Pengaruh Variasi Serbuk Tembaga Terhadap Kekuatan Tarik Dan Tekan Pada Komposit Serbuk Kayu, Serat Kelapa, Dan Serbuk Tembaga Pada Kampas Kopling Sentrifugal Motor Matic

MOHAMAD RANDY ADRIAN RADITY, . (2024) Pengaruh Variasi Serbuk Tembaga Terhadap Kekuatan Tarik Dan Tekan Pada Komposit Serbuk Kayu, Serat Kelapa, Dan Serbuk Tembaga Pada Kampas Kopling Sentrifugal Motor Matic. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

[img] Text
COVER.pdf

Download (1MB)
[img] Text
BAB 1.pdf

Download (274kB)
[img] Text
BAB 2.pdf
Restricted to Registered users only

Download (1MB) | Request a copy
[img] Text
BAB 3.pdf
Restricted to Registered users only

Download (1MB) | Request a copy
[img] Text
BAB 4.pdf
Restricted to Registered users only

Download (1MB) | Request a copy
[img] Text
BAB 5.pdf
Restricted to Registered users only

Download (230kB) | Request a copy
[img] Text
DAFTAR PUSTAKA.pdf

Download (270kB)
[img] Text
LAMPIRAN.pdf
Restricted to Registered users only

Download (2MB) | Request a copy

Abstract

Penelitian ini bertujuan untuk mengetahui pengaruh variasi serbuk tembaga terhadap kekuatan tarik dan tekan pada komposit serbuk kayu sangon, serat kelapa, dan serbuk tembaga yang digunakan dalam kampas kopling sentrifugal motor matic. Penelitian ini dimulai dengan melakukan pembuatan 5 spesimen dengan bentuk ASTM D695 dan ASTM D638 yang selanjutnya akan dilakukan pengujian tekan, pengujian tarik, struktur mikro, dan kekerasan. Hasil penelitian menunjukkan bahwa peningkatan persentasi serbuk tembaga dalam komposit secara signifikan meningkatkan kekuatan tarik dan tekan komposit serbuk kayu, searbut tembaga, dan serbuk tembaga. Komposisi paling optimal ada pada komposit dengan komposisi tembaga sebesar 10% yang memiliki kekuatan tarik sebesar 11,19 MPa dan kekuatan tarik sebesar 90,8 MPa. Penelitian ini menyimpulkan bahwa penggunaan serbuk tembaga sebagai bahan penguat dalam komposit dapat meningkatkan performa mekanis kampas kopling sentrifugal. This research aims to determine the effect of variations in copper powder on the tensile and compressive strength of a composite of sangon wood powder, coconut fiber and copper powder used in centrifugal clutch linings for automatic motorbikes. This research begins by making 5 specimens in the form of ASTM D695 and ASTM D638 which will then be subjected to compression testing, tensile testing, microstructure and hardness. The results showed that increasing the percentage of copper powder in the composite significantly increased the tensile and compressive strength of wood powder, copper fiber and copper powder composites. The most optimal composition is a composite with a copper composition of 10% which has a tensile strength of 11.19 MPa and a tensile strength of 90.8 MPa. This research concludes that the use of copper powder as a reinforcing material in composites can improve the mechanical performance of centrifugal clutch linings.

Item Type: Thesis (Sarjana)
Additional Information: 1). Ahmad Kholil, S.T., M.T. 2). Dr. Eng. Agung Premono, M.T.
Subjects: Teknologi dan Ilmu Terapan > Teknik Mesin, Mekanika Teknik
Divisions: FT > S1 Teknik Mesin
Depositing User: Users 23401 not found.
Date Deposited: 26 Jul 2024 04:43
Last Modified: 26 Jul 2024 04:43
URI: http://repository.unj.ac.id/id/eprint/46782

Actions (login required)

View Item View Item