PEMANFAATAN ABU SEKAM PADI DAN PLASTIK PET MENJADI PENGGANTI SEBAGIAN AGREGAT HALUS DALAM PEMBUATAN PAVING BLOCK SEBAGAI IMPLEMENTASI PADA MATA KULIAH PRAKTIK UJI BAHAN

SUGANDA WIJAYA, . (2022) PEMANFAATAN ABU SEKAM PADI DAN PLASTIK PET MENJADI PENGGANTI SEBAGIAN AGREGAT HALUS DALAM PEMBUATAN PAVING BLOCK SEBAGAI IMPLEMENTASI PADA MATA KULIAH PRAKTIK UJI BAHAN. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text COVER.pdf Download (3MB)
	Text BAB 2.pdf Restricted to Registered users only Download (305kB) | Request a copy
	Text BAB 3.pdf Restricted to Registered users only Download (552kB) | Request a copy
	Text BAB 4.pdf Restricted to Registered users only Download (373kB) | Request a copy
	Text BAB 5.pdf Restricted to Registered users only Download (142kB) | Request a copy
	Text LAMPIRAN.pdf Restricted to Registered users only Download (566kB) | Request a copy
	Text DAFTAR PUSTAKA.pdf Download (218kB)
	Text BAB 1.pdf Download (206kB)

Abstract

Penelitian ini bertujuan untuk memanfaatkan limbah dari abu sekam padi dan plastik PET dalam pembuatan paving block. Dikarenakan limbah plastik PET memiliki kelebihan tidak mudah untuk terurai dan tahan lama, sedangkan abu sekam padi memiliki kelebihan daya ikat yang baik, di mana limbah plastik PET tidak memiliki daya ikat untuk mengikat campuran lain, kemudian untuk menutupi kekurangan itu maka di kombinasikan abu sekam padi dengan plastik PET. Metode yang digunakan pada penelitian ini yaitu metode eksperimen pada paving block dengan mengganti sebagian agregat halus dengan agregat buatan dengan variasi 0%, 5%, 10% dan 15% terhadap berat agregat halus. Benda uji dilakukan pengujian pada umur 28 Hari sesuai dengan SNI 03-0691-1996. Benda uji berukuran 210 mm x 105 mm x 60 mm. Jenis pengujian yang dilakukan adalah pengujian tampak dan ukuran, uji kuat tekan, uji ketahanan aus dan uji daya serap air. Didapatkan hasil pengujian nilai kuat tekan untuk variasi 5%, 10% dan 15% berturut-turut adalah 20 MPa, 17,597 MPa, dan 15,927 MPa. Paving block dengan variasi 5% temasuk kedalam mutu B, sedangkan paving block dengan variasi 10% & 15% tidak termasuk ke dalam mutu B melainkan masuk kedalam mutu C. This Research aims to utilize waste from rice husk ash and PET plastic, in the manufacture of Paving block, Because PET plastic waste has the advantages of not easy to decompose and durable while rice husk ash has the advantage of good binding power, where PET plastic waste does not have the binding power to bind other mixtures, then to cover this deficiency, rice husk ash in combined with PET plastic. The method use in this research is ecxperimental method on paving block by replacing some of the fine aggregate with artificial aggregate with variations 0%, 5%, 10% dan 15% of the weight of the fine aggregate. The specimens were tested at the age of 28 days in accordance with SNI 03-0691-1996. The test object size is 210 mm x 105 mm x 60 mm. Thpes of the test carried out are visible and sizing test, compressive strength test, wear resistance test dan water absorption test. The results of testing the compressive strength values for variations of 5%, 10% and 15% respectively are 20 MPa, 17.597 MPa, and 15.927 MPa. Paving blocks with a variation of 5% are included in the B quality, while the paving blocks with a variation of 10% & 15% are not included in the B quality but are included in the C quality.

Item Type:	Thesis (Sarjana)
Additional Information:	1. Dra. Daryati, MT 2. Dra. Rosmawita Saleh, M.Pd
Subjects:	Teknologi dan Ilmu Terapan > Teknik Sipil Teknologi dan Ilmu Terapan > Konstruksi Bangunan
Divisions:	FT > S1 Pendidikan Teknik Bangunan
Depositing User:	Users 13535 not found.
Date Deposited:	08 Mar 2022 03:27
Last Modified:	08 Mar 2022 03:27
URI:	http://repository.unj.ac.id/id/eprint/22876

Actions (login required)

View Item