PEMANFAATAN CAMPURAN LIMBAH PLASTIK HDPE DAN FLY ASH SEBAGAI SUBTITUSI AGREGAT HALUS PADA PAVING BLOCK SEBAGAI IMPLEMENTASI PADA MATA KULIAH ILMU BAHAN BANGUNAN

ARI RAMADDAN, . (2026) PEMANFAATAN CAMPURAN LIMBAH PLASTIK HDPE DAN FLY ASH SEBAGAI SUBTITUSI AGREGAT HALUS PADA PAVING BLOCK SEBAGAI IMPLEMENTASI PADA MATA KULIAH ILMU BAHAN BANGUNAN. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text COVER.pdf Download (1MB)
	Text BAB 1.pdf Download (385kB)
	Text BAB 2.pdf Restricted to Registered users only Download (687kB)
	Text BAB 3.pdf Restricted to Registered users only Download (864kB)
	Text BAB 4.pdf Restricted to Registered users only Download (594kB)
	Text BAB 5.pdf Restricted to Registered users only Download (329kB)
	Text DAFTAR PUSTAKA.pdf Download (320kB)
	Text LAMPIRAN.pdf Restricted to Registered users only Download (2MB)

Abstract

Paving block merupakan material bangunan yang dibuat dari campuran semen, agregat, dan air yang digunakan sebagai lapisan perkerasan permukaan tanah. Penelitian ini bertujuan untuk menganalisis karakteristik paving block dengan memanfaatkan HDPE dan Fly Ash sebagai bahan substitusi sebagian pasir, serta mengetahui pengaruhnya terhadap persyaratan mutu berdasarkan SNI 03-0691-1996. Metode yang digunakan dalam penelitian ini adalah metode eksperimental dengan benda uji paving block berbentuk balok berukuran 20 x 10 x 6 cm. Substitusi agregat halus dilakukan menggunakan campuran HDPE dan Fly Ash dengan variasi persentase sebesar 0%, 5%, 10%, 15% dan 20%. Pengujian meliputi pengujian kuat tekan, ketahanan aus, penyerapan air dan ketahanan terhadap natrium sulfat. Pengujian dilakukan pada umur 28 hari sesuai dengan ketentuan SNI 03-0691-1996. Hasil penelitian menunjukkan bahwa penggunaan campuran HDPE dan Fly Ash sebagai substitusi sebagian agregat halus dapat meningkatkan mutu paving block apabila digunakan pada proporsi yang tepat. Nilai rata-rata kuat tekan tertinggi yaitu variasi 15% sebesar 26,667 Mpa. Penelitian ini mengacu berdasarkan SNI 03-0691-1996 paving block dengan presentase 0%, 5%, 10%, 15%, dan 20% campuran HDPE dan Fly Ash sebagai subtitusi agregat halus masuk kedalam klasifikasi mutu B yaitu sebagai pelataran parkir. Berdasarkan Pengujian ketahanan aus, variasi 0%,5%,10%,15% dan 20% memenuhi kelas mutu A. Pada pengujian penyerapan air, variasi 0% dan 5% termasuk dalam mutu B, sedangkan variasi 10%, 15% dan 20% juga tergolong mutu C. ***** Paving blocks are construction materials made from a mixture of cement, aggregates, and water, and are used as surface pavement layers. This study aims to analyze the characteristics of paving blocks by utilizing HDPE and fly ash as partial substitutes for sand, as well as to determine their effects on quality requirements based on SNI 03-0691-1996. The method employed in this research is an experimental method using paving block specimens in the form of rectangular blocks measuring 20 × 10 × 6 cm. The substitution of fine aggregates was carried out using a mixture of HDPE and fly ash with percentage variations of 0%, 5%, 10%, 15%, and 20%. The tests conducted included compressive strength, abrasion resistance, water absorption, and resistance to sodium sulfate. All tests were performed at the age of 28 days in accordance with SNI 03-0691-1996. The results indicate that the use of HDPE and fly ash as partial substitutes for fine aggregates can improve the quality of paving blocks when applied in appropriate proportions. The highest average compressive strength was obtained at the 15% variation, reaching 26.667 MPa. Based on SNI 03-0691-1996, paving blocks with 0%, 5%, 10%, 15%, and 20% HDPE and fly ash substitution of fine aggregates fall into quality classification B, which is suitable for parking areas. Based on abrasion resistance testing, variations of 0%, 5%, 10%, 15%, and 20% meet the requirements for quality class A. In the water absorption test, variations of 0% and 5% fall into quality class B, while variations of 10%, 15%, and 20% are classified as quality class C.

Item Type:	Thesis (Sarjana)
Additional Information:	1). Anisah, M.T. ; 2). R. Eka Murtinugraha, M.Pd.
Subjects:	Teknologi dan Ilmu Terapan > Teknik Sipil Teknologi dan Ilmu Terapan > Konstruksi Bangunan
Divisions:	FT > S1 Pendidikan Teknik Bangunan
Depositing User:	Ari Ramaddan .
Date Deposited:	10 Feb 2026 03:12
Last Modified:	10 Feb 2026 03:12
URI:	http://repository.unj.ac.id/id/eprint/65202

Actions (login required)

View Item