PEMANFAATAN CANGKANG TELUR SEBAGAI INHIBITOR KOROSI PADA CAT BESI: ANALISIS EFEKTIVITAS DAN DAYA TAHAN

SODIK MAULANA, . (2025) PEMANFAATAN CANGKANG TELUR SEBAGAI INHIBITOR KOROSI PADA CAT BESI: ANALISIS EFEKTIVITAS DAN DAYA TAHAN. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text COVER.pdf Download (1MB)
	Text BAB I.pdf Download (211kB)
	Text BAB II.pdf Restricted to Registered users only Download (1MB) | Request a copy
	Text BAB III.pdf Restricted to Registered users only Download (239kB) | Request a copy
	Text BAB IV.pdf Restricted to Registered users only Download (785kB) | Request a copy
	Text BAB V.pdf Restricted to Registered users only Download (182kB) | Request a copy
	Text DAFTAR PUSTAKA.pdf Download (199kB)
	Text Lampiran.pdf Restricted to Registered users only Download (1MB) | Request a copy

Abstract

Korosi merupakan permasalahan umum yang menyebabkan kerusakan struktural pada logam serta kerugian ekonomi yang cukup besar. Salah satu upaya pencegahan yang banyak dikembangkan adalah penggunaan cat pelindung dengan penambahan inhibitor alami. Dalam penelitian ini, serbuk cangkang telur ayam digunakan sebagai bahan aditif dalam cat alkid satu lapis, dengan tujuan untuk meningkatkan ketahanan terhadap korosi serta mengoptimalkan fungsi filler alami berbasis kalsium karbonat (CaCO₃). Penelitian dilakukan menggunakan metode eksperimen laboratorium dengan pendekatan uji perendaman selama 120 jam dalam larutan NaCl 3,5%. Lima variasi konsentrasi serbuk cangkang telur (0%, 5%, 10%, 15%, dan 20%) diaplikasikan pada pelat besi dan dievaluasi menggunakan uji kehilangan massa, uji visual berdasarkan standar ASTM D610, serta uji daya rekat cat dengan metode Cross Cut Test (ISO 2409). Data yang diperoleh kemudian dianalisis secara kuantitatif dan kualitatif untuk menilai efektivitas perlindungan terhadap korosi. Hasil menunjukkan bahwa penambahan serbuk cangkang telur secara signifikan menurunkan laju korosi dari 0,0052 mm/tahun menjadi 0,0022 mm/tahun, serta meningkatkan skor visual permukaan hingga 9-G. Formulasi optimal terdapat pada konsentrasi 10%, yang memberikan perlindungan korosi baik serta daya rekat sempurna (nilai adhesi 0). Penggunaan serbuk cangkang telur terbukti efektif sebagai alternatif inhibitor alami dan ramah lingkungan untuk aplikasi cat pelindung logam berbasis alkid. Kata kunci: cangkang telur, inhibitor alami, korosi ****** Corrosion is a common problem that causes structural damage to metals and significant economic losses. One of the most widely developed preventive measures is the use of protective paint with the addition of natural inhibitors. In this study, chicken eggshell powder was used as an additive in single-layer alkyd paint, with the aim of increasing corrosion resistance and optimizing the function of natural calcium carbonate (CaCO₃) based fillers. The study was conducted using a laboratory experimental method with a 120-hour immersion test in a 3.5% NaCl solution. Five variations of eggshell powder concentration (0%, 5%, 10%, 15%, and 20%) were applied to iron plates and evaluated using mass loss testing, visual testing based on ASTM D610 standards, and paint adhesion testing using the Cross Cut Test method (ISO 2409). The data obtained were then analyzed quantitatively and qualitatively to assess the effectiveness of corrosion protection. The results showed that the addition of eggshell powder significantly reduced the corrosion rate from 0.0052 mm/year to 0.0022 mm/year and improved the visual surface score to 9-G. The optimal formulation was found at a concentration of 10%, which provided good corrosion protection and perfect adhesion (adhesion value of 0). The use of eggshell powder has proven effective as a natural and environmentally friendly alternative inhibitor for alkyd-based metal protective coatings Keywords: corrosion, eggshell, natural inhibitors

Item Type:	Thesis (Sarjana)
Additional Information:	1. Dr. Wardoyo, S.T., M.T. ; 2. Dr.Siska Titik Dwiyati, M.T.
Subjects:	Teknologi dan Ilmu Terapan > Teknik Lingkungan, Teknik Sanitasi Teknologi dan Ilmu Terapan > Teknik Mesin, Mekanika Teknik Teknologi dan Ilmu Terapan > Manufaktur
Divisions:	FT > D IV Teknologi Rekayasa Manufaktur
Depositing User:	Sodik Maulana .
Date Deposited:	13 Aug 2025 01:55
Last Modified:	13 Aug 2025 06:33
URI:	http://repository.unj.ac.id/id/eprint/58670

Actions (login required)

View Item