PENGARUH PENGEROLAN DINGIN DAN ANIL TERHADAP KEKERASAN, KETAHANAN KOROSI, DAN STRUKTUR MIKRO PADA PADUAN KUNINGAN Cu-35Zn

DIMAS ANDRIAN PUTRA, . (2025) PENGARUH PENGEROLAN DINGIN DAN ANIL TERHADAP KEKERASAN, KETAHANAN KOROSI, DAN STRUKTUR MIKRO PADA PADUAN KUNINGAN Cu-35Zn. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text COVER.pdf Download (722kB)
	Text BAB 1.pdf Download (294kB)
	Text BAB 2.pdf Restricted to Registered users only Download (676kB) | Request a copy
	Text BAB 3.pdf Restricted to Registered users only Download (1MB) | Request a copy
	Text BAB 4.pdf Restricted to Registered users only Download (2MB) | Request a copy
	Text BAB 5.pdf Restricted to Registered users only Download (278kB) | Request a copy
	Text DAFTAR PUSTAKA.pdf Download (252kB)
	Text LAMPIRAN.pdf Restricted to Registered users only Download (1MB) | Request a copy

Abstract

Penelitian ini bertujuan untuk mengetahui pengaruh proses pengerolan dingin dan anil terhadap struktur mikro, kekerasan, dan ketahanan korosi pada paduan kuningan Cu-35Zn. Sampel diberikan perlakuan pengerolan dingin dengan variasi reduksi ketebalan 20 %, 40 % dan 70 %, kemudian dilakukan proses anil pada temperatur 300 ℃ - 600 ℃ masing-masing selama 30 menit. Analisis struktur mikro dilakukan menggunakan mikroskop optik. Struktur mikro menunjukkan bahwa deformasi menghasilkan butir yang lebih kecil dan memanjang sehingga meningkatkan kekerasan, sedangkan anil memperbesar butir dan menurunkan kekerasan. Nilai kekerasan diuji menggunakan metode Vickers, dan ketahanan korosi dianalisis dengan uji weight loss menggunakan media korosi larutan H2SO4. Hasil penelitian menunjukkan bahwa pengerolan dingin meningkatkan kekerasan material akibat pengerolan dingin diikuti dengan meningkatnya ketahanan korosi. Nilai kekerasan paduan meningkat seiring bertambahnya deformasi plastis saat pengerolan dingin, yaitu 135,88 HV (20 %), 160,78 HV (40 %), dan 212,2 HV (70 %), sedangkan ketahanan korosi juga meningkat setelah pengerolan dingin, ditunjukkan oleh penurunan laju korosi dari 0,5153 mmpy (20 %) menjadi 0,3435 mmpy (40 %) dan 0,1656 mmpy (70 %). Perlakuan anil menurunkan kekerasan secara signifikan pada semua tingkat deformasi, seperti pada deformasi 20% yang turun dari 133 HV (300 °C) menjadi 53,9 HV (600 °C), serta menurunkan laju korosi, di mana setiap tingkat deformasi menunjukkan penurunan tertinggi pada anil 600 °C dan tertinggi pada 300 °C. Proses anil terbukti mampu mengembalikan ketahanan korosi dan memperbaiki struktur mikro melalui rekristalisasi. ***** This study aims to investigate the effects of cold rolling and annealing processes on the microstructure, hardness, and corrosion resistance of Cu-35Zn brass alloy. Samples were subjected to cold rolling with thickness reductions of 20 %, 40 %, and 70 %, followed by annealing at temperatures ranging from 300 °C to 600 °C for 30 minutes. Microstructural analysis using an optical microscope revealed that deformation produced finer, elongated grains that increased hardness, while annealing led to grain growth and decreased hardness. Hardness was measured using the Vickers method, and corrosion resistance was evaluated through weight loss testing in H₂SO₄ solution. The results showed that cold rolling enhanced both hardness and corrosion resistance, with hardness increasing alongside the degree of plastic deformation: 135.88 HV (20 %), 160.78 HV (40 %), and 212.2 HV (70 %). Corrosion rate decreased accordingly: 0.5153 mmpy (20 %), 0.3435 mmpy (40 %), and 0.1656 mmpy (70 %). Annealing significantly reduced hardness across all deformation levels, for instance, from 133 HV (300 °C) to 53.9 HV (600 °C) at 20% deformation. It also improved corrosion resistance, showing the greatest effect at 600 °C. Overall, annealing proved effective in restoring corrosion resistance and refining microstructure through recrystallization.

Item Type:	Thesis (Sarjana)
Additional Information:	1). Dr. Imam Basori, S.T., M.T. ; 2). Ferry Budhi Susetyo, S.T., M.T., M.Si.
Subjects:	Teknologi dan Ilmu Terapan > Teknik Mesin, Mekanika Teknik Teknologi dan Ilmu Terapan > Teknik Pertambangan, Metalurgi
Divisions:	FT > S1 Pendidikan Teknik Mesin
Depositing User:	Dimas Andrian Putra .
Date Deposited:	08 Aug 2025 07:48
Last Modified:	08 Aug 2025 08:00
URI:	http://repository.unj.ac.id/id/eprint/59104

Actions (login required)

View Item