PENGARUH PENAMBAHAN UNSUR NIKEL (Ni) TERHADAP STRUKTUR MIKRO, KEKERASAN, DAN KETAHANAN KOROSI PADUAN KUNINGAN Cu-34Zn

HENDI WAHYUDIN, . (2025) PENGARUH PENAMBAHAN UNSUR NIKEL (Ni) TERHADAP STRUKTUR MIKRO, KEKERASAN, DAN KETAHANAN KOROSI PADUAN KUNINGAN Cu-34Zn. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text Cover.pdf Download (1MB)
	Text BAB I.pdf Download (254kB)
	Text BAB II.pdf Restricted to Registered users only Download (703kB) | Request a copy
	Text BAB III.pdf Restricted to Registered users only Download (1MB) | Request a copy
	Text BAB IV.pdf Restricted to Registered users only Download (1MB) | Request a copy
	Text BAB V.pdf Restricted to Registered users only Download (209kB) | Request a copy
	Text Daftar Pustaka.pdf Download (232kB)
	Text Lampiran.pdf Restricted to Registered users only Download (2MB) | Request a copy

Abstract

Penelitian ini bertujuan untuk menganalisis pengaruh penambahan unsur nikel (Ni) terhadap struktur mikro, kekerasan, dan ketahanan korosi pada paduan kuningan Cu-34Zn sebagai upaya pengembangan material alternatif untuk peralatan medis yang kuat dan tahan korosi. Kajian pustaka didasarkan pada teori diagram fasa Cu-Zn dan mekanisme solid solution strengthening. Proses penelitian meliputi pengecoran gravitasi dengan variasi penambahan Ni sebesar 0,5 wt%, 1 wt%, dan 1,5 wt%, dilanjutkan dengan perlakuan panas homogenisasi. Pengujian dilakukan di Laboratorium Material Universitas Negeri Jakarta menggunakan Optical Emission Spectrometer (OES) untuk analisis komposisi, mikroskop optik untuk pengamatan struktur mikro, uji kekerasan metode vickers, serta uji korosi metode weight loss dalam larutan H₂SO₄ 30%. Hasil penelitian menunjukkan bahwa penambahan Ni memperhalus struktur butir dan meningkatkan kestabilan fasa α serta mendorong terbentuknya fasa β. Nilai kekerasan meningkat signifikan pada komposisi Cu-34Zn-1,5Ni dari 131,18 VHN menjadi 144,46 VHN setelah homogenisasi. Uji korosi menunjukkan peningkatan ketahanan dengan laju korosi terendah sebesar 0,0093 mmpy pada paduan Cu-34Zn-1,5Ni. Dengan demikian, penambahan Ni terbukti meningkatkan sifat mekanik dan ketahanan korosi, menjadikan paduan ini potensial sebagai material alternatif untuk aplikasi medis. Kata kunci: Cu-Zn-Ni, homogenisasi, kekerasan, ketahanan korosi, struktur mikro. ***** This study aims to analyze the effect of nickel (Ni) addition on the microstructure, hardness, and corrosion resistance of Cu-34Zn brass alloy as an effort to develop an alternative material for medical equipment with high strength and corrosion resistance. The literature review is based on the Cu-Zn phase diagram theory and the solid solution strengthening mechanism. The experimental process involved gravity casting with variations of Ni addition at 0.5 wt%, 1 wt%, and 1.5 wt%, followed by a homogenization heat treatment. The tests were conducted at the Materials Laboratory, Universitas Negeri Jakarta, using an Optical Emission Spectrometer (OES) for composition analysis, an optical microscope for microstructural observation, a Vickers hardness tester, and a weight loss corrosion test in 30% H₂SO₄ solution. The results show that the addition of Ni refines the grain structure, enhances the stability of the α-phase, and promotes the formation of the β-phase. The hardness value significantly increased in the Cu-34Zn-1.5Ni composition from 131.18 VHN to 144.46 VHN after homogenization. The corrosion test indicated improved resistance, with the lowest corrosion rate of 0.0093 mmpy observed in the Cu-34Zn-1.5Ni alloy. Therefore, the addition of Ni effectively enhances the mechanical properties and corrosion resistance, making this alloy a potential alternative material for medical applications. Keywords: Cu-Zn-Ni, homogenization, hardness, corrosion resistance, microstructure.

Item Type:	Thesis (Sarjana)
Additional Information:	1). Dr. Imam Basori, M.T. ; 2). Dr. Eng. Agung Premono, M.T.
Subjects:	Teknologi dan Ilmu Terapan > Teknik Mesin, Mekanika Teknik Teknologi dan Ilmu Terapan > Manufaktur
Divisions:	FT > S1 Teknik Mesin
Depositing User:	HENDI WAHYUDIN .
Date Deposited:	23 Dec 2025 07:26
Last Modified:	23 Dec 2025 07:26
URI:	http://repository.unj.ac.id/id/eprint/62891

Actions (login required)

View Item