KARAKTERISTIK KOMPOSIT SERAT RAMI DAN KELAPA SEBAGAI MATERIAL PEREDAM SUARA

ARZHETA HAFIZ PRASETYO, . (2026) KARAKTERISTIK KOMPOSIT SERAT RAMI DAN KELAPA SEBAGAI MATERIAL PEREDAM SUARA. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text COVER_1502621078.pdf Download (1MB)
	Text BAB 1.pdf Download (378kB)
	Text BAB 2.pdf Restricted to Registered users only Download (1MB) | Request a copy
	Text BAB 3.pdf Restricted to Registered users only Download (894kB) | Request a copy
	Text BAB 4.pdf Restricted to Registered users only Download (1MB) | Request a copy
	Text BAB 5.pdf Restricted to Registered users only Download (358kB) | Request a copy
	Text DAFTAR PUSTAKA.pdf Download (346kB)
	Text LAMPIRAN.pdf Restricted to Registered users only Download (856kB) | Request a copy

Abstract

Kebisingan yang melebihi tingkat yang wajar dapat menyebabkan masalah kesehatan, mengganggu kenyamanan, dan menurunkan produktivitas, sehingga diperlukan bahan yang dapat menyerap suara dengan baik. Material peredam suara tradisional umumnya terbuat dari bahan sintetis seperti busa polimer, glasswool, dan rockwool, yang kurang ramah lingkungan dan dapat menyebabkan iritasi. Maka dari itu, dibutuhkan alternatif bahan yang berbasis serat alami yang terjangkau dan lebih ramah lingkungan. Serat rami dan serat kelapa adalah sumber daya alam yang melimpah di Indonesia dan memiliki struktur berpori yang baik untuk penyerapan suara. Penelitian ini bertujuan untuk menganalisis karakteristik penyerap suara dari komposit yang menggunakan serat rami, serat kelapa, dan campurannya dengan resin polyurethane. Pengujian koefisien penyerapan suara dilakukan dengan metode tabung impedansi mengikuti standar ASTM E1050. Hasil penelitian menunjukkan bahwa komposit yang menggabungkan serat rami dan kelapa memiliki kemampuan penyerapan suara yang baik, dengan nilai maksimum koefisien serap mencapai 0,59 pada frekuensi 3500 Hz. Selain itu, peningkatan ketebalan material juga meningkatkan kemampuan penyerapan suara, di mana ketebalan 9 cm menghasilkan nilai tertinggi hingga 0,70. Komposit ini berpotensi menjadi pilihan material penyerap suara yang efektif, murah, dan ramah lingkungan. ***** Noise that exceeds reasonable levels can cause health problems, disturb comfort, and reduce productivity, so materials that can absorb sound well are needed. Traditional sound-absorbing materials are generally made from synthetic materials such as polymer foam, glass wool, and rock wool, which are less environmentally friendly and can cause irritation. Therefore, an alternative material based on natural fibers that is affordable and more environmentally friendly is needed. Jute and coconut fibers are abundant natural resources in Indonesia and have a porous structure that is ideal for sound absorption. This study aims to analyze the sound absorption characteristics of composites using jute fibers, coconut fibers, and their mixture with polyurethane resin. Sound absorption coefficient testing was conducted using the impedance tube method in accordance with the ASTM E1050 standard. The results showed that composites combining hemp and coconut fibers had good sound absorption capabilities, with a maximum absorption coefficient value of 0.59 at a frequency of 3500 Hz. Additionally, increasing the material thickness also enhances sound absorption capability, with a thickness of 9 cm yielding the highest value of 0.70. This composite has the potential to be an effective, affordable, and environmentally friendly sound-absorbing material.

Item Type:	Thesis (Sarjana)
Additional Information:	1). Dr. Siska Titik Dwiyati, M.T. ; 2). Drs. Syaripuddin, M.Pd.
Subjects:	Sains > Kimia Teknologi dan Ilmu Terapan > Teknik Mesin, Mekanika Teknik Teknologi dan Ilmu Terapan > Teknik Pertambangan, Metalurgi
Divisions:	FT > S1 Pendidikan Teknik Mesin
Depositing User:	Arzheta Hafiz Prasetyo
Date Deposited:	02 Feb 2026 06:20
Last Modified:	02 Feb 2026 06:20
URI:	http://repository.unj.ac.id/id/eprint/64668

Actions (login required)

View Item