SINTESIS MATERIAL BARIUM W-HEKSAFERRIT DENGAN SUBSTITUSI Co-Ti TERHADAP Fe PADA BaCoTiFe16-2xCoxTixO27 SEBAGAI MATERIAL PENYERAP GELOMBANG MIKRO

DESRIYAN LESTARI, . (2015) SINTESIS MATERIAL BARIUM W-HEKSAFERRIT DENGAN SUBSTITUSI Co-Ti TERHADAP Fe PADA BaCoTiFe16-2xCoxTixO27 SEBAGAI MATERIAL PENYERAP GELOMBANG MIKRO. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

Text PDF-SKRIPSI-DESRIYAN LESTARI-3225111281.pdf Download (6MB)

Abstract

Telah dilakukan pembuatan Barium W-Heksaferrit BaCoTiFe16-2xCoxTixO27 yang didoping ion Co dan ion Ti dengan variasi x = 0 – 0.5 menggunakan metode mechanical alloying. Proses preparasi bahan dasar BaCo3, Fe2O3, Co3O4, dan TiO2 dicampur dengan cara wet milling dengan media toluena selama 1 jam. Selanjutnya dikalsinasi pada temperature 750ºC selama 3 jam dan sintering pada penahanan temperatur 1100ºC selama 3 jam. Karakterisasi pembentukan fasa magnet dilakukan dengan menggunakan difraksi sinar-X (XRD) dan Scaning Electron Microscopy (SEM). Sedangkan untuk sifat kemagnetan dilakukan dengan menggunakan Permagraph. Hasil pengujian material magnet menunjukan nilai koersivitas material menurun dengan semakin banyaknya subtitusi. Material dengan x = 0.5 memiliki nilai koersivitas intrinsik (Hc) 0.523 kA/m, dengan nilai Hc yang rendah menunjukan bahwa subtitusi Co-Ti terhadap Fe pada BaCoTiFe16-2xCoxTixO27 berpeluang untuk digunakan sebagai material penyerap gelombang mikro. Barium W-Hexaferitte BaCoTiFe16-2xCoxTixO27 doped by ions Co and ions Ti have been made with the variation of x = 0 - 0.5 by using mechanical alloying method. The preparation raw material process of BaCO3, Fe2O3, Co3O4 and TiO2 were done by wet milling mixing for 1 hours using toluene. Then calcination at a temperature of 750°C for 3 hours and sintering of 1100°C for 3 hours. The characterization of formation magnetic phase tested by using X-Ray Diffraction (XRD) and Scanning Electron Microscopy (SEM). As for the magnetic properties is tested by using Permagraph. The test results of magnetic material showed that the more substitutions then the value of coercivity decreases. The material with x = 0.5 has intrinsic coercivity (Hc) of 0523 kA / m, with a low Hc showed that the Co-Ti substitution for Fe on BaCoTiFe16-2xCoxTixO27 potentially to be used as a microwave absorbent material.

Item Type:	Thesis (Sarjana)
Additional Information:	1). Dr. Erfan Handoko, M.Si. ; 2). Dr. Widyaningrum Indrasari, M.Si.
Subjects:	Sains > Fisika
Divisions:	FMIPA > S1 Fisika
Depositing User:	Users 8922 not found.
Date Deposited:	26 Apr 2022 06:12
Last Modified:	26 Apr 2022 06:12
URI:	http://repository.unj.ac.id/id/eprint/27559