT TEKAN MORTAR. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text COVER.pdf Download (2MB)
	Text BAB 1.pdf Download (281kB)
	Text BAB 2.pdf Restricted to Registered users only Download (694kB) | Request a copy
	Text BAB 3.pdf Restricted to Registered users only Download (502kB) | Request a copy
	Text BAB 4.pdf Restricted to Registered users only Download (430kB) | Request a copy
	Text BAB 5.pdf Restricted to Registered users only Download (204kB) | Request a copy
	Text DAFTAR PUSTAKA.pdf Download (205kB)
	Text LAMPIRAN.pdf Restricted to Registered users only Download (2MB) | Request a copy

Abstract

*Abstrak* Lisa Dwi Rusgiana, Dra. Daryati, MT, Sittati Musalamah, MT. 2021. Penambahan Tumbukan Batu Bata Terhadap Kuat Tekan Mortar. Program Studi Pendidikan Teknik Bangunan. Fakultas Teknik; Universitas Negeri Jakarta. Penelitian ini bertujuan untuk mengetahui pengaruh penggunaan tumbukan batu bata sebagai bahan tambah semen dalam peningkatan kualitas mortar. Mortar ini menggunakan perbandingan campuran 1 semen : 2 pasir, dengan faktor air semen (FAS) 0,4 dan variasi presentase 0% sebagai kontrol, 2,5%, 5%, 7,5% 10%, 12,5%, dan 15% terhadap berat semen yang digunakan. Metode penelitian menggunakan metode eksperimen, pembuatan dan pengujian sifat mekanik mortar mengacu pada SNI 03-6882-2002. Batu bata diolah menjadi butir halus hingga ukuran 0,050 mm atau lolos saringan No. 300. Benda uji berbentuk kubus berukuran 5 cm×5 cm×5 cm sebanyak 35 sampel dengan masing-masing variasi 5 sampel dan perawatan mortar dengan perendaman selama 28 hari. Hasil penelitian penambahan tumbukan batu bata terhadap kuat tekan rata-rata mortar dengan variasi presentase 0%, 2,5%, 5%, 7,5% 10%, 12,5%, dan 15% berturut-turut adalah 13,2 MPa, 17,6 MPa, 18,8 MPa, 19,6 MPa, 17,6 MPa, 10,4 MPa, dan 7,6 MPa. Pada variasi 0% didapatkan hasil kuat tekan 13,2 MPa dan termasuk jenis mortar tipe N, sehingga tidak memenuhi ketentuan mortar tipe M sebesar 17,2 MPa. Pada variasi 2,5%, 5%, 7,5%, dan 10% masuk dalam jenis mortar tipe M karena melebihi batas kekuatan minimum pada SNI. Setelah variasi 7,5% terjadi penurunan kuat tekan mortar akibat semakin banyak tumbukan batu bata yang ditambahkan, maka batu bata yang berfungsi sebagai bahan tambah pada mortar menjadi tidak optimal dan proses hidrasi semen melambat. Kata kunci: Batu Bata, Kuat Tekan, Mortar. *ABSTRACT* Lisa Dwi Rusgiana, Dra. Daryati, MT, Sittati Musalamah, MT. 2021. Addition Of Dust Againts Mortar Compressive Strength. Program Studi Pendidikan Teknik Bangunan. Fakultas Teknik; Universitas Negeri Jakarta. The research is to know the improvement quality of mortar by adding brick powder from waste brick. The mortar use mixture ratio 1 cement : 2 sand, with 0,4 FAS and use variation percentage 0% as control, 2,5%, 5%, 7,5%, 10%, 12,5%, dan 15% againts the wight of cement. The research use experiment method, and SNI 03-6881-2002 as reference for fabrication and mechanical properties test of mortar. The brick waste processed as fine aggregate up to size 0,050 mm or pass filter no. 300. The amount of sample is 35 with 5 each variation, the form of the sample is cube with the measure 5cm x 5cm x 5cm, the curing sample is soaked for 28 days. The result is by adding waste brick againts the average compressive strength of mortar with variation 0%, 2,5%, 5%, 7,5%, 10%, 12,5% and 15% are 13,2 MPa, 17,6 MPa, 18,8 MPa, 19,6 MPa, 17,6 MPa, 10,4 MPa, and 7,6 MPa. The compressive strength of sample variation 0% has 13,2 MPa, which the sample doesn’t meet the requirements of mortar type M that has amount 17,2 MPa. The sample with 2,5%, 5%, 7,5%, and 10% variation meet the requirements of mortar type M. The sample after 7,5% variation has decreased the compressive strength, it because adding more brick powder as additive on mortar is not optimal and slow down the hidration process on cement. Keywords: Dust brick, Compressive strength, Mortar.

Item Type:	Thesis (Sarjana)
Additional Information:	1) Dra. Daryati, MT 2) Sittati Musalamah, MT
Subjects:	Teknologi dan Ilmu Terapan > Teknik Sipil Teknologi dan Ilmu Terapan > Konstruksi Bangunan
Divisions:	FT > S1 Pendidikan Teknik Bangunan
Depositing User:	Users 12424 not found.
Date Deposited:	02 Sep 2021 22:19
Last Modified:	02 Sep 2021 22:19
URI:	http://repository.unj.ac.id/id/eprint/19402

Actions (login required)

View Item