HANIFAH WIDYA PUTRI, . (2016) STUDI SIFAT KEOPTIKAN DYE-SENSITIZED SOLAR CELL (DSSC) DENGAN DYE EKSTRAKSI KULIT BUAH RAMBUTAN (Nephelium Lappaceum). Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.
![]() |
Text
3225122051- HANIFAH WIDYA PUTRI.pdf Download (2MB) |
Abstract
Krisis energi mendorong kepada pengembangan sumber energi alternatif seperti panel surya. Salah satu jenis panel surya adalah DSSC. Penelitian ini bertujuan untuk memanfaatkan kulit buah rambutan (Nephelium Lappaceum) sebagai fotosensitizer dalam Dye Sensitized Solar Cell (DSSC) serta mengetahui sifat optik DSSC tersebut. Struktur DSSC berbentuk sandwich yang terdiri dari kaca konduktif sebagai substrat, TiO2 sebagai bahan semikonduktor, dye alami sebagai donor elektron dan elektrolit sebagai transfer elektron. Hasil X-Ray Diffraction lapisan TiO2 menunjukkan intensitas relatif tinggi, dengan pola difraksi anatase dan ukuran kristal 60.8 nm. Karakterisasi spektroskopi UV-Vis digunakan untuk mengevaluasi sifat optik dalam sel surya. Hasil penelitian menunjukan bahwa fotosensitizer menghasilkan absorbsi gelombang pada rentang panjang gelombang 400nm-600nm. Transmitansi DSSC relatif rendah berada pada rentang 300nm800nm yang menunjukan adanya absorbsi pada panjang gelombang tertentu. DSSC dengan elektroda pembanding karbon mempunyai absorbansi yang lebih tinggi yaitu 3.964 dibandingkan dengan elektroda yang dilapisi emas, yaitu 3.27. Sementara itu, hasil pengukuran lebar celah pita energi DSSC berada pada 2.8 Ev. The energi crisis encourages the development of alternative energi sources such as solar panels. One type of solar panel is DSSC. This research aims to utilize the rind of Rambutan (Nephelium lappaceum) as a photosensitizer in the Dyesensitized Solar Cell (DSSC) and discover the optical properties of the DSSC. The structure of DSSC is sandwich-shaped which consists of a conductive glass as a substrate, TiO2 as a semiconductor material, a natural dye as an electron donor and an electrolyte as an electron transfer. The X-Ray Diffraction results of the layer of TiO2 showed a relatively high intensity, with the the diffraction pattern of anatase and crystal size of 60.8 nm. The characterization of UV-Vis spectroscopy was used to evaluate the optical properties of the solar cell. The results showed that the photosensitizer produces wave absorption in the wavelength range of 400nm600nm. The transmittance of DSSC was relatively low in the range of 300nm800Nm that showed the presence of absorption at certain wavelengths. DSSC with the reference electrode of carbon had has a higher absorbance namely of 3,964 compared with the gold-plated electrodes, which was 3.27eV. Meanwhile, the measurement result of DSSC energi band gap width was at 2.8 eV.
Item Type: | Thesis (Sarjana) |
---|---|
Additional Information: | 1) Cecep E. Rustana, Ph.D 2) Dr. Sunaryo, M.Si |
Subjects: | Sains > Fisika |
Divisions: | FMIPA > S1 Fisika |
Depositing User: | sawung yudo |
Date Deposited: | 06 Apr 2022 04:07 |
Last Modified: | 06 Apr 2022 04:07 |
URI: | http://repository.unj.ac.id/id/eprint/25886 |
Actions (login required)
![]() |
View Item |